Hot-Corrosion Behavior of Gd2O3–Yb2O3 Co-Doped YSZ Thermal Barrier Coatings in the Presence of V2O5 Molten Salt
Source abstract
Abstract
In this study, thermal barrier coatings (TBC) consisting of 3.5 mol% Yb2O3-stabilized ZrO2 co-doped with 1 mol% Gd2O3 and 1 mol% Yb2O3 (referred to as GdYb-YSZ) were fabricated by means of air plasma spraying. The as-fabricated coatings exhibited a metastable tetragonal (t′) structure. The hot-corrosion behavior of the GdYb–YSZ TBCs was investigated at 700, 800, 900, and 1000 °C for 10 h in the presence of V2O5 molten salt. During the corrosion tests, the t′ phase transformed into a monoclinic (m) phase; nevertheless, it was still detected on the corroded surfaces. The amount of t′ phase decreased with increasing corrosion temperature. The corrosion products formed on the GdYb-YSZ TBCs in V2O5 comprised Yb, Gd-doped YVO4, and m-ZrO2, irrespective of the temperature of corrosion. However, higher temperatures changed the morphologies of the Yb- and Gd-doped YVO4 corrosion products. The GdYb–YSZ TBCs exhibited improved corrosion resistance to V2O5 molten salt when compared to YSZ TBCs, and the related mechanism is discussed in detail in this paper.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: High-Temperature Coating Behaviors · Advanced ceramic materials synthesis · Nuclear Materials and Properties
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
School of Mechanical & Electrical Engineering, Hunan Applied Technology University, Changde 415000, China
Funding
Hunan Provincial Department of Education General Project
References (42)
Show source-provided references
1. Overview on advanced thermal barrier coatings10.1016/j.surfcoat.2010.08.151 ↗
2. Surface roughness affects metastable non-wetting behavior of silicate melts on thermal barrier coatings10.1007/s12598-021-01773-6 ↗
3. CMAS corrosion behavior and protection method of thermal barrier coatings for aeroengine
4. Microstructural understanding of the oxidation and inter-diffusion behavior of Cr-coated Alloy 800H in supercritical water10.1016/j.corsci.2022.110910 ↗
5. Restraining the Cr-Zr interdiffusion of Cr-coated Zr alloys in high temperature environment: A Cr/CrN/Cr coating approach10.1016/j.corsci.2023.111015 ↗
6. Novel ceramic materials for thermal barrier coatings
7. Thermal barrier coatings of new rare-earth composite oxide by EB-PVD10.1016/j.jallcom.2013.10.157 ↗
8. Liu, Y., Ravichandran, R., Chen, K.Y., and Patnaik, P. (2021). Application of machine learning to solid particle erosion of APS-TBC and EB-PVD TBC at elevated temperatures. Coatings, 11.10.3390/coatings11070845 ↗
9. Xie, Z.H., Liu, Q., Lee, K.I., Zhu, W., Wu, L.T., and Wu, R.T. (2022). The effect of bond coat roughness on the cmas hot corrosion resistance of EB-PVD thermal barrier coatings. Coatings, 12.10.3390/coatings12050596 ↗
10. PS−PVD alumina overlayer on thermal barrier coatings against CMAS attack10.1007/s11666-021-01172-4 ↗
11. Molten-volcanic-ash-phobic thermal barrier coating based on biomimetic structure10.1002/advs.202205156 ↗
12. Ultrafast laser reconstructed PS-PVD thermal barrier coatings with superior silicophobic triple-scale micro/nano structure10.1016/j.matdes.2023.111846 ↗
13. Life time of new SYSZ thermal barrier coatings produced by plasma spraying method under thermal shock test and high temperature treatment10.1016/j.ceramint.2013.07.023 ↗
14. Effect of dopants on the phase stability of zirconia-based plasma sprayed thermal barrier coatings10.1016/j.jeurceramsoc.2009.08.008 ↗
15. Crystallization behavior of calcium–magnesium–alumina–silicate coupled with NaCl/Na2SO410.1016/j.corcom.2022.08.003 ↗
16. Microstructure and thermal properties of nanostructured gadolinia doped yttria-stabilized zirconia thermal barrier coatings produced by air plasma spraying10.1016/j.ceramint.2016.05.084 ↗
17. Effect of doping CeO2 and Sc2O3 on structure, thermal properties and sintering resistance of YSZ10.1016/j.ceramint.2020.11.032 ↗
