The Corrosion Resistance of Aluminum Alloy Modified by Laser Radiation

This study presents an analysis of the impact of the oxide layers, prepared utilizing fiber laser radiation (1062 nm) in ambient air with different process parameters, on the corrosion resistance of EN 5754 aluminum alloy. Due to both high corrosion resistance and high fatigue strength, a 5754 alloy is used, among others, in the marine, aerospace, automotive, and chemical industries. Nevertheless, it corrodes in aggressive environments (with high chloride ions concentration). The controlled delivery of laser radiation energy in the oxygen environment allows the formation of the oxide layer on the surface of the material. We have determined that it significantly affects the resistance of these materials to corrosion. As a result of laser irradiation, changes in the chemical structure of the surface layer (chemical composition as well as surface development) can be observed. It may exert both a positive and a negative consequence on the corrosion resistance. The electrochemical corrosion tests (potentiodynamic polarization and electrochemical impedance spectroscopy EIS) have been carried out in an aggressive environment (3% NaCl). Moreover, microscopic examination, chemical tests, and roughness were also performed. The study revealed that appropriate control of the laser process can significantly increase the original corrosion resistance of the 5754 aluminum alloy.