Plasma Spraying with Wire Feeding: A Facile Route to Enhance the Coating/Substrate Interfacial Metallurgical Bonding
Source abstract
Abstract
Thermal spray coatings are widely used in many applications, and the adhesion effect at the coating/substrate interface plays an important role during the service life. The thermal spraying coating and substrate is primarily combined by a mechanical seizure effect. In this work, a strategy to generate interfacial metallurgical bonding is proposed. Plasma spraying with wire feeding was adopted to increase the size of sprayed particles, and metallurgical bonding was clearly formed between deposited particles and the substrate (304 stainless-steel and 7075 aluminum alloy). Interface reaction can be found at both NiAl/7075 and NiAl/304 interfaces. Typical Al-Al3Ni eutectic phase with higher microhardness was formed at NiAl/7075 interface. The adhesive strength of the coatings was significantly improved to 82.67 ± 3.96 MPa and 64.45 ± 2.84 MPa, respectively, for NiAl coating on 304 and 7075 substrates through tensile adhesion tests (TAT) without surface roughening pretreatment. This technique shows a promising aspect of the application of thermal spray coatings.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: High-Temperature Coating Behaviors · Intermetallics and Advanced Alloy Properties · Advanced ceramic materials synthesis
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Faculty of Material and Manufacturing, Beijing University of Technology, Beijing 100124, China
Funding
National Key Research and Development Program
References (30)
Show source-provided references
1. Influence of substrate roughness on the bonding mechanisms of high velocity oxy-fuel sprayed coatings10.1016/j.tsf.2005.03.024 ↗
2. Bahbou, F., and Nylen, P. (2005, January 2–4). Relationship between surface topography parameters and adhesion strength for plasma spraying. Proceedings of the Thermal Spray connects (ITSC 2005): Explore its surfacing potential!, The Material Information Society, Basel, Switzerland.10.31399/asm.cp.itsc2005p1027 ↗
3. Investigation of particle flattening behaviour and bonding mechanisms of APS sprayed coatings on magnesium alloys10.1016/j.surfcoat.2006.11.034 ↗
4. Oxidation of Ni-based single crystal after grit-blasting during exposure at high temperature10.1080/09603409.2017.1281869 ↗
5. Metallurgical bond between magnesium AZ91 alloy and aluminium plasma sprayed coatings10.1016/j.surfcoat.2015.10.032 ↗
6. Effect of laser textured groove wall interface on molybdenum coating diffusion and metallurgical bonding10.1016/j.surfcoat.2020.126561 ↗
7. Intrinsic residual stresses in single splats produced by thermal spray processes10.1016/S1359-6454(01)00099-4 ↗
8. An effective approach for creating metallurgical selfbonding in plasma-spraying of NiCr-Mo coating by designing shell-core-structured powders10.1016/j.actamat.2016.03.020 ↗
9. Role of condensates and adsorbates on substrate surface on fragmentation of impinging molten droplets during thermal spray10.1016/S0040-6090(01)00769-6 ↗
10. Effect of substrate oxidation on spreading of plasma-sprayed nickel on stainless steel10.1016/j.surfcoat.2007.04.041 ↗
11. Role of substrate temperature on microstructure formation in plasma-sprayed splats10.1016/j.surfcoat.2012.11.016 ↗
12. Lugscheider, E., Dicks, R., Kowalsky, K., Cook, D., Nassenstein, K., and Verpoort, C. (2004, January 10–12). A materials system and method of its application for the wear protection of aluminium engine cylinder bore surfaces. Proceedings of the 2004 International Thermal Spray Conference, Osaka, Japan.10.31399/asm.cp.itsc2004p0304 ↗
13. Melting and resolidification of a substrate in contact with a molten metal: Operational maps10.1016/S0017-9310(97)00222-6 ↗
14. Fauchais, P.L., Heberlein, J.V.R., and Boulos, M.I. (2014). Powders, Wires, Cords, and Rods. Thermal Spray Fundamentals, Springer.10.1007/978-0-387-68991-3 ↗
15. Role of powder granulometry and substrate topography in adhesion strength of thermal spray coatings10.1007/s11666-016-0411-y ↗
16. Li, H., Wei, Y., Qu, H., Lin, J., and Fu, H. (2020). Method and device for preparing spherical metal powder by hot wire assisted plasma arc. (CN110919017A), China.
17. Merz, R., Prinz, F.B., Ramaswami, K., Terk, M., and Weiss, L.E. (1994, January 1). Shape deposition manufacturing. Proceedings of the 1994 International Solid Freeform Fabrication Symposium, Austin, TX, USA.
18. A review of testing methods for thermal spray coatings10.1179/1743280414Y.0000000029 ↗
19. Mann, A.B. (2005). Surfaces and Interfaces for Biomaterials, Woodhead Publishing. [1st ed.].
20. Sasmal, S., and Anoop, M.B. (2019). Nanotechnology in Eco-Efficient Construction, Woodhead Publishing. [2nd ed.].
21. Mcdonald, A., Moreau, C., and Chandra, S. (2006, January 4–6). Estimating the Thermal Contact Resistance between Plasma-Sprayed Molybdenum and Metal Surfaces. Proceedings of the 3rd International Conference on Spray Deposition and Melt Atomization, Bremen, Germany.
22. Oxidation of stainless steel particles with and without an alumina shell during their flight in a plasma jet10.1615/HighTempMatProc.v4.i3.20 ↗
23. Effect of processing parameters on adhesion strength of arc sprayed NiAl coating
24. Microstructure and mechanical properties of twin-wire arc sprayed Ni-Al composite coatings on 6061-T6 aluminum alloy sheet10.1007/s12613-014-0931-8 ↗
25. The effect of Al-Mg substrate preparation on the adhesion strength of plasma sprayed Ni-Al coatings10.1016/j.surfcoat.2017.02.069 ↗
26. Microstructural characterization and hardness evaluation of HVOF sprayed Ni–5Al coatings on Ni- and Fe-based superalloys10.1016/j.jmatprotec.2008.08.009 ↗
27. Reaction mechanism and oxidation resistance at 700–900 °C of high porosity NiAl intermetallic10.1016/j.corsci.2021.109731 ↗
28. Development and characterization of Al–Al3Ni–Sn metal matrix composite10.1016/j.matchemphys.2020.124027 ↗
29. Martin, J.W., Doherty, R.D., and Cantor, B. (1997). Stability of Microstructure in Metallic Systems, Cambridge University Press. [2nd ed.].10.1017/CBO9780511623134 ↗
30. Eutectic solidification microstructure of an Al−4Ni−2Mn alloy10.1016/j.jallcom.2016.07.259 ↗