Effect of Coating Process on Properties of Two-Component Waterborne Polyurethane Coatings for Wood
Source abstract
Abstract
Acrylic acid has good environmental weather resistance, water resistance, alcohol resistance, dirt resistance, and other properties. An acrylic acid dispersion with a core–shell structure was prepared and reacted with a polyisocyanate-type curing agent to prepare a waterborne polyurethane topcoat suitable for wood. The prepared two-component polyurethane topcoat was used in combination with a waterborne primer and a waterborne sealing primer and applied to Pine (Pinus strobus) boards to carry out gloss, wear resistance, and adhesion experiments. The effects of different coating amounts and spraying times on the comprehensive properties of the wood coatings were studied. The experimental results showed that when the self-made two-component polyurethane topcoat for wood was matched with the primer and the sealing primer, the coating amount of the sealing primer had little effect on improving the adhesion and wear resistance but had a significant effect on the gloss. The spraying times of the primer and the topcoat greatly impacted the adhesion, but they had no decisive impact on the improvement of the gloss. When the coating amount was 60 g/m2 for the waterborne sealing primer, 100 g/m2 for waterborne primer, and 120 g/m2 for the self-made topcoat and the coating was sprayed twice, the comprehensive performance of the obtained film on the wood was the best. This research on the preparation and coating process optimization of the two-component waterborne polyurethane coatings for wood can provide a technical basis for the application of two-component waterborne polyurethane topcoats for wood.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Polymer composites and self-healing · Lignin and Wood Chemistry · Natural Fiber Reinforced Composites
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Co-Innovation Center of Efficient Processing and Utilization of Forest Resources, Nanjing Forestry University, Nanjing 210037, China
College of Furnishings and Industrial Design, Nanjing Forestry University, Nanjing 210037, China
Funding
Natural Science Foundation of Jiangsu Province
References (40)
Show source-provided references
1. Qin, Y., and Yan, X. (2022). Effect of the Addition of Shellac Self-Healing and Discoloration Microcapsules on the Performance of Coatings Applied on Ebiara Solid Board. Coatings, 12.10.3390/coatings12111627 ↗
2. Yang, Z., Han, Y., Peng, W., Wang, L., and Yan, X. (2022). Effect of Fluorane Microcapsule Content on Properties of Thermochroic Waterborne Topcoat on Tilia europaea. Polymers, 14.10.3390/polym14173638 ↗
3. Xia, Y., Yan, X., and Peng, W. (2022). Preparation of Cellulose Modified Wall Material Microcapsules and Its Effect on the Properties of Wood Paint Coating. Polymers, 14.10.3390/polym14173534 ↗
4. Pan, P., Yan, X., and Zhao, W. (2022). Effect of Coating Process of Photochromic and Thermochromic Composite Microcapsules on Coating Properties for Basswood. Coatings, 12.10.3390/coatings12091246 ↗
5. Huang, N., Yan, X., and Han, Y. (2022). Preparation of Melamine-Formaldehyde Resin/Rice Husk Powder Coated Epoxy Resin Microcapsules and Effects of Different Microcapsule Contents on the Properties of Waterborne Coatings on Tilia europaea Surface. Coatings, 12.10.3390/coatings12081213 ↗
6. Han, Y., Yan, X., and Tao, Y. (2022). Effect of Transparent, Purple, and Yellow Shellac Microcapsules on Properties of the Coating on Paraberlinia bifoliolata Surface. Polymers, 14.10.3390/polym14163304 ↗
7. A Review on Waterborne Thermosetting Polyurethane Coatings Based on Castor Oil: Synthesis, Characterization, and Application10.1080/03602559.2016.1275681 ↗
8. Preparation and Corrosion Resistance of gamma-aminopropyltriethoxysilane-TiO2-GO/Waterborne Polyurethane Coating10.20964/2020.11.44 ↗
9. The improved breathability of polyurethane coated cotton fabric via micro-cracking
10. Coatings prepared from waterborne polyurethane dispersions obtained with polycarbonates of 1,6-hexanediol of different molecular weights10.1016/j.porgcoat.2013.06.005 ↗
11. Emulsifyable air drying urethane alkyds10.1016/j.porgcoat.2009.09.017 ↗
12. Yin, X., Li, X.Y., and Luo, Y.J. (2017). Synthesis and Characterization of Multifunctional Two-Component Waterborne Polyurethane Coatings: Fluorescence, Thermostability and Flame Retardancy. Polymers, 9.10.3390/polym9100492 ↗
13. Effect of resins on the salt spray resistance and wet adhesion of two component waterborne polyurethane coating10.1515/epoly-2019-0046 ↗
14. Liu, H.N., Bi, Z.J., Wan, Z., Wang, X.M., Wan, Y., Guo, X.X., and Cai, Z.Y. (2020). Preparation and Performance Optimization of Two-Component Waterborne Polyurethane Locomotive Coating. Coatings, 10.10.3390/coatings10010004 ↗
15. Effect of polyether/polyester polyol ratio on properties of waterborne two-component polyurethane coatings10.1016/j.porgcoat.2020.105545 ↗
16. Wang, R.T., Li, C.X., Jiang, Z.H., and Wang, Z.J. (2022). Self-Assembly of Amphiphilic Linear-Dendritic Carbosilane Block Surfactant for Waterborne Polyurethane Coating. Polymers, 12.10.3390/polym12061318 ↗
17. Analysis of volumetric swelling and shrinkage of heat treated woods: Experimental and artificial neural network modeling approach
18. Influence of nanoparticles and olive leaf extract in polyacrylate coating on the weathering performance of thermally modified wood10.1007/s00107-021-01761-8 ↗
19. Synthesis and assessment of novel anticorrosive polyurethane coatings containing an amine-functionalized nanoclay additive prepared by the cathodic electrophoretic deposition method10.1039/C5RA26609B ↗
20. (1985). Furniture—Assessment of Wearability of Surface Coatings (Standard No. GB/T 4893.8-1985). (In Chinese).
