Health and Durability of Protective and Thermal Barrier Coatings Monitored in Service by Visual Inspection
Source abstract
Abstract
Protective and Thermal Barrier Coatings (TBC) applied on gas-turbine blades gradually degrade due to oxidation, aluminum depletion and impacts of environmental particles. Among various non-destructive coating testing methods (NDT), visual inspection can be undertaken regularly in service, but it provides little quantitative information, and only surface defects can be detected. This work aims at in-service monitoring of turbine blades with multilayer coatings applied by atmospheric plasma spraying (APS) in a few variants. They were validated during a series of accelerated mission tests of a retired military turbofan engine in a test cell together with five other technologies. The fifty-hour rainbow test focused on assessing coating durability. Between engine runs, 12 borescope inspections were conducted to monitor the health of the blades. Finally, the blades were disassembled and examined using computed tomography (CT) and metallographic methods. Throughout the testing, 31 newly-coated blades (66%) withstood the tests, producing results comparable to the reference blades. However, 16 blades suffered intolerable failures observed as increased roughness, gradual loss of the topcoat, spallation and minor foreign object damage. Visual inspection results were generally in agreement with subsequent laboratory tests.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: High-Temperature Coating Behaviors · Laser-induced spectroscopy and plasma · Vacuum and Plasma Arcs
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Instytut Techniczny Wojsk Lotniczych (ITWL), 6 Księcia Bolesława Street, 01-494 Warsaw, Poland
Funding
National Centre for Research and Development
References (69)
Show source-provided references
1. Ozgurluk, Y., Doleker, K.M., Ozkan, D., Ahlatci, H., and Karaoglanli, A.C. (2019). Cyclic hot corrosion failure behaviors of EB-PVD TBC systems in the presence of sulfate and vanadate molten salts. Coatings, 9.10.3390/coatings9030166 ↗
2. Song, D., Song, T., Paik, U., Lyu, G., Jung, Y.G., Choi, B.G., Kim, I.S., and Zhang, J. (2019). Crack-growth behavior in thermal barrier coatings with cyclic thermal exposure. Coatings, 9.10.3390/coatings9060365 ↗
3. Kopec, M., Kukla, D., Yuan, X., Rejmer, W., Kowalewski, Z.L., and Senderowski, C. (2021). Aluminide Thermal Barrier Coating for High Temperature Performance of MAR 247 Nickel Based Superalloy. Coatings, 11.10.3390/coatings11010048 ↗
4. Goral, M., Pytel, M., Ochal, K., Drajewicz, M., Kubaszek, T., Simka, W., and Nieuzyla, L. (2021). Microstructure of aluminide coatings modified by Pt, Pd, Zr and Hf formed in low-activity CVD process. Coatings, 11.10.3390/coatings11040421 ↗
5. Kościelniak, B., Chmiela, B., Sozańska, M., Swadźba, R., and Drajewicz, M. (2021). Oxidation Behavior of Inconel 740H Nickel Superalloy in Steam Atmosphere at 750 °C. Materials, 14.10.3390/ma14164536 ↗
6. Tamarin, Y. (2002). Protective Coatings for Turbine Blades, ASM International.
7. Failure Prevention of Gas Turbine Blades Through Pack Aluminization10.1007/s11668-018-0498-1 ↗
8. PVD TBC experience on GE aircraft engines10.1007/s11666-997-0012-x ↗
9. Microstructure degradation of EB-PVD TBCs on Pd-Pt-modified aluminide coatings under cyclic oxidation conditions10.1016/j.surfcoat.2013.09.022 ↗
10. Lifetime improvement of EB-PVD 7YSZ TBCs by doping of Hf or Zr in NiCoCrAlY bond coats10.1016/j.corsci.2020.109205 ↗
11. Cold spray for production of in-situ nanocrystalline MCrAlY coatings – Part I: Process analysis and microstructure characterization10.1016/j.surfcoat.2021.126854 ↗
12. Li, X., Peng, X.Y., Dong, H., Zhou, Y., Wang, T., Ren, K., and Sun, L. (2019). The Evaluation of Durability of Plasma-Sprayed Thermal Barrier Coatings with Double-layer Bond Coat. Coatings, 9.10.3390/coatings9040241 ↗
13. Nicolaus, M., Möhwald, K., and Maier, H.J. (2021). Thermally Sprayed Nickel-Based Repair Coatings for High-Pressure Turbine Blades: Controlling Void Formation during a Combined Brazing and Aluminizing Process. Coatings, 11.10.3390/coatings11060725 ↗
14. Liebert, C.H., and Levine, S.R. (1982). Further Industrial Tests of Ceramic Thermal-Barrier Coatings, NASA Lewis Research Center. NASA Technical Paper 2057.
