Effect of Sintering Temperature on Tensile Properties of Ti-6Al-4V Alloy Manufactured Through Metal Injection Molding

Titanium and titanium alloys exhibit low density, high strength and excellent corrosion resistance, and have become workhorses in modern aerospace and chemical processing industries. Recently, Ti-6Al-4V alloy has been manufactured through metal injection molding (MIM). MIM is widely utilized in various manufacturing industries due to the near-net-forming process, especially in the preparation of difficult-to-deform high-temperature alloys. Sintering temperature is vital to ensuring good tensile mechanical properties. In this work, Ti-6Al-4V alloy was sintered under various sintering temperatures, from 1150 to 1250 °C. The effect of sintering temperature on the mechanical properties was evaluated. The tensile test results exhibited that a yield strength of 896.35 MPa, an ultimate tensile strength of 980.83 MPa and plastic elongation of 9.61% were produced at 1150 °C for 4 h; a yield strength of 877.23 MPa, an ultimate tensile strength of 981.92 MPa and plastic elongation of 7.74% were produced at 1200 °C for 4 h; and a yield strength of 923.33 MPa, an ultimate tensile strength of 1002.24 MPa and plastic elongation of 6.57% were produced at 1250 °C for 4 h.