21. (1985). Furniture—Assessment of Adhesion of Surface Coatings—Cross Cut (Standard No. GB/T 4893.4-1985). (In Chinese).
22. Pan, P., Yan, X., and Peng, W. (2022). Tung Oil Microcapsules Prepared with Different Emulsifiers and Their Effects on the Properties of Coating Film. Coatings, 12.10.3390/coatings12081166 ↗
23. Han, Y., Yan, X., and Tao, Y. (2022). Effect of Transparent, Purple, and Yellow Shellac Microcapsules on the Optical Properties and Self-Healing Performance of Waterborne Coatings. Coatings, 12.10.3390/coatings12081056 ↗
24. Han, Y., Yan, X., and Tao, Y. (2022). Effect of Number of Impregnations of Microberlinla sp with Microcapsule Emulsion on the Performance of Self-Repairing Coatings on Wood Surfaces. Coatings, 12.10.3390/coatings12070989 ↗
25. Wang, Y., and Yan, X. (2022). Preparation of Resin-Coated Waterborne Coating Microcapsules and Its Effect on the Properties of Waterborne Coating for Wood Surfaces. Coatings, 12.10.3390/coatings12101394 ↗
26. (1985). Furniture—Assessment of Surface Resistance to Alternation of Heat and Cold (Standard No. GB/T 4893.7-1985). (In Chinese).
27. (2020). Test of Surface Coatings of Furniture—Part 2: Determination of Resistance to Wet Heat (Standard No. GB/T 4893.2-2020). (In Chinese).
28. (2020). Test of Surface Coatings of Furniture—Part 3: Determination of Resistance to Dry Heat (Standard No. GB/T 4893.3-2020). (In Chinese).
29. RAFT mediated one-pot synthesis of glycopolymer particles with tunable core-shell morphology10.1039/C6PY02202B ↗
30. Amphiphilic polymeric particles with core-shell nanostructures: Emulsion-based syntheses and potential applications10.1007/s00396-010-2276-9 ↗
31. The heat resistance of a polyurethane coating filled with modified nano-CaCO310.1016/j.apsusc.2014.07.022 ↗
32. Rogina-Car, B., Kovacevic, S., Dordevic, S., and Dordevic, D. (2020). Influence of Washing and Sterilization on Properties of Polyurethane Coated Fabrics Used in Surgery and for Wrapping Sterile Items. Polymers, 12.10.3390/polym12030642 ↗
33. EIS study on failure process of two polyurethane composite coatings10.1016/j.porgcoat.2010.04.017 ↗
34. Bergamasco, S., Tamantini, S., Zikeli, F., Vinciguerra, V., Mugnozza, G.S., and Romagnoli, M. (2022). Synthesis and Characterizations of Eco-Friendly Organosolv Lignin-Based Polyurethane Coating Films for the Coating Industry. Polymers, 14.10.3390/polym14030416 ↗
35. Understanding Glass through Differential Scanning Calorimetry10.1021/acs.chemrev.8b00510 ↗
36. Blends of polymers with similar glass transition temperatures: A DMTA and DSC study10.1002/app.20531 ↗
37. The effects of polydopamine coated Cu nanoparticles on the tribological properties of polydopamine/PTFE coatings10.1016/j.triboint.2016.06.031 ↗
38. Huang, N., Yan, X., and Zhao, W. (2022). Influence of Photochromic Microcapsules on Properties of Waterborne Coating on Wood and Metal Substrates. Coatings, 12.10.3390/coatings12111750 ↗
39. Han, Y., Yan, X., and Zhao, W. (2022). Effect of Thermochromic and Photochromic Microcapsules on the Surface Coating Properties for Metal Substrates. Coatings, 12.10.3390/coatings12111642 ↗
40. Yan, X., Han, Y., and Yin, T. (2021). Coating Process Optimization and Self-Healing Performance Evaluation of Shellac Microcapsules Coated with Melamine/Rice Husk Powder. Appl. Sci., 11.10.3390/app11188373 ↗