Galvanic Corrosion Behavior of the X80 Steel Welded Joint

Wire beam electrode techniques and classical electrochemical techniques were used to investigate the effect of the area ratio of each part of the welded joint on the galvanic corrosion behavior. The results showed that the order of the corrosion current density of the different regions in the simulated X80 steel welded joint was as follows: coarse-grained heat-affected zone > fine-grained heat-affected zone > intercritical heat-affected zone > base metal > weld metal. As the area ratio of weld metal increased, the galvanic potential shifted positively, the maximum anode galvanic current density increased and the main anode galvanic effect increased. On the other hand, as the area ratio of the base metal and the heat-affected zone decreased, the coupled potential shifted negatively and the maximum anode galvanic current density decreased. The galvanic corrosion intensity of the simulated X80 steel welded joint increased as the area ratio of the weld metal decreased and increased as the area ratio of the heat-affected zone and base metal increased. To enhance corrosion resistance, it is advisable to choose a shape with a larger groove to increase the WM area in the welded joint. Additionally, selecting a welding method with lower heat input and a higher energy density can help reduce the HAZ area in the welded joint.