Edible Films Based on Black Chia (Salvia hispanica L.) Seed Mucilage Containing Rhus microphylla Fruit Phenolic Extract

Functional films based on black chia (Salvia hispanica L.) seed mucilage (BCm) containing Rhus microphylla (Rm) fruit phenolic extract were built and characterized. A hydro-alcohol extract (HAE) of Rm was incorporated as the bioactive agent due to its noteworthy phenolic profile, and good antioxidant and antifungal activities. The effects of the BCm concentration (0.2% and 0.4%, w/v), HAE incorporation, and their interaction with glycerol (1.0%, w/v) and calcium chloride (0.05%, w/v) on the films’ physicochemical properties were evaluated. The filmogenic solutions successfully fitted to the Herschel–Bulkley model (R2 < 0.999), exhibiting a pseudoplastic and shear thinning character, typical of polymer solutions. Interestingly, their rheological properties were not (p > 0.05) changed by the HAE addition, but their surface tension was enhanced (p < 0.05), which could favor their coating ability. The polyanionic nature of the systems (zeta potential-Zp values from −26.9 to −33.3 mV) allowed them to interact with Ca2+ cations, thus forming stable and resistant films. All the films showed low water solubility (15.0% to 22.3%) and high permeability (3.7 to 4.0 × 10−10 g m−1 s−1 Pa−1), as well as high biodegradability (moisture content from 66.0% to 80.9%); although the moisture content was reduced (p < 0.05) with HAE addition. The combination of higher BCm ratio and HAE addition (BCm0.4+Rm) led to a more resistant, thick, opaque, and dark film compared with the others obtained. This study reveals the BCm-based films’ potential, highlighting those with HAE, representing a novel alternative to improve the quality of food products.