Influence of NaCl Freeze Thaw Cycles and Cyclic Loading on the Mechanical Performance and Permeability of Sulphoaluminate Cement Reactive Powder Concrete

This paper aimed to investigate the coupling effects of NaCl freeze–thaw cycles and cyclic loading on the mechanical performance and permeability of sulphoaluminate cement reactive powder concrete (RPC). Firstly, the compressive and flexural strengths of sulphoaluminate cement RPC were investigated. Then, the chloride ion permeability, mechanical strengths (compressive and flexural strengths) and mass loss were determined. Results indicated that the increased steel fibers content and curing age played positive roles in the mechanical strengths. The threshold values of steel fibers and curing age were 3.0% and 14 days. Sulphoaluminate cement RPC with early curing age (5 h) showed relatively high mechanical strengths: flexural strength (8.69~17.51 MPa), and compressive strength (34.1~38.5 MPa). The mass loss, the chloride migration coefficient, and the compressive strength loss increased linearly with NaCl freeze–thaw cycles. Meanwhile, the flexural strength loss increased with the exponential function. The relative dynamic modulus of elasticity of specimens decreased linearly with the increased freeze–thaw cycles. Finally, it was observed from this paper, cyclic loading demonstrated negative roles on the mechanical strengths and resistance to chloride penetration.