Physicochemical and Preliminary Biological Properties of Thin Films Based on Fluoride-Doped Hydroxyapatite in a Dextran Matrix for Biomedical Applications

A spin-coating technique was used to produce new thin films of fluoride-doped hydroxyapatite (HApF) and fluoride-doped hydroxyapatite in a dextran matrix (HApF-Dx) with the potential to be used as nanocoatings for various biomedical implants. The stability of the suspensions used in obtaining the thin films was confirmed by ultrasonic measurements with double-distilled water as a reference. The HApF and HApF-Dx thin films obtained by spin-coating showed diffraction patterns corresponding to hexagonal hydroxyapatite. The X-ray photoelectron spectroscopy studies confirmed the partial substitution of hydroxyl groups (-OH) by fluoride ions. The FTIR studies were conducted in order to highlight the presence of the functional group specific for the HAp in the samples and the influence of the dextran addition on the vibrational characteristics. The surface morphologies of the HApF and HApF-Dx thin films were explored using scanning electron microscopy (SEM), atomic force microscopy (AFM), and metallographic microscopy (MM). The surfaces of the HApF and HApF-Dx thin films were found to be smooth, homogenous, and nanostructured. The biocompatibility assays on HGF-1 cells confirmed that both coatings exhibited good cell viability for all the tested time intervals (24 and 48 h). The findings highlighted the potential of HApF and HApF-Dx coatings for biomedical applications. Additional information about the HGF-1 adherence and development on the surface of the HApF and HApF-Dx coatings was obtained using metallographic microscopy, scanning electron microscopy, and atomic force microscopy techniques. This research demonstrates that the spin-coating method can be successfully used to fabricate HApF and HApF-Dx nanocoatings for potential biomedical applications.