Room- and high temperature Wear Resistance of MCrAlY Coatings Deposited by Detonation Gun (D-gun) and Supersonic Plasma Spraying (SSPS) Techniques

In this study, CoNiCrAlY metallic coatings were deposited on an Inconel 718 nickel-based superalloy substrate material using the detonation gun (D-gun) and supersonic plasma spraying (SSPS) techniques. The microstructural and mechanical properties in addition to their room and high temperature wear behavior of the produced coatings were evaluated. The wear tests were performed at room temperature (rt), 250 and 500 °C using 2N and X-ray diffraction (XRD), scanning electron microscopy (SEM), and energy-dispersive spectroscopy (EDS) analyses of the worn coatings were performed to assess their wear performance. The coatings produced with D-gun process exhibited higher hardness and lower porosity (550 ± 50 HV0.25 hardness and 1.2 ± 1.0% porosity) than SSPS coatings (with 380 ± 30 HV0.25 hardness and 1.5 ± 1.0% porosity) which resulted in better room- and high temperature wear performance for D-gun coatings. The worn surfaces of both coatings exhibited formation of tribological layers and superficial microstructural changes by varying temperature and load conditions. Increasing load and temperature resulted in increased wear loss whereas increasing temperature resulted in reduced COF values for both coatings.