Study on High-Temperature, Ultra-Low Wear Behaviors of Ti6Al4V Alloy with Thermal Oxidation Treatment

Thermal oxidation (TO) is a simple and economical way to enhance the wear resistance of the Ti6Al4V alloy. The TO temperature has a very important effect on the tribological properties of the TiO2 layer formed. However, the impact of the oxidation temperature on the high-temperature tribological behavior of a TO-treated Ti6Al4V alloy is not clear. Therefore, the Ti6Al4V alloy was oxidized at 400 °C, 600 °C, and 700 °C for 36 h, and the sliding friction experiments were conducted at room temperature (RT) and 400 °C with a Si3N4 ball as the counter body to comparatively study the effect of the oxidation temperature on the high-temperature friction behavior of the TO-treated Ti6Al4V alloy. The results show that the TO treatment can effectively improve the wear resistance of the samples at both room and high temperatures. Among them, the oxidation-treated samples at 700 °C show the best wear resistance, with a reduction of 92.6% at high temperatures; the amount of wear loss at room temperature was so small that it was almost incalculable. At room temperature, the friction surface formed uneven agglomerate formations, resulting in an elevated coefficient of friction (CoF) compared to the untreated samples. At a high temperature, however, the CoF is reduced compared to the untreated samples due to the formation of a homogeneous transfer film in the wear area that is caused by the interaction of Si3N4 and oxygen.