Unraveling the Cracking Mechanisms of Air Plasma-Sprayed Thermal Barrier Coatings: An In-Situ SEM Investigation
Source abstract
Abstract
In this research work, real-time three-point bending coupled with the scanning electron microscopy (SEM) technique were used to study the crack formation and growth of air plasma spraying (APS) thermal barrier coatings (TBCs). The acquired micrographs were then used to study the strain fields in the vicinity of the cracking region using digital image correlation (DIC) analysis. Fractography analysis for the fractured regions of the APS coatings was also discussed. Based on real-time observation, it was found that roughness of the coatings’ free surface (e.g., valleys) can promote the initiation of cracks since it acts as stress concentration points. Pores and splats features of the coating microstructure contribute to crack branching and crack path deflection, respectively. The former phenomenon (i.e., crack branching) negatively affects the lifetime of the TBC system as it results in an increased fracture area, while the latter can improve the fracture toughness of the coatings and its durability through improving the coating’s ability to dissipate the energy required for crack propagation.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: High-Temperature Coating Behaviors · Advanced ceramic materials synthesis · Metal and Thin Film Mechanics
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Centre for Manufacturing and Materials, Coventry University, Coventry CV1 5FB, UK
Thermal Spray Innovations, 5662 Salzburg, Austria
CN Technical Services Ltd., Wisbech PE13 2XQ, UK
References (49)
Show source-provided references
1. Thermal Barrier Coatings for Gas Turbine Use10.1016/0921-5093(89)90798-3 ↗
2. The Effects of Coating Materials in Spark Ignition Engine Design10.1016/j.matdes.2011.11.053 ↗
3. Thermal Barrier Coatings for Gas-Turbine Engine Applications10.1126/science.1068609 ↗
4. Advanced Thermal Spray Technologies for Applications in Energy Systems10.1016/j.surfcoat.2008.04.022 ↗
5. Thermal Barrier Coatings Overview: Design, Manufacturing, and Applications in High-Temperature Industries10.1021/acs.iecr.1c00788 ↗
6. Application of Thermal Barrier Coating for Improving the Suitability of Annona Biodiesel in a Diesel Engine10.2298/TSCI16S4973R ↗
7. Gao, W., and Li, Z.B.T. (2008). Developments in High Temperature Corrosion and Protection of Materials, Woodhead Publishing.10.1533/9781845694258 ↗
8. In-Situ Observation of Crack Propagation in Thermally Sprayed Coatings10.1016/j.surfcoat.2010.03.064 ↗
9. Evaluation of Failure Micromechanisms of Advanced Thermal Spray Coatings by In Situ Experiment10.4028/www.scientific.net/KEM.606.187 ↗
10. Mechanisms Controlling the Durability of Thermal Barrier Coatings10.1016/S0079-6425(00)00020-7 ↗
11. Gok, M.G., and Goller, G. (2019). Methods for Film Synthesis and Coating Procedures, InTech Open.
12. Non-Linear Mechanical Behavior of Plasma Sprayed Alumina under Mechanical and Thermal Loading10.1007/s11666-009-9362-x ↗
13. Deformation and Strain Distribution in Plasma Sprayed Nickel-Aluminum Coating Loaded by a Spherical Indenter10.1016/S0921-5093(03)00414-3 ↗
14. Modified Indentation Techniques to Probe Inelasticity in Ni-5% Al Coatings from Different Processes10.1007/s11666-008-9243-8 ↗
15. Fracture Characteristics of Thermal Barrier Coatings after Tensile and Bending Tests10.1016/S0257-8972(02)00154-8 ↗
16. Fatigue Behavior of Bodies with Thermally Sprayed Metallic and Ceramic Deposits10.1007/s11666-008-9205-1 ↗
17. Amer, M., Hayat, Q., Janik, V., Jennett, N., Nottingham, J., and Bai, M. (2022). A Review on In Situ Mechanical Testing of Coatings. Coatings, 12.10.3390/coatings12030299 ↗
18. Mechanical Behavior of Freestanding 8YSZ Thin Films under Tensile and Bending Loads10.1016/j.surfcoat.2020.125771 ↗
19. In-Situ and Real-Time Tests on the Damage Evolution and Fracture of Thermal Barrier Coatings under Tension: A Coupled Acoustic Emission and Digital Image Correlation Method10.1016/j.surfcoat.2013.12.010 ↗
20. In Situ Characterization of High Temperature Elastic Modulus and Fracture Toughness in Air Plasma Sprayed Thermal Barrier Coatings under Bending by Using Digital Image Correlation10.1016/j.ceramint.2020.04.158 ↗
21. Effect of Bond Coat Topography on the Fracture Mechanics and Lifetime of Air-Plasma Sprayed Thermal Barrier Coatings10.1016/j.surfcoat.2021.127447 ↗
22. Acoustic Emission Evaluation of Fracture Characteristics in Thermal Barrier Coatings under Bending10.1016/j.surfcoat.2013.06.085 ↗
23. Characterization of the Mechanical Properties of Thermal Barrier Coatings by 3 Points Bending Tests and Modified Small Punch Tests10.1016/j.surfcoat.2017.09.070 ↗
24. Bending-Driven Failure Mechanism and Modelling of Double-Ceramic-Layer Thermal Barrier Coating System10.1016/j.ijsolstr.2017.10.024 ↗
25. Measurements and Understanding of the Stiffness of an Air Plasma Sprayed Thermal Barrier Coating10.1016/j.surfcoat.2020.125678 ↗
26. Musalek, R., Vilemova, M., Matejicek, J., Rey, U., and Carlos, J. (2014, January 16–18). In-Situ Observation of Ongoing Microstructural Changes in Functionally Graded Thermal Spray Coating during Mechanical Loading. Proceedings of the Surface Modification Technologies XXVIII, Tampere, Finland.