15. Savinkin, V.V., Vizureanu, P., Sandu, A.V., Ratushnaya, T.Y., Ivanischev, A.A., and Surleva, A. (2020). Improvement of the turbine blade surface phase structure recovered by plasma spraying. Coatings, 10.10.3390/coatings10010062 ↗
16. Ghadami, F., Davoudabadi, M.A., and Ghadami, S. (2022). Cyclic Oxidation Properties of the Nanocrystalline AlCrFeCoNi High-Entropy Alloy Coatings Applied by the Atmospheric Plasma Spraying Technique. Coatings, 12.10.20944/preprints202202.0252.v1 ↗
17. The Study on Delamination Life of TBC through Burner-Rig Test10.1007/s12541-017-0066-8 ↗
18. Shahoo, P., and Sobieski, P.A. (2007, January 14–17). Performance Characteristics of Thermal Barrier Coatings: A Case Study. Proceedings of the ASME Turbo Expo 2007: Power for Land, Sea and Air, Montreal, QC, Canada.10.1115/GT2007-28352 ↗
19. Witz, G., Schaudinn, M., Sopka, J., and Buecklers, T. (2016, January 13–17). Development of Advanced Thermal Barrier Coatings with Improved Temperature Capability. Proceedings of the ASME Turbo Expo 2016: Turbomachinery Technical Conference and Exposition, Seoul, Korea.10.1115/GT2016-57425 ↗
20. Microstructural characteristics and oxidation behavior of the modified MCrAlX coatings: A critical review10.1016/j.vacuum.2020.109980 ↗
21. Hu, Z.C., Liu, B., Wang, L., Cui, Y.H., Wang, Y.W., Ma, Y.D., Sun, W.W., and Yang, Y. (2020). Research Progress of Failure Mechanism of Thermal Barrier Coatings at High Temperature via Finite Element Method. Coatings, 10.10.3390/coatings10080732 ↗
22. Chang, S., and Oh, K.Y. (2019). Contribution of High Mechanical Fatigue to Gas Turbine Blade Lifetime during Steady-State Operation. Coatings, 9.10.3390/coatings9040229 ↗
23. Wei, Z.Y., and Cai, H.N. (2021). Understanding the Failure Mechanism of Thermal Barrier Coatings Considering the Local Bulge at the Interface between YSZ Ceramic and Bond Layer. Materials, 15.10.3390/ma15010275 ↗
24. Effects of Thermal Barrier Coatings on Diesel and Gas turbine engines: A review
25. Abdul-Aziz, A., and Wroblewski, A. (2016). Durability Analysis and Experimental Validation of Environmental Barrier Coating (EBC) Performance Using Combined Digital Image Correlation and NDE. Coatings, 6.10.3390/coatings6040070 ↗
26. Mevissen, F., and Meo, M. (2019). A Review of NDT/Structural Health Monitoring Techniques for Hot Gas Components in Gas Turbines. Sensors, 19.10.3390/s19030711 ↗
27. Non-Destructive Measurement of Top Coat Thickness in TBC Systems by 3D Optical Topometry10.1080/10589759.2014.984297 ↗
28. Recent Progress in Turbine Blade and Compressor Blisk Regeneration10.1016/j.procir.2014.07.016 ↗
29. Kukla, D., Kopec, M., Sitek, R., Olejnik, A., Kachel, S., and Kiszkowiak, Ł. (2021). A Novel Method for High Temperature Fatigue Testing of Nickel Superalloy Turbine Blades with Additional NDT Diagnostics. Materials, 14.10.3390/ma14061392 ↗
30. Bruchwald, O., Nicolaus, M., Frackowiak, W., Reimche, W., Möhwald, K., and Maier, H.J. (2016, January 13–17). Material characterization of thin coatings using high frequency eddy current technology. Proceedings of the 19th World Conference on Non-Destructive Testing (WCNDT 2016), Munich, Germany.
