Insight of Weathering Processes Based on Monitoring Surface Characteristic of Tropical Wood Species

The main aim of the presented research was to compare the influence of selected ageing factors, such as UV radiation and complex artificial weathering methods, on the colour, wettability and roughness changes in garapa, tatajuba, courbaril and massaranduba from South America—tropical wood species that are popular for external usage in European countries. Both processes caused wood surfaces to become darker and turn to shades of brown. The highest total colour changes were shown in courbaril wood (wood with the highest extractives content). The wood surface roughness demonstrated variation, depending on the wood section and measurement direction, and increased after ageing treatments. Changes in surface contact angle were significant after the inclusion of water and drying in the weathering process (wettability decreased). Anatomical analyses of the tested tropical woods revealed structural changes after used artificial weathering treatments (distortion between cell elements, degradation of the middle lamella, micro-cracks in cell walls, thinning and degradation of parenchyma cells, cracks along pits within vessels). As a result of desorption tension, the changes caused by UV irradiation were much smaller than those caused by full artificial weathering. Fourier-transform infrared spectroscopy (FTIR) analysis indicated the occurrence of lignin and hemicelluloses oxidative changes after the weathering process which resulted in the formation of carbonyl and carboxyl compounds. The depolymerisation of cellulose was also identified. The results show that the observed changes may affect the long-term durability of finishes applied over wood subjected to weathering factors for a short period before finishing.