Moisture Vapor Resistance of Coated and Laminated Breathable Fabrics Using Evaporative Wet Heat Transfer Method

This study examined the effects of the fiber materials, fabric structural parameters, and surface modification method on the moisture vapor resistance of coated and laminated fabrics according to the measuring method in comparison with evaporative wet heat transfer method. The moisture vapor resistance (Ref) of the coated and laminated fabrics measured using evaporative wet heat transfer method was much more precise than water vapor transmission rate (WVTR) and water vapor permeability (WVP) measured using American Society for Testing and Materials (ASTM) and Japanese Industrial Standard (JIS) methods. The correlation coefficient between Ref and WVTR in the laminated and coated polyethylene terephthalate (PET) fabric specimens was the highest, i.e., −0.833, and −0.715, in coated fabric specimens. Hence, selecting an appropriate measuring method according to the fabric materials and surface modification method is very critical. According to curvilinear regression analysis, the influential factor affecting breathability of the PET fabric specimens measured using evaporative wet heat transfer method was fabric weight (R2 = 0.847) and fabric thickness (R2 = 0.872) in the laminated fabric specimens. Meanwhile, as per multiple linear regression, the most influential fabric structural parameters affecting the breathability of laminated fabric specimens measured using evaporative wet heat transfer method were the fabric density, weight/thickness, and weight followed by the fabric thickness (R2 = 0.943). These results would be valid for laminated breathable fabrics with characteristics within the range of this study and are of practical use for engineering laminated fabrics with high breathability.