27. Evaluating the Toughness of APS and HVOF-Sprayed Al2O3-ZrO2-Coatings by in-Situ-and Macroscopic Bending10.1016/j.jeurceramsoc.2017.11.056 ↗
28. Low Conductivity Plasma Sprayed Thermal Barrier Coating Using Hollow Psz Spheres: Correlation between Thermophysical Properties and Microstructure10.1016/j.surfcoat.2007.08.042 ↗
29. Next Generation Thermal Barrier Coatings for the Gas Turbine Industry10.1007/s11666-010-9593-x ↗
30. (2023, May 08). Haynes International HASTELLOY® X Alloy Principal Features. Available online: https://haynesintl.com/docs/default-source/pdfs/new-alloy-brochures/high-temperature-alloys/brochures/x-brochure.pdf?sfvrsn=15b829d4_40.
31. A Parametric Study of the Stress State of Thermal Barrier Coatings: Part I: Creep Relaxation
32. Characterization Techniques for Nanotechnology Applications in Textiles
33. High-resolution Scanning Electron Microscopy of Immunogold-labelled Cells by the Use of Thin Plasma Coating of Osmium10.1046/j.1365-2818.2002.01082.x ↗
34. Imaging with Backscattered Electrons in a Scanning Electron Microscope10.1002/sca.4950030103 ↗
35. (2002). Standard Test Method for Flexural Strength of Advanced Ceramics at Ambient Temperature (Standard No. ASTM C1161-02).
36. Gere, J.M. (2004). Mechanics of Materials, Thomson Learning.
37. (2017). Standard Test Methods for Flexural Properties of Unreinforced and Reinforced Plastics and Electrical Insulating Materials (Standard No. ASTM D790-17).
38. The State of the Art of Two-dimensional Digital Image Correlation Computational Method10.1002/eng2.12038 ↗
39. Ncorr: Open-Source 2D Digital Image Correlation Matlab Software10.1007/s11340-015-0009-1 ↗
40. Reliability-Guided Digital Image Correlation for Image Deformation Measurement10.1364/AO.48.001535 ↗
41. Numerical Analyses of the Residual Stress and Top Coat Cracking Behavior in Thermal Barrier Coatings under Cyclic Thermal Loading10.1016/j.engfracmech.2018.04.031 ↗
42. Effect of Bond-Coat Surface Roughness on Failure Mechanism and Lifetime of Air Plasma Spraying Thermal Barrier Coatings10.1007/s11431-017-9236-x ↗
43. Effect of Non-Uniform Growth of TGO Layer on Cracking Behaviors in Thermal Barrier Coatings: A Numerical Study10.1016/j.surfcoat.2019.04.069 ↗
44. Toughening Mechanism of Thermal Barrier Coatings10.1007/s10765-021-02820-1 ↗
45. Toughening Mechanisms for Ceramic Materials10.1016/0955-2219(92)90026-A ↗
46. Enhancing the Hot-Corrosion Resistance of Atmospheric Plasma Sprayed Ni-Based Coatings by Adding a Deoxidizer10.1016/j.matdes.2021.110154 ↗
47. A State-of-the-Art Review of Crack Branching10.1016/j.engfracmech.2021.108036 ↗
48. LXXV. The Moving Griffith Crack10.1080/14786445108561302 ↗
49. An Experimental Investigation into Dynamic Fracture: III. On Steady-State Crack Propagation and Crack Branching10.1007/BF01157550 ↗