Design and Preparation of a Novel Double-Modified Cement-Based Protective Coating Material and Its Improved Protection Performance Against Chloride Corrosion

The service of reinforced concrete structures (RCSs) in harsh coastal environments is often threatened by chloride corrosion. The penetration of chloride ions through concrete pores into the steel/concrete interface will cause the depassivation and corrosion of steel rebars, which will lead to the deterioration and failure of RCSs durability. It is important to repair and protect the corrosion damage of existing concrete structures and ensure their high durability, and the high performance of repairing and protecting materials is crucial. In this paper, a novel cement-based protective coating material with low porosity, high impermeability and chloride-corrosion resistance was designed and prepared by introducing polypropylene fiber and high-performance cement into commercial cement-based protective materials through the double modification strategy of fiber-toughening and substrate-enhancing, in order to provide a reliable corrosion protection solution for the high durability and long life of RCSs under chloride erosion environment. Based on this, the microstructure and pore structure of the double-modified coating material was systematically analyzed by SEM, XRD, X-CT and other characterization methods. The impermeability and chloride corrosion resistance of this material were scientifically evaluated, and the protection mechanism was systematically discussed. The results show that the impermeability of the double-modified coating material is about 2.8 times higher than that of the untreated mortar. At the same time, the corrosion current density was significantly reduced to 8.60 × 10−7 A·cm−2, which was about 86% lower than that of the untreated sample (6.11 × 10−6 A·cm−2). The new cement-based coating material optimized by double-modification effectively inhibits the formation and propagation of microcracks in the protective coating through the bridging effect of fibers. At the same time, the regulation of cement hydration products and the densification of pore structure are realized by adjusting the composition of cement matrix. Based on the above two aspects of microstructure improvement, the chloride-corrosion protection performance of the novel cement-based protective coating material has been greatly improved.