High-Temperature Hot Corrosion Resistance of CrAl/NiCoCrAlY/AlSiY Gradient Composite Coating on TiAl Alloy
Source abstract
Abstract
TiAl alloys are used in high-temperature components such as the turbine blades of aeroengines because of their excellent properties. However, TiAl alloys are prone to thermal corrosion when in near-ocean service. In order to solve this problem, a hot-corrosion-resistant CrAl/NiCoCrAlY/AlSiY gradient composite coating was prepared on the surface of the TiAl alloy. The phase composition and morphology of the coating were analyzed. Hot corrosion tests of the traditional NiCoCrAlY coating and CrAl/NiCoCrAlY/AlSiY gradient composite coating on a TiAl substrate were performed. The samples were coated with 75%Na2SO4 + 25%NaCl salt film and treated at 950 °C for 100 h, and the corrosion products were analyzed. The results indicate that compared with the TiAl substrate and traditional NiCoCrAlY-coated samples, the composite coating showed better hot corrosion resistance, only slightly cracking, and no corrosion loss occurred. This is mainly because the continuous Al2O3 layer can effectively resist the damage caused by the melting reaction in salt, and the Cr-rich layer can not only slow the mutual diffusion of elements but also generate a good corrosion resistance chromium oxide protective layer under serious corrosion. Moreover, the corrosion mechanism of the TiAl substrate, traditional NiCoCrAlY coating, and experimental composite coating was analyzed in detail.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Intermetallics and Advanced Alloy Properties · High-Temperature Coating Behaviors · High Entropy Alloys Studies
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
College of Materials Science and Technology, Nanjing University of Aeronautics and Astronautics, Nanjing 210016, China
Wuxi Research Institute, Nanjing University of Aeronautics and Astronautics, Nanjing 210016, China
National Key Laboratory of Advanced Composites, AECC Beijing Institute of Aeronautical Materials, Beijing 100095, China
Institute of Wenzhou, Zhejiang University, Wenzhou 325006, China
Funding
National Major Science and Technology Projects of China · National Natural Science foundation of China
References (30)
Show source-provided references
1. Tetsui, T. (2024). Identifying low-cost, machinable, impact-resistant TiAl alloys suitable for last-stage turbine blades of jet engines. Intermetallics, 168.10.1016/j.intermet.2024.108263 ↗
2. Gao, Z., Hu, R., Zou, H., Zhou, M., and Luo, X. (2024). Insight into the Ta alloying effects on the oxidation behavior and mechanism of cast TiAl alloy. Mater. Design, 241.10.1016/j.matdes.2024.112941 ↗
3. Tribological Properties of γ-TiAl Alloy Fretting against Nickel-Based Superalloy at Elevated Temperature10.1080/10402004.2024.2320708 ↗
4. Swadźba, R., Swadźba, L., Mendala, B., Bauer, P.P., Laska, N., and Schulz, U. (2020). Microstructure and cyclic oxidation resistance of Si-aluminide coatings on γ-TiAl at 850 °C. Surf. Coat. Technol., 403.10.1016/j.surfcoat.2020.126361 ↗
5. Garip, Y. (2020). Investigation of isothermal oxidation performance of TiAl alloys sintered by different processing methods. Intermetallics, 127.10.1016/j.intermet.2020.106985 ↗
6. Dai, J., Sun, C., Wang, A., Zhang, H., Li, S., and Zhang, H. (2021). High temperature oxidation and hot corrosion behaviors of Ti2AlNb alloy at 923 K and 1023 K. Corros. Sci., 184.10.1016/j.corsci.2021.109336 ↗
7. Corrosion failures in gas turbine hot components10.1007/s11668-012-9571-3 ↗
