Concrete Damage in Field Conditions and Protective Sealer and Coating Systems
Source abstract
Abstract
Concrete structures undergo different forms of damage during their service life. The aim of this study is to identify the most common forms of concrete damage in field conditions. A number of concrete elements and structures were visually inspected and the damage was photographed. The damage phenomena covered are delamination, popout, spalling, scaling, drying shrinkage cracking, corrosion-induced cracking, map cracking, rust and salt stains, discoloration, and mold and moss growths. The probable reasons for these damage phenomena are discussed in this study. Moreover, this study highlights how concrete structures can be protected from the aforementioned forms of damage by using sealer and coating systems as surface treatments. Different sealer and coating systems, emphasizing their selection for specific uses, installation on concrete substrate, effects on concrete durability, performance criteria, and performance evaluation methods have been discussed. Furthermore, some recommendations are given to improve the performance of concrete sealer and coating systems for the protection of concrete structures in field conditions.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Concrete Corrosion and Durability · Concrete and Cement Materials Research · Smart Materials for Construction
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Angelo Del Zotto School of Construction Management, George Brown College, 146 Kendal Avenue, Toronto, ON M5T 2T9, Canada
References (97)
Show source-provided references
1. van Breugel, K., Ye, G., and Yuan, Y. (2010). Service life of reinforced concrete structures under combined mechanical and environmental loads. 2nd International Symposium on Service Life Design for Infrastructure (Pro070), RILEM Publications SARL.
2. Damage of concrete and reinforcement of reinforced-concrete foundations caused by environmental effects10.1016/j.proeng.2015.08.187 ↗
3. Material and structural destruction of concrete elements in the industrial environment10.1016/j.proeng.2017.02.024 ↗
4. (2002). Types and Causes of Concrete Deterioration, Portland Cement Association (PCA). Concrete Information, PCA R&D Serial No. 2617.
5. A review on surface treatment for concrete—Part 2: Performance10.1016/j.conbuildmat.2016.11.128 ↗
6. A review on concrete surface treatment Part I: Types and mechanisms10.1016/j.conbuildmat.2016.12.025 ↗
7. The effect of sealers on the freeze-thaw resistance of mortar10.1016/0008-8846(92)90043-U ↗
8. Assessing the protective qualities of treated and untreated concrete surfaces under cyclic wetting and drying10.1016/0360-1323(96)00020-0 ↗
9. Mechanisms of frost damage
10. Darwin, D., Browning, J., Gong, L., and Hughes, S.R. (2007). Effects of Deicers on Concrete Deterioration. A Report on Research Sponsored by the Structural Engineering and Materials Laboratory, The University of Kansas Center for Research, Inc.. University of Kansas (SL Report 07–3).
11. Effects of deicers on concrete deterioration
12. Hooton, R.D., and Julio-Betancourt, G.A. (2005). Investigation of the Effects of Various Deicing Chemicals, Curing Methods, and Concrete Placement on Salt Scaling Resistance of Concrete Surface, University of Toronto. Final Report to Ready Mixed Concrete Association of Ontario.
13. Julio-Betancourt, G.A. (2009). Effect of De-icer and Anti-icer Chemicals on the Durability, Microstructure, and Properties of Cement-Based Materials. [Ph.D. Thesis, University of Toronto].
14. Kozikowski, R.L., Taylor, P.C., and Pyc, W.A. (2007). Evaluation of Potential Concrete Deterioration Related to Magnesium Chloride (MgCl2) Deicing Salts, Portland Cement Association (PCA). PCA R&D Serial No. 2770.
15. Sutter, L.L., Peterson, K., Julio-Betancourt, G., Hooton, D., van dam, T.J., and Smith, K. (2008). The Deleterious Chemical Effects of Concentrated Deicing Solutions on Portland Cement Concrete. Study SD 2002-01 Implementation Guide, Michigan Tech Transportation Institute.