31. Ultrasonic Detection of Delamination and Material Characterization of Thermal Barrier Coatings10.1007/s11666-012-9811-9 ↗
32. Porosity Characterization of Thermal Barrier Coatings by Ultrasound with Genetic Algorithm Backpropagation Neural Network10.1155/2021/8869928 ↗
33. Hastie, S., Chan, A., Wiens, K., Nagy, D., Tollett, R., and Lowden, P. (2021, January 7–11). Computed Tomography Wall Thickness Inspection to Support Gas Turbine Blade Life Extension. Proceedings of the ASME Turbo Expo 2021: Turbomachinery Technical Conference and Exposition, Virtual.10.1115/GT2021-60316 ↗
34. CT Inspection of Cooled Turbine Blades10.2478/jok-2020-0064 ↗
35. Investigation of Interfacial Properties of Atmospheric Plasma Sprayed Thermal Barrier Coatings with Four-Point Bending and Computed Tomography Technique10.1016/j.surfcoat.2012.05.099 ↗
36. Błachnio, J., Chalimoniuk, M., Kułaszka, A., Borowczyk, H., and Zasada, D. (2021). Exemplification of Detecting Gas Turbine Blade Structure Defects Using the X-ray Computed Tomography Method. Aerospace, 8.10.3390/aerospace8040119 ↗
37. Thermophysical properties of multiphase Fe-Al intermetallic-oxide ceramic coatings deposited by gas detonation spraying10.1016/j.tca.2019.04.009 ↗
38. Thermal conductivity analysis and lifetime testing of suspension plasma-sprayed thermal barrier coatings10.3390/coatings4030630 ↗
39. Artificial Disbonds for Calibration of Transient Thermography Inspection of Thermal Barrier Coating Systems10.1016/j.ndteint.2011.09.008 ↗
40. Application of Pulsed Thermography to Quality Assurance of Thermal Barrier Coatings10.1177/0954410011414312 ↗
41. Chung, Y., Lee, S., and Kim, W. (2021). Latest Advances in Common Signal Processing of Pulsed Thermography for Enhanced Detectability: A Review. Appl. Sci., 11.10.3390/app112412168 ↗
42. Assessment of usability of the exploited gas turbine blade heat-resistant coatings10.1016/j.engfailanal.2019.07.016 ↗
43. Wang, Y., Gao, X., and Netzelmann, U. (2018, January 25–29). Detection of Surface Cracks in Metals under Coatings by Induction Thermography. Proceedings of the 2018 International Conference on Quantitative InfraRed Thermography, QIRT Council, Berlin, Germany.10.21611/qirt.2018.064 ↗
44. Linear Laser Fast Scanning Thermography NDT for Artificial Disbond Defects in Thermal Barrier Coatings10.1364/OE.25.031789 ↗
45. Muzika, L., Svantner, M., Honner, M., and Houdkova, S. (2021). Laser Scanning Thermography for Coating Thickness Inspection. Eng. Proc., 8.10.3390/engproc2021008017 ↗
46. Nondestructive Inspection of Thermal Barrier Coating of Gas Turbine High Temperature Components10.1002/tee.22255 ↗
47. Non-Destructive Thickness Measurement of Thermal Barrier Coatings Using Terahertz Radiation10.1007/s42247-021-00275-6 ↗
48. Nondestructive Evaluation of Thermal Barrier Coating Thickness Degradation Using Pulsed IR Thermography and THz-TDS Measurements: A Comparative Study10.1016/j.ndteint.2020.102367 ↗
49. Thermographic Inspection of TBC Coated Gas Turbine Blades: Discrimination between Coating over-Thicknesses and Adhesion Defects10.1016/j.infrared.2006.06.018 ↗
50. Frackowiak, W., Barton, S., Reimche, W., Bruchwald, O., Zaremba, D., Schlobohm, J., Li, Y., Kaestner, M., and Reithmeier, E. (2018, January 11–15). Near-Wing Multi-Sensor Diagnostics of Jet Engine Components. Proceedings of the ASME Turbo Expo 2018: Turbomachinery Technical Conference and Exposition, Oslo, Norway.10.1115/GT2018-76793 ↗
51. Advanced Characterization Techniques for Turbine Blade Wear and Damage10.1016/j.procir.2016.09.005 ↗
52. Laser deposited high temperature thin film sensors for gas turbines10.1108/AEAT-11-2018-0292 ↗
53. Feist, J. (2015, January 20–23). Luminescent Thermal History Sensors Fundamentals and Applications for Thermal Profiling. Proceedings of the STO-MP-AVT-229—Test Cell and Controls Instrumentation and EHM Technologies for Military Air, Land and Sea Turbine Engines, NATO STO, Rzeszów, Poland.
