A Comparative Study of Chloride Adsorption Ability and Corrosion Protection Effect in Epoxy Coatings of Various Layered Double Hydroxides
Source abstract
Abstract
The positive influence of chloride adsorption on the enhanced protection effect was always emphasized in the published literature. The concrete contribution of chloride adsorption and physical barrier effect of LDH in coatings still remains unclear at present. This work was aimed at exploring the significance of the chloride adsorption role of LDH in the corrosion protection of epoxy coatings. The synthesized LDH samples were characterized by scanning electronic microscopy (SEM), X-ray diffraction (XRD) and Fourier transform infrared spectroscopy (FTIR) to show the influence of different parameters on its morphology, structure and composition, respectively. The corrosion-electrochemical behavior was investigated using electrochemical impedance spectroscopy (EIS) and salt spray test. It was found that although CaAl-LDH presented a lower chloride adsorption ability in comparison with other samples; it showed effective corrosion protection due to the higher physical barrier effect of CaAl-LDH with typically hexagonal and plate-like morphology due to good compatibility with the epoxy coatings. The results indicated that the corrosion protection effect of the incorporated LDH was more closely related to its physical barrier role rather than the role of the chloride adsorption, which was misunderstood in the previous publications. This work clarified the contribution comparison of the chloride adsorption and physical barrier of LDH in epoxy coating corrosion protection for the first time.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Layered Double Hydroxides Synthesis and Applications · Corrosion Behavior and Inhibition · Magnesium Oxide Properties and Applications
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Luoyang Ship Material Research Institute, Xiamen 361101, China
Science and Technology on Marine Corrosion and Protection Laboratory, Xiamen 361101, China
China Ship Development and Design Center, Wuhan 430064, China
Liaoning Provincial Key Laboratory for Preparation and Application of Special Functional Materials, Shenyang University of Chemical Technology, Shenyang 110142, China
Funding
State Key Laboratory for Marine Corrosion and Protection Foundation · Xiamen Science and Technology Plan Project
References (45)
Show source-provided references
1. Phosphate ions as corrosion inhibitors for reinforcement steel in chloride-rich environments10.1016/j.electacta.2013.03.180 ↗
2. PEO coatings with active protection based on in-situ formed LDH-nanocontainer10.1149/2.0301702jes ↗
3. Achieving high performance corrosion and wear resistant epoxy coatings via incorporation of noncovalent functionalized graphene10.1016/j.carbon.2016.12.044 ↗
4. Self-healing coatings using superabsorbent polymers for corrosion inhibition in carbon steel10.1016/j.corsci.2012.03.007 ↗
5. Influence of embedded ZnAlCe-NO3− layered double hydroxides on the anticorrosion properties of sol–gel coatings for aluminum alloy10.1016/j.porgcoat.2014.12.015 ↗
6. Incorporation of layered double hydroxides modified with benzotriazole into an epoxy resin for the corrosion protection of Zn-Mg coated steel10.1016/j.porgcoat.2020.105894 ↗
7. Enhancing corrosion resistance of epoxy coating on steel reinforcement by aminobenzoate intercalated layered double hydroxides10.1016/j.porgcoat.2019.05.023 ↗
8. Improving the corrosion protection ability of epoxy coating using CaAl LDH intercalated with 2-mercaptobenzothiazole as a pigment on steel substrate10.1016/j.porgcoat.2022.106765 ↗
9. Fatigue and tensile behaviors of fiber-reinforced thermosetting composites embedded with nanoparticles10.1177/0021998318790093 ↗
10. Mechanical properties of linear low-density polyethylene fire-retarded with melamine polyphosphate10.1002/app.46770 ↗
11. Synthesis of inhibitor nanocontainers with two-dimensional structure and their anticorrosion action in sol-gel coating on AA2024-T3 aluminum alloy10.1149/2.0851712jes ↗
12. To TXH Molybdate intercalated hydrotalcite/graphene oxide composite as corrosion inhibitor for carbon steel10.1016/j.surfcoat.2020.126165 ↗
13. Wang H A smart anti-corrosion coating based on triple functional fillers10.1016/j.cej.2022.137078 ↗
14. Multifunctional inhibition based on layered double hydroxides to comprehensively control corrosion of carbon steel in concrete10.1016/j.corsci.2017.06.026 ↗
15. A composite corrosion inhibitor of MgAl layered double hydroxides co-intercalated with hydroxide and organic anions for carbon steel in simulated carbonated concrete pore solutions10.1149/2.0141911jes ↗