18. Novel thermal barrier coatings based on rare-earth zirconates/YSZ double-ceramic-layer system deposited by plasma spraying10.1016/j.jallcom.2015.05.189 ↗
19. Reaction products of Sm2Zr2O7 with calcium-magnesium-aluminum-silicate (CMAS) and their evolution10.1007/s40145-021-0514-x ↗
20. Composition optimization, high-temperature stability, and thermal cycling performance of Sc-doped Gd2Zr2O7 thermal barrier coatings: Theoretical and experimental studies10.1007/s40145-021-0549-z ↗
21. GdPO4 as a novel candidate for thermal barrier coating applications at elevated temperatures10.1016/j.surfcoat.2018.06.016 ↗
22. She, Y.J., Guo, Y.W., Tan, Z.X., and Liao, K. (2020). Na2SO4 + V2O5 Corrosion behavior of BaNd2Ti3O10 for thermal barrier coating applications. Coatings, 10.10.3390/coatings10090901 ↗
23. Evaluation of microstructural evolution of thermal barrier coatings exposed to Na2SO4 using impedance spectroscopy10.1016/j.corsci.2010.12.023 ↗
24. Hot corrosion of V2O5-coated NdMgAl11O19 ceramic in air at 950 °C10.1016/j.jeurceramsoc.2013.02.016 ↗
25. Hot corrosion behavior of the La2(Zr0.7Ce0.3)2O7 ceramic in molten V2O5 and a Na2SO4+V2O5 salt mixture10.1016/j.jallcom.2016.07.257 ↗
26. A comparative investigation on the corrosion degradation of plasma sprayed YSZ and LnMgAl11O19 (Ln = Nd, Sm, Gd) coatings exposed to the molten V2O5 + Na2SO4 salt mixture at 1100 °C10.1016/j.jeurceramsoc.2019.04.055 ↗
27. Mechanism study and power transmission feature of acoustically stimulated and thermally loaded composite shell structures with double curvature10.1016/j.compstruct.2021.114557 ↗
28. Multi objective optimization of sound transmission across laminated composite cylindrical shell lined with porous core investigating Non-dominated Sorting Genetic Algorithm10.1016/j.ast.2017.06.008 ↗
29. Hot corrosion of stabilized zirconia thermal barrier coatings and the role of Mg inhibitor10.1111/jace.13631 ↗
30. Evaluation of hot corrosion behavior of plasma sprayed Scandia and yttria co-stabilized nanostructured thermal barrier coatings in the presence of molten sulfate and vanadate salt10.1016/j.jeurceramsoc.2014.08.029 ↗
31. Hot corrosion behavior of Sc2O3-Y2O3-ZrO2 thermal barrier coatings in presence of Na2SO4 + V2O5 molten salt10.1016/j.corsci.2014.04.001 ↗
32. Comparison of hot corrosion behavior of nanostructured ScYSZ and YSZ thermal barrier coatings10.1016/j.ceramint.2016.01.147 ↗
33. The hot corrosion behavior of plasma sprayed zirconia coatings stabilized with yttria, ceria, and titania in sodium sulfate and vanadium oxide10.1002/maco.201307331 ↗
34. Na2SO4 and V2O5 molten salts corrosion resistance of plasma-sprayed nanostructured ceria and yttria co-stabilized zirconia thermal barrier coatings10.1016/j.ceramint.2015.12.085 ↗
35. Corrosion products evolution and hot corrosion mechanisms of REPO4 (RE= Gd, Nd, La) in the presence of V2O5 + Na2SO4 molten salt10.1016/j.jeurceramsoc.2018.10.031 ↗
36. Hot corrosion evaluation of Gd2O3-Yb2O3 co-doped Y2O3 stabilized ZrO2 thermal barrier oxides exposed to Na2SO4+V2O5 molten salt10.1016/j.ceramint.2016.11.109 ↗
37. Phase stability and thermal conductivity of RE2O3 (RE=La, Nd, Gd, Yb) and Yb2O3 co-doped Y2O3 stabilized ZrO2 ceramics10.1016/j.ceramint.2016.01.138 ↗
38. High temperature corrosion behavior of zirconia ceramic in molten Na2SO4+NaVO3 salt mixture10.1016/j.ceramint.2015.08.116 ↗
39. Influence of Y2O3 addition on the microstructure of TiC reinforced Ti-based composite coating prepared by laser cladding10.1016/j.matchar.2022.111962 ↗
40. Oxide acid-base reactions in ceramic corrosion
41. Scandia-stabilized zirconia for resistance to molten vanadate-sulfate corrosion10.1016/0257-8972(89)90044-3 ↗
42. Hot corrosion behavior of La2Zr2O7 with the addition of Y2O3 thermal barrier coatings in contacts with vanadate-sulfate salts10.1016/j.jallcom.2010.05.121 ↗