Flow Kinetics of Molten Silicates through Thermal Barrier Coating: A Numerical Study

Mohammad Rizviul Kabir, Anil Kumar Sirigiri, Ravisankar Naraparaju, Uwe Schulz

Coatings· Volume 9· Issue 5

Abstract

Infiltration of molten calcium–magnesium–alumina–silicates (CMAS) through thermal barrier coatings (TBCs) causes structural degradation of TBC layers. The infiltration kinetics can be altered by careful tailoring of the electron beam physical vapor deposition (EB-PVD) microstructure such as feather arm lengths and inter-columnar gaps, etc. Morphology of the feathery columns and their inherent porosities directly influences the infiltration kinetics of molten CMAS. To understand the influence of columnar morphology on the kinetics of the CAMS flow, a finite element based parametric model was developed for describing a variety of EB-PVD top coat microstructures. A detailed numerical study was performed considering fluid-solid interactions (FSI) between the CMAS and TBC top coat (TC). The CMAS flow characteristics through these microstructures were assessed quantitatively and qualitatively. Finally, correlations between the morphological parameters and CMAS flow kinetics were established. It was shown that the rate of longitudinal and lateral infiltration could be minimized by reducing the gap between columns and increasing the length of the feather arms. The results also show that the microstructures with long feather arms having a lower lateral inclination decrease the CMAS infiltration rate, therefore, reduce the CMAS infiltration depth. The analyses allow the identification of key morphological features that are important for mitigating the CMAS infiltration.
Source: crossref · Quality: baseline

Research context

OpenAlex topics: High-Temperature Coating Behaviors · Advanced ceramic materials synthesis · Particle Dynamics in Fluid Flows

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

Affiliations

Experimental and Numerical Methods, Institute of Materials Research, German Aerospace Center (DLR), Linder Höhe, 51147 Cologne, Germany

High Temperature and Functional Coatings, Institute of Materials Research, German Aerospace Center (DLR), Linder Höhe, 51147 Cologne, Germany

Funding

Deutsche Forschungsgemeinschaft

References (45)

