High Temperature Corrosion Behaviors of 20G Steel, Hastelloy C22 Alloy and C22 Laser Coating under Reducing Atmosphere with H2S
Source abstract
Abstract
High-temperature corrosion behaviors of 20G steel, Hastelloy C22 alloy and C22 laser coating was evaluated by corrosion mass gain measurements at 450 °C. The corrosive atmosphere is 0.2 vol% H2S–0.1 vol% O2–N2, which simulated the severe high-temperature corrosion environment occurred under low-NOx combustion in pulverized-coal furnaces. Experimental results showed that the corrosion resistance of the C22 laser coating and the C22 alloy was obviously better than 20G steel. Furthermore, it should be noted that the C22 laser coating fabricated in this study displayed a higher corrosion resistance than the commercial C22 alloy although they had the same chemical composition. The severe pitting corrosion was observed in 20G steel with the corrosion products consisting of FeS2, Fe2O3 and Fe3O4. The C22 alloy and C22 laser coating exhibited the uniform corrosion and their main corrosion products were NiS2, CrS and a small amount of chromium and manganese oxides.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: High-Temperature Coating Behaviors · Hydrogen embrittlement and corrosion behaviors in metals · Metal and Thin Film Mechanics
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Key Laboratory of Energy Transfer and System of Power Station of Ministry of Education, North China Electric Power University, Beijing 102206, China
Funding
the Fundamental Research Funds for the Central Universities
References (37)
Show source-provided references
1. Impact of air staging along furnace height on NOx emissions from pulverized coal combustion10.1016/j.fuproc.2010.01.009 ↗
2. Low NOx combustion technologies for high temperature applications10.1016/S0196-8904(01)00051-6 ↗
3. Control of combustion-generated nitrogen oxides by selective non-catalytic reduction10.1016/j.jenvman.2006.03.006 ↗
4. Effects of near-wall air application in a pulverized-coal 300 MWe utility boiler on combustion and corrosive gases10.1021/acs.energyfuels.7b01476 ↗
5. Hydrogen sulfide corrosion in low-NOx combustion systerms10.1007/BF02833575 ↗
6. Influence of the gas particle flow characteristics of a low-NOx swirl burner on the formation of high temperature corrosion10.1016/j.fuel.2014.06.027 ↗
7. Fireside corrosion in pc-fired boilers10.1016/0360-1285(90)90048-8 ↗
8. Xu, L.-G., Huang, Y.-J., Wang, J., Zou, L., and Yue, J.-F. (2018). High-temperature corrosion properties of water wall material 15CrMoG under reducing atmosphere. J. Zhejiang Univ. (Eng. Sci.), 52.
9. High temperature corrosion of water wall materials T23 and T24 in simulated furnace atmospheres10.1016/S1004-9541(11)60252-8 ↗
10. Xu, W., Tan, H., Liu, Y., Wei, B., and Hui, S.e. (2018). Research on determination of high temperature corrosion tendency of water walls and limiting concentration range of H2S near walls. Electr. Power, 51.
11. Jones, R.H., Baer, D.R., and Windisch, J.C.F. (2006, January 12–16). Corrosion enhanced enrichment of sulfur and implications for alloy 22. Proceedings of the NACE International Corrosion Conference, San Diego, CA, USA.
12. Stress corrosion cracking of metals and alloys in aggressive H2S–CO2–Cl– environments10.1134/S1063784219120211 ↗
13. The mechanism of stress corrosion cracking of alloy 600 in high temperature water10.1016/0010-938X(96)00183-7 ↗
14. Davis, J.R. (2000). Nickel, Cobalt, and Their Alloys, ASM International Materials Park. [1st ed.].
15. Pitting corrosion behaviour of austenitic stainless steels—Combining effects of Mn and Mo additions10.1016/j.corsci.2008.04.005 ↗
16. Sigma and random grain boundaries and their effect on the corrosion of the Ni-Cr-Mo alloy 2210.1149/2.1111605jes ↗
17. Jakupi, P., Noël, J.J., and Shoesmith, D.W. (2010). Intergranular corrosion resistance of ∑3 grain boundaries in alloy 22. Electrochem. Solid-State Lett., 13.10.1149/1.3272851 ↗
18. A comparative study on the high temperature corrosion of TP347H stainless steel, C22 alloy and laser-cladding C22 coating in molten chloride salts10.1016/j.corsci.2014.03.012 ↗
19. Crevice corrosion penetration rates of alloy 22 in chloride-containing waters10.5006/1.3278339 ↗
20. Corrosion product analysis on crevice corroded Alloy-22 specimens10.1016/j.corsci.2011.01.028 ↗
21. Effect of simulated ground water chemistry on stress corrosion cracking of alloy 2210.5006/1.3278312 ↗
22. The dissolution and passivation kinetics of stainless alloys containing molybdenum-1. Coulometric studies of Fe-Cr and Fe-Cr-Mo alloys10.1016/0010-938X(85)90111-8 ↗
23. Influence of chromium and molybdenum on the corrosion of nickel-based alloys10.5006/1.3279907 ↗
24. Cr, Mo and W alloying additions in Ni and their effect on passivity10.1016/j.electacta.2004.01.061 ↗
25. The evolution of crevice corrosion damage on the Ni–Cr–Mo–W alloy-22 determined by confocal laser scanning microscopy10.1016/j.corsci.2011.09.028 ↗
26. The impedance properties of the oxide film on the Ni–Cr–Mo Alloy-22 in neutral concentrated sodium chloride solution10.1016/j.electacta.2010.07.064 ↗
27. A study on corrosion behaviors of Ni–Cr–Mo laser coating, 316 stainless steel and X70 steel in simulated solutions with H2S and CO210.1016/j.surfcoat.2016.02.017 ↗
28. Laser cladding of stainless steel with hastelloy10.1002/1527-2648(200104)3:4<242::AID-ADEM242>3.0.CO;2-D ↗
29. High power diode laser cladding10.1016/S0924-0136(03)00109-2 ↗
30. Characteristics of cobalt-based alloy coating on tool steel prepared by powder feeding laser cladding10.1016/j.optlastec.2006.12.005 ↗
31. Characterization of dilution action in laser-induction hybrid cladding10.1016/j.optlastec.2010.12.005 ↗
32. The anti-corrosion behavior under multi-factor impingement of Hastelloy C22 coating prepared by multilayer laser cladding10.1016/j.apsusc.2017.12.108 ↗
33. Laser cladding technology to small diameter pipes10.1016/S0029-5493(99)00159-4 ↗
34. Microstructures, mechanical properties and corrosion resistance of Hastelloy C22 coating produced by laser cladding10.1016/j.jallcom.2012.10.193 ↗
35. Investigations on the behavior of laser cladding Ni–Cr–Mo alloy coating on TP347H stainless steel tube in HCl rich environment10.1016/j.surfcoat.2013.06.048 ↗
36. Standardization Administration of China (2017). GB/T 5310–2017: Seamless Steel Tubes and Pipes for High Pressure Boiler, Standards Press of China.
37. Discussion on the mechanisms and factors of the gas side high temperature corrosion in water wall tubes for coal fired boilers