Application of AC-DC-AC Accelerated Aging to Assess the Galvanic Corrosion Risk of Mild Steel Coated with Graphene-Embedded Epoxy Coatings

This study presents a novel approach to evaluate the galvanic corrosion risk of mild steel coated with graphene-embedded epoxy coatings. The potential for graphene platelets to promote anodic dissolution of the underlying steel substrate via galvanic corrosion mechanisms was systematically assessed through the accelerated alternating current-direct current-alternating current (AC-DC-AC) technique and cathodic disbondment testing. The possible risk of displacing cathodic reactions from the coating–steel interface to the dispersed graphene platelets within the epoxy matrix was investigated by evaluating the degradation trend of the graphene-containing coating under the AC-DC-AC test. The degradation behaviour of both pure epoxy and graphene-embedded epoxy coatings during accelerated aging was characterized using electrochemical impedance spectroscopy (EIS) measurements. The finding highlighted the negligible catalytic effect of incorporated graphene platelets on the anodic dissolution of steel substrate. On the other hand, as an inert filler, graphene platelets contributed to the enhancement of the structural integrity of the epoxy matrix during the AC-DC-AC test and natural immersion in NaCl 3.5 wt % solution by enhancing the barrier performance of the coating. Despite their spectacular barrier performance, damaged graphene-containing coatings performed inferiorly against corrosion-induced delamination compared to pure epoxy. Samples underwent the cathodic disbondment test to eliminate the effect of substrate anodic dissolution from corrosion-induced delamination. The accelerated delamination of graphene-embedded epoxy coatings was attributed to the destructive impact of graphene platelets on the interfacial adhesion of the epoxy matrix to the steel substrate.