8. Hot salt corrosion behavior of the Ti-44Al-4Nb-1.5Mo-(B,Y) alloy in the temperature range of 750-950 °C10.1016/j.jmrt.2023.08.220 ↗
9. Corrosion resistance and interfacial morphologies of a high Nb-containing TiAl alloy with and without thermal barrier coatings in molten salts10.1016/j.corsci.2019.05.011 ↗
10. NaCl-induced hot corrosion of a titanium aluminide alloy10.1016/0921-5093(95)03345-9 ↗
11. Inter-phase selective corrosion of γ-TiAl alloy in molten salt environment at high temperature10.1016/S1002-0071(12)60064-1 ↗
12. Gong, X., Chen, R.R., Wang, Y., Su, Y.Q., Guo, J.J., and Fu, H.Z. (2021). Microstructure and Oxidation Behavior of NiCoCrAlY Coating with Different Sm2O3 Concentration on TiAl Alloy. Front. Mater., 8.10.3389/fmats.2021.710431 ↗
13. Tian, S.W., Zhang, Y.F., Liu, J.H., Zeng, S.W., and Jiang, H.T. (2022). Interdiffusion mechanism at the interface between TiAl alloy and NiCoCrAlY bond coating. Surf. Coat. Technol., 444.10.1016/j.surfcoat.2022.128687 ↗
14. Han, D.J., Liu, D.D., Niu, Y.R., Qi, Z.X., Pan, Y.Y., Xu, H., Zheng, X.B., and Chen, G. (2021). Interface stability of NiCrAlY coating without and with a Cr or Mo diffusion barrier on Ti-42Al-5Mn alloy. Corros. Sci., 188.10.1016/j.corsci.2021.109538 ↗
15. Xue, G., Wang, Z., Xiang, L., Xiao, H., Zhao, Y., Wan, Y., Ning, H., and Xie, Z. (2022). Enhancing hot corrosion performance of NiCoCrAlY/AlSiY coating by arc enhanced glow discharge. Mater. Lett. X, 13.10.1016/j.mlblux.2022.100130 ↗
16. Formation process and oxidation behavior of MCrAlY + AlSiY composite coatings on a Ni-based superalloy10.1016/j.jmst.2021.10.055 ↗
17. Xue, G.M., Wang, Z.G., Wang, E.L., Tang, Y., Zhao, Y.H., Wang, Y.H., Hu, S.Y., Xiang, L., and Xie, Z.W. (2021). Enhanced Hot Salt-Water Corrosion Resistance of NiCoCrAlY-AlSiY Coating by Ion-Beam-Assisted Deposition. Coatings, 11.10.3390/coatings11091062 ↗
18. Zeng, S., Li, J., Chen, C., Meng, Y., Zhu, C.W., Bao, Y.W., Han, X.C., and Zhang, H.B. (2023). Oxidation behavior of CrAl coating with and without Nb addition in high temperature steam environment. J. Nucl. Mater., 581.10.1016/j.jnucmat.2023.154437 ↗
19. Xu, M., Li, S., Dong, Z., Liu, H., Wang, J., Bao, Z., Zhu, S., and Wange, F.H. (2023). High temperature performance and interface evolution of a NiCoCrAlY coating with Pt modification and Re-based diffusion barrier. Surf. Coat. Technol., 463.10.1016/j.surfcoat.2023.129510 ↗
20. Thermodynamic assessment of the Al-Ni system10.1016/0925-8388(95)02085-3 ↗
21. Microstructure and hot corrosion properties of an Al-Y coating on TiAl alloy10.1007/s11771-024-5561-3 ↗
22. Wang, D., Xiao, R., Qu, G., and Zhou, X. (2021). Influences of Laser Remelting on Hot Corrosion Resistance of Plasma-sprayed Nanostructured Al2O3-13wt.%TiO2 Coating. J. Phys. Conf. Ser., 1965.10.1088/1742-6596/1965/1/012084 ↗
23. Structure and Hot Corrosion Behavior of an Al-Co-Y Co-deposited Coating on TiAl Alloy10.1007/s11665-022-07481-1 ↗
24. Microstructure and hot corrosion resistance of Si-Al-Y coated TiAl alloy10.1007/s11771-020-4478-8 ↗
25. Comparative study of hot corrosion behavior of the enamel based composite coatings and the arc ion plating NiCrAlY on TiAl alloy
26. Hot corrosion resistance of plasma-sprayed MCrAlY coatings by laser remelting on TiAl alloy surface TiAl
27. Study on Hot Corrosion Behavior of Plasma-Sprayed NiCoCrAl-Y2O3 Coating on TiAl Alloy Surface
28. Hot corrosion of materials: A fluxing mechanism?10.1016/S0010-938X(01)00057-9 ↗
29. The preparation and hot corrosion resistance of gradient NiCoCrAlYSiB coatings10.1016/j.surfcoat.2004.12.005 ↗
30. Oxidation behavior of γ-TiAl alloy with NiCrAlY/Al duplex coating at 950 °C