Plasma Enhanced Fluorine-Free Superhydrophobic Polyester (PET) Fabric with Ultra-Robust Antibacterial and Antibacterial Adhesion Properties

Superhydrophobic antibacterial fabric possesses properties of antibacterial and antibacterial adhesion and shows huge demand in the field of medical textiles. However, current technologies are unable to fully address this. Hence, a simple method is highly desirable. Herein, the pristine polyester (PET) fabric is immersed into the solution containing ZnO nanoparticle and polydimethylsiloxane (PDMS), and the fiber surfaces are uniformly covered by a ZnO-PDMS layer after being treated by low pressure Ar plasma. The weight gain rate of the treated fabric is 3.5%, which is basically unchanged, and the air permeability, moisture permeability, and tensile properties of the fabric are basically not affected. It is found that the water contact angle (WCA) of the fabric is over 162.7°and sliding angle (SA) is less than 10°. The stable binding of PDMS and PET fibers induces a robust superhydrophobicity; even after 300 washing cycles and 600 friction cycles, it still remains superhydrophobic. The antibacterial rates of Escherichia coli and Staphylococcus aureus before washing were 99.89% and 99.85%, respectively, and after 100 cycles of washing, the antibacterial rates decreased to 99.36% and 99.17%, respectively. Therefore, it shows a good development prospect in the application of protecting clothing or textiles that require good antibacterial properties (such as bed sheets, duvet covers, etc.).