16. Performance characteristics of surface coatings applied to concrete for control of reinforcement corrosion10.1016/S0950-0618(00)00011-8 ↗
17. Chloride penetration resistance of concrete sealer and coating systems10.3846/13923730.2014.890659 ↗
18. Soudki, K.A., Jeffs, P., and Safiuddin, M.D. (2012). Chloride Penetration Resistance of Concrete Coating Systems on Region of Waterloo Bridges, Department of Civil and Environmental Engineering, Faculty of Engineering, University of Waterloo. Final Research Report Submitted to the Region of Waterloo.
19. Accelerated laboratory evaluation of surface treatments for protecting concrete bridge decks from salt scaling10.1016/j.conbuildmat.2014.01.014 ↗
20. Surface microstructure and scaling resistance of concrete10.1016/0008-8846(96)00138-X ↗
21. Al-Dulaijan, S.U., Maslehuddin, M., Al-Zahrani, M.M., Al-Juraifani, E.A., Al-Idi, S.H., and Al-Mehthel, M. (2000). Performance evaluation of cement-based surface coatings. Repair, Rehabilitation, and Maintenance of Concrete Structures, and Innovations in Design and Construction, Proceedings of the ACI Fourth International Conference (ACI SP-193), Seoul, Korea, 19–22 September 2000, American Concrete Institute.
22. Effectiveness of surface coatings in improving concrete durability10.1016/S0958-9465(02)00087-2 ↗
23. Use of surface treatment materials to improve concrete durability10.1061/(ASCE)0899-1561(1999)11:1(36) ↗
24. Concrete surface treatment: Effect of exposure temperature on chloride diffusion resistance10.1016/0008-8846(94)00127-K ↗
25. Evaluation of the durability of mortar and concrete applied with inorganic coating material and surface treatment system10.1016/j.conbuildmat.2005.08.012 ↗
26. Oshiro, T., and Tanigawa, S. (1988). Effect of surface coatings on the durability of concrete exposed to marine environment. Concrete in Marine Environment, Proceedings of the Second International Conference on Concrete in Marine Environment (ACI SP-109), Okinawa, Japan, 21–26 August 1988, American Concrete Institute.
27. Porter, L.C. (1975). Some surface treatments increase concrete durability. Durability of Concrete (ACI SP-47), American Concrete Institute.
28. Water vapor transmission and waterproofing performance of concrete sealer and coating systems10.3846/13923730.2014.893905 ↗
29. Experimental exploration of the waterproofing mechanism of inorganic sodium silicate-based concrete sealers10.1016/j.conbuildmat.2015.12.069 ↗
30. Coatings for the protection of structural materials
31. Effect of surface treatment on durability of concrete exposed to physical sulfate attack10.1016/j.conbuildmat.2014.10.006 ↗
32. Influence of surface coatings on carbonation of concrete10.1061/(ASCE)0899-1561(1990)2:1(35) ↗
33. Carbonation-induced and chloride-induced corrosion in reinforced concrete structures10.1061/(ASCE)MT.1943-5533.0001209 ↗
34. Palle, S., and Hopwood, T. (2006). Coatings, Sealants and Fillers to Address Bridge Concrete Deterioration and Aesthetics—Phase 1, Kentucky Transportation Center, College of Engineering, University of Kentucky. Research Report No. KTC06-36/SPR 291-04-1F.
35. Wenzlick, J.D. (2007). Bridge Deck Concrete Sealers, Missouri Department of Transportation. Final Research Report RI 04-051.
36. Attanayaka, A.M.U.B., Duyar, O., Liang, X., Aktan, H.M., and Ng, K.Y.S. (2003, January 12–16). Fundamentals of use of penetrating sealants for concrete bridge deck protection. Proceedings of the TRB 2003 Annual Meeting, Washington, DC, USA.
37. Cady, P.D. (1994). Sealers for Portland Cement Concrete Highway Facilities, Transportation Research Board (TRB), National Research Council. NCHRP Synthesis of Highway Practice 209.
38. Long-term chloride profiles in bridge decks treated with penetrating sealer or corrosion inhibitors10.1016/j.conbuildmat.2015.10.158 ↗
39. Filice, J., and Wong, J. (2001). Best Practice Guidelines for Selecting Concrete Bridge Deck Sealers, Alberta Transportation and Utilities.
