Enhancement Research on Piezoelectric Performance of Electrospun PVDF Fiber Membranes with Inorganic Reinforced Materials

The electrospun PVDF fiber membranes with the characteristics of light weight, strong signal and measurability, have been widely applied in the fields of environment, energy sensors and biomedical treatment. Due to the weakness of the piezoelectric and service properties, the conventional PVDF fiber membranes cannot meet the operating requirements. Based on the obtained optimal technological parameter of electrospun pure PVDF fiber membranes (P-PVDF) in the previous experiment (unpublished), three inorganic reinforced substances (AgNO3, FeCl3·6H2O, nanographene) were respectively used to dope and modify PVDF to prepare composite fiber membranes with the better piezoelectric performance. The morphology and crystal structure of the hybrid fiber membranes were observed and detected by scanning electron microscopy and X-ray diffraction, respectively. The results showed that the dopant could effectively promote the formation of β-phase, which can enhance the piezoelectric performance. The mechanical properties test and piezoelectric performance test exhibited that the static flexural strength, the elastic modulus, and the piezoelectric performance were improved with the addition of dopant. In addition, the influence on the addition of dopant and the doping modification mechanism were discussed. Finally, the conclusions showed that the minimum average diameter was obtained with the 0.3 wt% addition of AgNO3; the piezoelectric performance reached the strongest with the 0.8 wt% addition of FeCl3·6H2O; the mechanical properties were best with the 1.0 wt% addition of nanographene.