54. Measurements of turbine blade temperature in an operating aero engine using thermographic phosphors10.1088/1361-6501/ab4c20 ↗
55. Aust, J., Pons, D., and Mitrovic, A. (2022). Evaluation of Influence Factors on the Visual Inspection Performance of Aircraft Engine Blades. Aerospace, 9.10.3390/aerospace9010018 ↗
56. Thermal degradation of turbine components in a military turbofan10.1016/j.engfailanal.2022.106088 ↗
57. Bogdan, M., Błachnio, J., Kułaszka, A., and Zasada, D. (2021). Investigation of the Relationship between Degradation of the Coating of Gas Turbine Blades and Its Surface Color. Materials, 14.10.3390/ma14247843 ↗
58. Kozakiewicz, A., Jóźwiak, S., Jóźwiak, P., and Kachel, S. (2021). Material Origins of the Accelerated Operational Wear of RD-33 Engine Blades. Materials, 14.10.3390/ma14020336 ↗
59. Ion-plasma protective coatings for gas-turbine engine blades10.1134/S0036029507050047 ↗
60. Effect of Protective Coatings on Mechanical Properties of ZhS32-VI Heat-Resistant Alloy10.1007/s11223-010-9224-2 ↗
61. Swadzba, L., Maciejny, A., and Mendala, B. (2000, January 17–21). Overaluminising of NiCoCrAlY Coatings by Arc PVD on Ni-Base Superalloys. Proceedings of the Superalloys 2000 (Ninth International Symposium), Champion, PA, USA.10.7449/2000/Superalloys_2000_693_701 ↗
62. Evaluation of microstructural degradation in a failed gas turbine blade due to overheating10.1016/j.engfailanal.2019.04.021 ↗
63. Wee, S., Do, J., Kim, K., Lee, C., Seok, C., Choi, B.G., Choi, Y., and Kim, W. (2020). Review on mechanical thermal properties of superalloys and thermal barrier coating used in gas turbines. Appl. Sci., 10.10.3390/app10165476 ↗
64. Chen, K., Seo, D., and Canteenwalla, P. (2021). The Effect of High-Temperature Water Vapour on Degradation and Failure of Hot Section Components of Gas Turbine Engines. Coatings, 11.10.3390/coatings11091061 ↗
65. Applying Protective Coating on the Turbine Engine Turbine Blades by Means of Plasma Spraying10.2478/jok-2020-0012 ↗
66. Udalenie zharostojkih pokrytij s poverhnosti pera lopatok turbin v vodnyh malokoncentrirovannyh rastvorah (Removal of heat-resistant coatings from the surface of the turbine blade airfoil in aqueous low-concentrated solutions)
67. Gazturbinny Dwigatel RD-33 (2010). Rukawodstwo po Techniczeskoj Ekspluatcji (RD-33 Gas-Turbine Engine. Technical Maintenance Manual) 0088.00.1700 RE, Chernyshev Moscow Machine-Building Enterprise.
68. (2022, March 06). Mentor Visual iQ VideoProbe Intelligent Inspection Solutions. Available online: https://www.everestvit.pl/images/pdf/Mentor-Visual-iQ-Everest-Waygate-03-2020.pdf.
69. (2022, March 06). Mentor Visual iQ VideoProbe User’s Manual. Available online: https://www.instrumart.com/assets/MVIQ-manual.pdf.