40. A review of salt scaling: II. Mechanisms10.1016/j.cemconres.2007.03.003 ↗
41. Thomas, M.D.A. (2007). Optimizing the Use of Fly Ash in Concrete, Portland Cement Association (PCA).
42. Effects of deicing salts on the scaling resistance of concrete10.1061/(ASCE)MT.1943-5533.0001106 ↗
43. Investigation on spalling resistance of ultra-high-strength concrete under rapid heating and rapid cooling
44. Portland Cement Association (PCA) (1998). Control of air content in concrete. Concr. Technol. Today, 19, 1–3.
45. (2001). Concrete Slab Surface Defects: Causes, Prevention, Repair. Concrete Information, Portland Cement Association (PCA). PCA R&D Serial No. 2155.
46. Spalling in concrete subjected to shock wave blast10.1016/j.engstruct.2016.05.002 ↗
47. (2004). Delamination of Troweled Concrete Surfaces (CIP-20), National Ready Mixed Concrete Association (NRMCA).
48. Delatte, N. (2009). Types and causes of cracking in reinforced concrete. Failure, Distress, and Repair of Concrete Structures, Woodhead Publishing Limited.10.1533/9781845697037 ↗
49. Bentz, D.P., and Weiss, W.J. (2011). Internal Curing: A 2010 State-of-the Art Review, National Institute of Standards and Technology. NISTIR 7765.10.6028/NIST.IR.7765 ↗
50. (2009). Crazing Concrete Surfaces (CIP-3), National Ready Mixed Concrete Association (NRMCA).
51. Reinforcement corrosion initiation and activation times in concrete structures exposed to severe marine environments10.1016/j.cemconres.2009.07.003 ↗
52. Effect of CaCl2 and NaCl additions on concrete corrosivity10.1016/j.cemconres.2003.12.015 ↗
53. A study on chloride-induced depassivation of mild steel in simulated concrete pore solution10.1016/S0008-8846(02)00895-5 ↗
54. Factors controlling cracking of concrete affected by reinforcement corrosion10.1007/BF02480466 ↗
55. Modeling the time-to-corrosion cracking in chloride contaminated reinforced concrete structures
56. Probability of corrosion induced cracking in reinforced concrete10.1016/0008-8846(95)00110-X ↗
57. Deterioration of concrete due to reinforcement steel corrosion10.1016/0958-9465(95)00043-7 ↗
58. Effects of carbonation on mechanical properties and durability of concrete using accelerated testing method10.51400/2709-6998.2296 ↗
59. Performance of galvanized steel reinforcing bars against corrosion in concrete
60. Pietrosanto, J. (2010). Rust Coloured Stains on the Surface of Exposed Aggregate Concrete, Vic Mix, TJM Operations Pty Ltd.
61. Wong, H.S., Zhao, Y.X., Karimi, A.R., Buenfeld, N.R., and Jin, W.L. (2016). Rust distribution in corrosion-induced cracking concrete. Steel Corrosion-Induced Concrete Cracking, Butterworth Heinemann.
62. Soudki, K.A., Jeffs, P., and Safiuddin, M.D. (2011). Concrete Coating Systems on Region of Waterloo Bridges, Department of Civil and Environmental Engineering, Faculty of Engineering, University of Waterloo. Final Research Report Submitted to the Region of Waterloo.
63. (2007). Discoloration (CIP-23), National Ready Mixed Concrete Association (NRMCA).
64. Cwalina, B. (2014). Biodeterioration of concrete, brick and mineral-based building materials. Understanding Biocorrosion: Fundamentals and Applications, Woodhead Publishing Limited.10.1533/9781782421252.3.281 ↗
65. Extent of moisture and mould damage in structures of public building
66. Characterization of silicate sealers on concrete10.1016/S0008-8846(97)00167-1 ↗
67. Sealer and coating systems for the protection of bridge structures10.5897/IJPSX11.005 ↗
68. Commercially available waterproofing agents in India: A review
69. Laboratory studies to investigate the properties of CIR mixes containing steel slag as a substitute for virgin aggregates10.1016/j.conbuildmat.2011.06.047 ↗
70. Effects of copper slag and recycled concrete aggregate on the properties of CIR mixes with bitumen emulsion, rice husk ash, Portland cement, and fly ash10.1016/j.conbuildmat.2015.08.021 ↗
71. Surface treatments for concrete: Assessment methods and reported performance10.1016/S0950-0618(97)00019-6 ↗
72. A surface engineering approach applicable to concrete repair engineering
73. (2012). ASTM C672/C672M Standard Test Method for Scaling Resistance of Concrete Surfaces Exposed to De-icing Chemicals, ASTM International.
