Mechanical and Tribological Behavior of TiAlSiN/AlSiN Coatings Depending on the High-Temperature Treatment

TiAlSiN/AlSiN coatings, with 3 and 30 periods, were successfully deposited by cathodic-arc evaporation technology. The composition, structure, mechanical, and tribological properties were studied at thermal treatment from 700 °C to 900 °C. The SEM observation and EDS analysis verified the dense structure and stable element composition in the coating depth at increased temperatures. A limited surface oxidation was identified at 800 °C, which increased moderately at a higher temperature of 900 °C. The coating period displays a nanocomposite structure of TiAl(Si)N and AlN nanograins incorporated in an amorphous Si3N4 matrix obtained by XRD and XPS analyses. The coatings exhibit high hardness of 41.1 GPa and 36.4 GPa for the 3- and 30-period coatings, respectively. The coatings with higher modulation periods demonstrate an excellent high temperature hardness and resistance to elastic and plastic deformations up to 900 °C. The hardness of the coatings with a smaller modulation period reduces to 29.7 GPa at the same temperature, causing a decrease in the H/E and H3/E*2 ratios. The tribological tests found that the high-temperature wear resistance depends strongly on the coating composition and architecture. An oxidation wear mechanism dominates the coatings with a large modulation period, and the wear rate decreases with a temperature increase. Abrasive wear is predominant in coatings with a lower modulation period, leading to an increasing wear rate. Wear rate values of 7.27 × 10−6 mm3/N·m and 8.53 × 10−6 mm3/N·m were determined after annealing at 900 °C for the 3- and 30-period coatings, respectively.