Dual Component Polymeric Epoxy-Polyaminoamide Based Zinc Phosphate Anticorrosive Formulation for 15CDV6 Steel
Source abstract
Abstract
The present research is focused on a formulation with two active components as an anticorrosive polymer coating for 15CDV6 steel. The dual component formulation (epoxy-zinc phosphate (ZP) coating) consists of a polymeric epoxy resin Bisphenol A diglycidyl ether (DGEBA) cured with a polyaminoamide as a first component and zinc phosphate (Zn3(PO4)2(H2O)4) (ZP) added in 5% by weight as a second component. The anticorrosive performance of the epoxy-ZP coating was evaluated against the standard coating, which consists of only one component, the cured polymeric epoxy resin. The two polymer coatings were evaluated by electrochemical impedance spectroscopy (EIS). The surface morphology was of the two polymer coatings were characterized by scanning electron microscopy (SEM). The coated samples of 15CDV6 steel were tested in a harsh environment of corrosive electrolytes (3 wt % NaCl solution). Under these conditions, a very high impedance value was obtained for 15CDV6 steel coated with the epoxy-ZP coating. Even after exposure for a long period of time (5856 h), the performance was still acceptable, indicating that the epoxy-ZP coating is an excellent barrier. The standard epoxy coating provided an adequate corrosion protection performance for a short period of time, then the performance started to decline. The results were confirmed by surface characterization, a cross-sectional image obtained by optical microscopy for an epoxy-ZP coating applied on 15CDV6 steel exposed for 5856 h to a salt spray test showed that the coating is homogeneous and adheres well to the surface of the steel. So, the coating with a dual component could have great potential in marine applications as anticorrosive for steel.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Corrosion Behavior and Inhibition · Concrete Corrosion and Durability · Metal and Thin Film Mechanics
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Laboratory of Agroresources, Polymers and Process Engineering (LAPPE), Department of Chemistry, Faculty of Science, Ibn Tofail University, BP 133, 14000 Kenitra, Morocco
Department of Chemistry, An-Najah National University, P.O. Box 7 Nablus, Palestine
Scientific Research and Development, Al Istiqlal University, P.O. Box 10 Jericho, Palestine
References (28)
Show source-provided references
1. Anticorrosive properties of Hexa (3-methoxy propan-1, 2-diol) cyclotri-phosphazene compound for carbon steel in 3% NaCl medium: Gravimetric, electrochemical, DFT and Monte Carlo simulation studies10.1016/j.heliyon.2019.e01340 ↗
2. Anticorrosive formulation based of the epoxy resin–polyaminoamide containing zinc phosphate inhibitive pigment applied on sulfo-tartaric anodized AA 7075-T6 in NaCl medium10.1007/s40735-019-0218-8 ↗
3. Cadmium-and chromate-free coating schemes for corrosion protection of 15CDV6 steel10.1016/S0026-0576(11)00010-9 ↗
4. Development of copper coating technology on high strength low alloy steel filler wire for aerospace applications10.1016/j.matpr.2017.11.398 ↗
5. Dagdag, O., Essamri, A., El Gana, L., El Bouchti, M., Hamed, O., Cherkaoui, O., Jodeh, S., and El Harfi, A. (2018). Synthesis, characterization and rheological properties of epoxy monomers derived from bifunctional aromatic amines. Polym. Bull., 1–15.10.1007/s00289-018-2607-4 ↗
6. Anticorrosive performance approach combining an epoxy polyaminoamide–zinc phosphate coatings applied on sulfo-tartaric anodized aluminum alloy 508610.1007/s40735-018-0168-6 ↗
7. Polymeric-based epoxy cured with a polyaminoamide as an anticorrosive coating for aluminum 2024-T3 surface: experimental studies supported by computational modeling10.1007/s40735-019-0251-7 ↗
8. Exploring corrosion protection properties of solvent based epoxy-graphene oxide nanocomposite coatings on mild steel10.1016/j.corsci.2016.11.008 ↗
9. Anticorrosive performance of new epoxy-amine coatings based on zinc phosphate tetrahydrate as a nontoxic pigment for carbon steel in NaCl medium10.1007/s13369-018-3160-z ↗
10. Phosphorous-based epoxy resin composition as an effective anticorrosive coating for steel10.1007/s40090-018-0152-5 ↗
11. Mechanical and anticorrosive properties of graphene/epoxy resin composites coating prepared by in-situ method10.3390/ijms16012239 ↗
12. Aromatic phosphorodiamidate curing agent for epoxy resin coating with flame-retarding properties10.1016/j.porgcoat.2013.05.009 ↗
13. Corrosion protection and adhesion properties of the epoxy coating applied on the steel substrate pre-treated by a sol-gel based silane coating filled with amino and isocyanate silane functionalized graphene oxide nanosheets10.1016/j.apsusc.2017.12.240 ↗
14. The influence of a Zr-based conversion treatment on interfacial bonding strength and stability of epoxy coated carbon steel10.1016/j.porgcoat.2016.11.016 ↗
15. Study on corrosion electrochemical behavior of several different coating systems by EIS10.1016/j.porgcoat.2008.08.012 ↗
16. The role of zinc aluminum phosphate anticorrosive pigment in protective performance and cathodic disbondment of epoxy coating10.1016/j.corsci.2009.12.019 ↗
17. The effects of zinc aluminum phosphate (ZPA) and zinc aluminum polyphosphate (ZAPP) mixtures on corrosion inhibition performance of epoxy/polyamide coating10.1016/j.jiec.2012.11.027 ↗
18. Three generations of inorganic phosphates in solvent and water-borne paints: A synergism case10.1016/j.apsusc.2005.02.096 ↗
19. Enhancement of corrosion protection performance of epoxy coating by introducing new hydrogenphosphate compound10.1016/j.porgcoat.2017.03.014 ↗
20. Smart protection provided by epoxy clear coating doped with polystyrene microcapsules containing silanol and Ce (III) ions as corrosion inhibitors10.1016/j.surfcoat.2015.11.035 ↗
21. Effect of carbon nano-tubes on the corrosion resistance of alkyd coating immersed in sodium chloride solution10.1016/j.porgcoat.2015.04.003 ↗
22. (2019). ASTM B117-18 Standard Practice for Operating Salt Spray (Fog) Apparatus, ASTM.
23. Electrochemical investigation of high-performance silane sol–gel films containing clay nanoparticles10.1016/j.porgcoat.2010.04.007 ↗
24. Evaluation of self-healing ability in protective coatings modified with combinations of layered double hydroxides and cerium molibdate nanocontainers filled with corrosion inhibitors10.1016/j.electacta.2011.10.078 ↗
25. Amelioration of anticorrosion and hydrophobic properties of epoxy/PDMS composite coatings containing nano ZnO particles10.1016/j.porgcoat.2015.12.007 ↗
26. RGO modified ZnAl-LDH as epoxy nanostructure filler: A novel synthetic approach to anticorrosive waterborne coating10.1016/j.surfcoat.2017.07.053 ↗
27. Improvement of active corrosion protection of carbon steel by water-based epoxy coating with smart CeO2 nanocontainers10.1016/j.porgcoat.2017.10.015 ↗
28. The anti-corrosion performance of water-borne paints in long term tests10.1016/j.porgcoat.2017.04.031 ↗