74. (2013). ASTM C642 Standard Test Method for Density, Absorption and Voids in Hardened Concrete, ASTM International.
75. (2002). AASHTO T259 Standard Method of Test for Resistance of Concrete to Chloride Ion Penetration, American Association of State Highway and Transportation Officials.
76. (2013). ASTM D822/D822M Standard Practice for Filtered Open-Flame Carbon-Arc Exposures of Paint and Related Coatings, ASTM International.
77. (2016). ASTM B117 Standard Practice for Operating Salt Spray (Fog) Apparatus, ASTM International.
78. (2000). Test Procedure for Measuring the Vapour Transmission, Waterproofing and Hiding Power of Concrete Sealers (BT001), Technical Standards Branch, Alberta Transportation and Utilities (ATU).
79. (2000). Test Procedure for Measuring the Waterproofing Performance of Core Samples Taken from Sealed Concrete Surfaces (BT005), Technical Standards Branch, Alberta Transportation and Utilities (ATU).
80. (2008). AASHTO T161 Standard Method of Test for Resistance of Concrete to Rapid Freezing and Thawing, American Association of State Highway and Transportation Officials.
81. (2015). ASTM C666/C666M Standard Test Method for Resistance of Concrete to Rapid Freezing and Thawing, ASTM International.
82. (2014). ASTM D2243 Standard Test Method for Freeze-Thaw Resistance of Water-Borne Coatings, ASTM International.
83. (2016). AASHTO T260 Sampling and Testing for Chloride Ion in Concrete and Concrete Raw Materials, American Association of State Highway and Transportation Officials.
84. (2015). AASHTO T277 Standard Method of Test for Electrical Indication of Concrete’s Ability to Resist Chloride Ion Penetration, American Association of State Highway and Transportation Officials.
85. (2012). ASTM C1152/C1152M Standard Test method for Acid-Soluble Chloride in Mortar and Concrete, ASTM International.
86. (2012). ASTM C1202 Standard Test Method for Electrical Indication of Concrete’s Ability to Resist Chloride Ion Penetration, ASTM International.
87. (2010). ASTM C1543 Standard Test Method for Determining the Penetration of Chloride Ion into Concrete by Ponding, ASTM International.
88. (2011). ASTM D4587 Standard Practice for Fluorescent UV-Condensation Exposures of Paint and Related Coating, ASTM International.
89. (2013). ASTM D4585/D4585M Standard Practice for Testing Water Resistance of Coatings using Controlled Condensation, ASTM International.
90. (2012). ASTM D6489 Standard Test Method for Determining the Water Absorption of Hardened Concrete Treated with a Water-Repellent Coating, ASTM International.
91. (2013). ASTM D1653 Standard Test Methods for Water Vapor Transmission of Organic Coating Films, ASTM International.
92. (2016). ASTM E96/E96M Standard Test Methods for Water Vapor Transmission of Materials, ASTM International.
93. (2016). ASTM D3273 Standard Test Method for Resistance to Growth of Mold on the Surface of Interior Coating in an Environmental Chamber, ASTM International.
94. (2013). ASTM D3274 Standard Test Method for Evaluating Degree of Surface Disfigurement of Paint Films by Microbial (Fungal and Algal) Growth or Soil and Dirt Accumulation, ASTM International.
95. (2009). ASTM D4541 Standard Test Method for Pull-off Strength of Coatings Using Portable Adhesion Testers, ASTM International.
96. (2010). ASTM D2794 Standard Test Method for Resistance of Coatings to the Effects of Rapid Deformation (Impact), ASTM International.
97. (2016). ASTM D1654 Standard Test Method for Evaluation of Painted or Coated Specimens Subjected to Corrosive Environments, ASTM International.