A Direct Laser Sintering Approach for the Electrophoretic Deposition Overlay of Yttria-Stabilized Zirconia on the Surface of a Thermal Barrier Coating System

The laser sintering process and modification of yttria-stabilized zirconia (YSZ) coatings subjected to electrophoretic deposition (EPD) on YSZ air-plasma-sprayed (APS) thermal barrier coatings (TBCs) were investigated. A Ni-based superalloy was plasma-sprayed using yttria-stabilized zirconia (YSZ) to create a thermal barrier coating with a 400 μm thickness. The electrophoretic deposition (EPD) technique was used to deposit the nanopowder of YSZ on the surface of YSZ TBCs. In this study, a technology based on the direct sintering of a green EPD layer using a laser beam was employed. The best conditions for the deposition overlay of the YSZ coating using a DC current were obtained with an applied voltage of 40 V, deposition time of 5 min, and suspension concentration of 10 g/L. Iodine was added to the solutions as a stabilizing agent. To overcome the problems of high sintering temperatures, laser sintering was adopted as a new approach. The microstructures of all the specimens were studied using field emission scanning electron microscopy (FESEM) with energy-dispersive X-ray spectroscopy (EDS) analysis. Surface roughness was investigated using atomic force microscopy (AFM) analysis and the central line average (CLA). The direct laser sintering (DLS) process for the EPD overlay on the surface of the TBCs caused a reduction in surface roughness and porosity, and improvements in the microstructural and mechanical properties of the surface coatings were observed.