16. Insight into the Fabrication of ZnAl Layered Double Hydroxides Intercalated with Organic Anions and Their Corrosion Protection of Steel Reinforced Concrete10.1149/2.0361916jes ↗
17. Enhanced corrosion resistance of superhydrophobic layered double hydroxide films with long-term stability on Al substrate10.1021/acsami.8b02280 ↗
18. Enhanced corrosion protection by Al surface immobilization of in-situ grown layered double hydroxide films co-intercalated with inhibitors and low surface energy species10.1016/j.corsci.2019.108340 ↗
19. Construction of ecofriendly anticorrosive composite film ZnAl-LDH by modification of lignin onAA7075 surface10.1002/maco.202112402 ↗
20. Iqbal, M.A., Sun, L., Asghar, H., and Fedel, M. (2020). Chlorides Entrapment Capability of Various In-Situ Grown NiAl-LDHs: Structural and Corrosion Resistance Properties. Coatings, 10.10.3390/coatings10040384 ↗
21. Wang, Y., Huang, Q., Zhou, B., Yuan, Z., Wei, Y., and Fujita, T. (2021). Corrosion Protection of 6061 Aluminum Alloys by Sol-Gel Coating Modified with ZnLaAl-LDHs. Coatings, 11.10.3390/coatings11040478 ↗
22. Cao, Y., Fang, S., Chen, K., Qi, H., Zhang, X., Huang, C., Wang, J., and Liu, J. (2022). Insight into the Preparation of MgAl-Layered Double Hydroxide (LDH) Intercalated with Nitrates and Chloride Adsorption Ability Study. Appl. Sci., 12.10.3390/app12094492 ↗
23. Chloride binding capacity of LDHs with various divalent cations and divalent to trivalent cation ratios in different solutions10.1039/C9CE01322A ↗
24. Preparation of two-dimensional boron nitride-layered double hydroxide hybrid to reinforce the corrosion protection of the epoxy coating10.1002/maco.202112953 ↗
25. (2016). Electrochemical Impedance Spectroscopy (EIS) on Coated and Uncoated Metallic Specimens (Standard No. ISO 16773-2016).
26. (2007). Paints and Varnishes—Determination of Resistance to Neutral Salt Spray (Fog) (Standard No. GB/T 1771-2007).
27. Active protection coatings with layered double hydroxide nanocontainers of corrosion inhibitor10.1016/j.corsci.2009.10.020 ↗
28. Insitu grown superhydrophobic Zn–Al layered double hydroxides films on magnesium alloy to improve corrosion properties10.1016/j.apsusc.2015.02.086 ↗
29. One-step hydrothermal crystallization of a layered double hydroxide/alumina bilayer film on aluminum and its corrosion resistance properties10.1021/la901012w ↗
30. One-pot scalable in situ growth of highly corrosion-resistant MgAl-LDH/MBT composite coating on magnesium alloy under mild conditions10.1016/j.jmst.2021.03.021 ↗
31. In situ growth of corrosion resistant Mg-Fe layered double hydroxide film on Q235 steel10.1016/j.jcis.2021.12.018 ↗
32. Electrodeposited Zn-Al layered double hydroxide films for corrosion protection of aluminum alloys10.1016/j.electacta.2020.136796 ↗
33. Anion exchange in Zn–Al layered double hydroxides: In situ X-ray diffraction study10.1016/j.cplett.2010.06.041 ↗
34. MgAl-V2O74- LDHs/(PEI/MXene)10 composite film for magnesium alloy corrosion protection10.1016/j.jmst.2021.03.011 ↗
35. Effect of physical barrier and anion-exchange process of nitrate-intercalated ZnAl layered double hydroxide films grown on Al on corrosion protection10.1016/j.surfcoat.2021.127436 ↗
36. Zn–Al layered double hydroxides as chloride nanotraps in active protective coatings10.1016/j.corsci.2011.10.003 ↗
37. Ce-substituted Mg-Al layered double hydroxides to prolong the corrosion protection lifetime of aluminium alloys10.1016/j.apsusc.2021.151527 ↗
38. Facile preparation of wear-resistant and anti-corrosion films on magnesium alloy10.1080/02670844.2021.2025312 ↗
39. Fabrication and characterization of Mg–Mn hydrotalcite films on pure Mg substrates10.1088/2053-1591/ab3528 ↗
40. The effect of cerium cation on the microstructure and anti-corrosion performance of LDH conversion coatings on AZ31 magnesium alloy10.1016/j.jallcom.2019.153248 ↗
41. Chloride removal and corrosion inhibitions of nitrate, nitrite-intercalated Mg Al layered double hydroxides on steel in saturated calcium hydroxide solution10.1016/j.clay.2018.07.023 ↗
42. Chloride adsorption on aminobenzoate intercalated layered double hydroxides: Kinetic, thermodynamic and equilibrium studies10.1016/j.clay.2020.105495 ↗
43. Developing epoxy-based anti-corrosion functional nanocomposite coating with CaFe-Tolyl-triazole layered double hydroxide@g-C3N4 as nanofillers on Q235 steel substrate against NaCl corrosive environment10.1016/j.cej.2022.137624 ↗
44. Composite nanocontainers synthesized by in-situ growth of metal organic frameworks on layered double hydroxides having both passive and active protecting capabilities10.1016/j.porgcoat.2021.106695 ↗
45. Construction of an epoxy coating with excellent protection performance on the AA 2024-T3 using ion-exchange materials loaded with eco-friendly corrosion inhibitors10.1016/j.porgcoat.2022.106786 ↗