Show source-provided references
1. Influence of EB-PVD TBC microstructure on thermal barrier coating system performance under cyclic oxidation conditions10.1016/S0257-8972(99)00343-6 ↗
2. Mechanisms controlling the durability of thermal barrier coatings10.1016/S0079-6425(00)00020-7 ↗
3. Some recent trends in research and technology of advanced thermal barrier coatings10.1016/S1270-9638(02)00003-2 ↗
4. Materials design for the next generation thermal barrier coatings10.1146/annurev.matsci.33.011403.113718 ↗
5. Emerging materials and processes for thermal barrier systems10.1016/j.cossms.2004.03.009 ↗
6. Thermal-barrier coatings for more efficient gas-turbine engines10.1557/mrs.2012.232 ↗
7. Thermochemical interaction of thermal barrier coatings with molten CaO–MgO–Al2O3–SiO2 (CMAS) deposits10.1111/j.1551-2916.2006.01209.x ↗
8. Molten silicate interactions with thermal barrier coatings10.1016/j.surfcoat.2014.04.007 ↗
9. Role of environment deposits and operating surface temperature in spallation of air plasma sprayed thermal barrier coatings10.1016/S0257-8972(96)02994-5 ↗
10. A delamination mechanism for thermal barrier coatings subject to calcium–magnesium–alumino–silicate (CMAS) infiltration10.1016/j.actamat.2004.11.028 ↗
11. CMAS degradation of environmental barrier coatings10.1016/j.surfcoat.2007.06.045 ↗
12. CMAS corrosion of EB PVD TBCs: Identifying the minimum level to initiate damage10.1016/j.ijrmhm.2009.07.005 ↗
13. Environmental degradation of thermal-barrier coatings by molten deposits10.1557/mrs.2012.230 ↗
14. Novel thermal barrier coatings that are resistant to high-temperature attack by glassy deposits10.1016/j.actamat.2007.08.028 ↗
15. Infiltration-inhibiting reaction of gadolinium zirconate thermal barrier coatings with CMAS melts10.1111/j.1551-2916.2007.02175.x ↗
16. CMAS-resistant thermal barrier coatings (TBC)10.1111/j.1744-7402.2009.02373.x ↗
17. Pubbysetty, R.P. (2016). Developing the CMAS (CaO–MgO–Al2O3–SiO2) Resistant TBCs (Thermal Barrier Coatings): Alumina (Al2O3) as A Candidate for Restricting the CMAS Infiltration in TBCs. [Master’s Thesis, RWTH Aachen].
18. Gomez Chavez, J.J. (2016). Yttria Rich TBCs as Candidates for CMAS Resistant Top Coats. [Master’s Thesis, University of Texas].
19. Interaction and infiltration behavior of Eyjafjallajökull, Sakurajima volcanic ashes and a synthetic CMAS containing FeO with/in EB-PVD ZrO2–65 wt % Y2O3 coating at high temperature10.1016/j.actamat.2017.06.055 ↗
20. Jet engine coatings for resisting volcanic ash damage10.1002/adma.201004783 ↗
21. Degradation of La2Zr2O7 and other novel EB-PVD thermal barrier coatings by CMAS (CaO–MgO–Al2O3–SiO2) and volcanic ash deposits10.1016/j.surfcoat.2013.07.029 ↗
22. Volcanic ash-induced decomposition of EB-PVD Gd2Zr2O7 thermal barrier coatings to Gd-oxyapatite, zircon, and Gd, Fe–zirconolite10.1111/jace.12251 ↗
23. Effect of CMAS deposits on MOCVD coatings in the system Y2O3–ZrO2: Phase relationships10.1111/jace.12502 ↗
24. Tailoring the EB-PVD columnar microstructure to mitigate the infiltration of CMAS in 7YSZ thermal barrier coatings10.1016/j.jeurceramsoc.2016.07.027 ↗
25. Effect of morphology on thermal conductivity of EB-PVD PYSZ TBCs10.1016/j.surfcoat.2006.05.003 ↗
26. EB-PVD alumina (Al2O3) as a top coat on 7YSZ TBCs against CMAS/VA infiltration: Deposition and reaction mechanisms10.1016/j.jeurceramsoc.2018.03.027 ↗
27. Oxidation induced stress fields in an EB-PVD thermal barrier coating10.1016/S0257-8972(02)00167-6 ↗
28. A parametric study of damage initiation and propagation in EB-PVD thermal barrier coatings10.1016/j.mechmat.2009.09.004 ↗
29. An analytical model for predicting thermal residual stresses in multilayer coating systems10.1016/j.tsf.2005.04.027 ↗
30. Hochstein, L. (2017). Lebensdauer von 7YSZ EB-PVD Wärmedämmschichten in Flugtriebwerken mit Lokaler CMAS Belastung: Ausfallmechanismen und Modellierung. [Master’s Thesis, TU Dresden].
31. Estimation of CMAS Infiltration depth in EB-PVD TBCs: A new constraint model supported with experimental approach10.1016/j.jeurceramsoc.2019.02.040 ↗
32. Microstructure and texture of EB-PVD TBCs grown under different rotation modes10.1016/S0921-5093(03)00470-2 ↗
33. (ABAQUS, 2016). ABAQUS, V., 6.16; Documentation, Theory manual.
34. The anorthite–diopside system: Structural and devitrification study. Part II: Crystallinity analysis by the Rietveld–RIR method10.1111/j.1551-2916.2005.00578.x ↗
35. Liquid and magma viscosity in the anorthite-forsterite-diopside-quartz system and implications for the viscosity-temperature paths of cooling magmas10.1029/2006JB004812 ↗
36. Shock compression of molten silicate: Results for a model basaltic composition10.1029/JB093iB01p00367 ↗
37. New acoustic velocity measurements on CaO–MgO–Al2O3–SiO2 liquids: Reevaluation of the volume and compressibility of CaMgSi2O6–CaAl2Si2O8 liquids to 25 GPa10.1029/2007JB005010 ↗
38. Direct shock compression experiments on premolten forsterite and progress toward a consistent high-pressure equation of state for CaO–MgO–Al2O3–SiO2–FeO liquids10.1002/jgrb.50374 ↗
39. Mechanical and thermal properties of calcium–magnesium aluminosilicate (CMAS) glass10.1016/j.jeurceramsoc.2015.03.032 ↗
40. Density changes during the fractional crystallization of basaltic magmas: Fluid dynamic implications10.1007/BF00378108 ↗
41. Viscosity of magmatic liquids: A model10.1016/j.epsl.2008.03.038 ↗
42. High temperature viscosity of calcium–magnesium–aluminosilicate glass from synthetic sand10.1016/j.scriptamat.2016.07.020 ↗
43. CMAS behavior of yttrium aluminum garnet (YAG) and yttria-stabilized zirconia (YSZ) thermal barrier coatings10.1016/j.surfcoat.2017.08.023 ↗
44. Effect of CMAS composition on hot corrosion behavior of gadolinium zirconate thermal barrier coating materials10.1149/2.0531709jes ↗
45. Volcanic ash melting under conditions relevant to ash turbine interactions10.1038/ncomms10795 ↗