Abrasion Resistance of Superhydrophobic Coatings on Aluminum Using PDMS/SiO2

Superhydrophobic coatings have shown tremendous improvement in the usability of metals such as aluminum. These coatings are capable of adding attractive features such as self-cleaning, anti-corrosion, and anti-biofouling to the array of diverse features that aluminum possesses, including lightweight and high ductility. For superhydrophobic surfaces, having considerable abrasion resistance is as important as achieving a high contact angle. In this work, two types of coatings have been prepared, each composed of functionalized silica nanoparticles along with polydimethylsiloxane (PDMS) dispersed in ethanol, and their superhydrophobicity and abrasion characteristics have been investigated. The same silica nanoparticles are present in each coating, but each has a different proportion of the PDMS base to its curing agent. The surface morphology of the coatings was studied with the aid of a scanning electron microscope (SEM) and an atomic force microscope (AFM). The surface chemical composition was characterized using an energy dispersive X-ray spectroscope (EDX). The prepared coatings were analyzed for their degree of superhydrophobicity, abrasion resistance and adhesion characteristics. In addition, atomic force microscopy was used to understand the adhesion characteristics of the coatings.