High Lithium Content and Site Disorder in the Transition Metal Oxide Argyrodites Li 7 TiO 5 X (X = Cl – , Br – )

Alexandra Morscher, Lucia Corti, Samuel L. Goodwin, Andrés Acín-Lalanza, Matthew A. Wright, T. Wesley Surta, Ruiyong Chen, Matthew S. Dyer, Frédéric Blanc, Luke M. Daniels, John B. Claridge, Matthew J. Rosseinsky

Chemistry of Materials· Volume 38· Issue 13

Abstract

High Resolution Image Download MS PowerPoint Slide Sulfide lithium argyrodites are a key materials family that are studied as solid electrolytes in commercial all-solid-state batteries (ASSBs), while their oxide analogues remain relatively unexplored. This study presents the discovery of Li 7 TiO 5 X (X = Cl –, Br – ), the first lithium argyrodite materials in which a transition metal is used as the framework-forming cation, expanding the chemical space that is accessible for oxide argyrodites. Incorporation of Ti 4+ enables the lithium content to be maximized to 7 Li + per formula unit. Interestingly, even with the high lithium content, Li 7 TiO 5 Cl retains a Li + site disordered cubic F 4̅3 m structure at room temperature with Li + occupancy of the T5, T5a, and T3 positions, and exhibits an ionic conductivity of 2.2(2) × 10 –6 S cm –1 with the lowest reported activation energy (0.36(2) eV) for bulk Li + ion transport in an oxide argyrodite. Conversely, Li 7 TiO 5 Br adopts the same F 4̅3 m symmetry at room temperature but with an ordered arrangement of Li + positions via full occupancy of the T5a and T3 positions, and thus has an ionic conductivity that is 3 orders of magnitude lower (∼10 –9 S cm –1 ) and a much higher activation energy (0.58(2) eV) than Li 7 TiO 5 Cl. Order–disorder behavior is observed below 250 K in Li 7 TiO 5 Cl, where a Li + site ordering pattern is observed that is distinct from Li 7 TiO 5 Br and all sulfide argyrodites, yielding a tetragonal symmetry ( I 4̅) for only the second time to date in the argyrodite structure type. This unique order–disorder behavior, alongside the ability to incorporate transition metal cations within this material family emphasizes the potential to access much greater structural diversity via the expansive chemical space that is available for exploration in oxide argyrodites.
Source: openalex_inverted_index · Quality: baseline

Research context

OpenAlex topics: Advanced Battery Materials and Technologies · Advancements in Battery Materials · Thermal Expansion and Ionic Conductivity

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

Affiliations

Department of Chemistry, University of Liverpool, Crown Street, L69 7ZD Liverpool, U.K.

Leverhulme Research Centre for Functional Materials Design, Materials Innovation Factory, University of Liverpool, 51 Oxford Street, Liverpool L7 3NY, U.K.

Stephenson Institute for Renewable Energy, University of Liverpool, Peach Street, L69 7ZF Liverpool, U.K.

Funding

Engineering and Physical Sciences Research Council · Leverhulme Research Centre for Functional Materials Design · Faraday Institution

References (51)

Show source-provided references
1. 10.1016/S0167-2738(00)00327-110.1016/S0167-2738(00)00327-1 ↗
2. 10.1002/advs.20210077410.1002/advs.202100774 ↗
3. 10.1038/s41578-019-0165-510.1038/s41578-019-0165-5 ↗
4. 10.1021/acs.chemrev.0c0010110.1021/acs.chemrev.0c00101 ↗
5. 10.1038/natrevmats.2016.10310.1038/natrevmats.2016.103 ↗
6. 10.1088/2516-1083/ab73dd10.1088/2516-1083/ab73dd ↗
7. 10.1021/cm901819c10.1021/cm901819c ↗
8. 10.1002/adma.20050260410.1002/adma.200502604 ↗
9. 10.1016/j.ssi.2008.02.01710.1016/j.ssi.2008.02.017 ↗
10. 10.1016/j.elecom.2007.02.00810.1016/j.elecom.2007.02.008 ↗
11. 10.1021/jacs.9b0835710.1021/jacs.9b08357 ↗
12. 10.1038/s41560-023-01208-910.1038/s41560-023-01208-9 ↗
13. 10.1038/nenergy.2016.14110.1038/nenergy.2016.141 ↗
14. 10.1021/acs.accounts.0c0087410.1021/acs.accounts.0c00874 ↗
15. 10.1016/0025-5408(79)90125-910.1016/0025-5408(79)90125-9 ↗
16. 10.1016/S0925-8388(97)00326-510.1016/S0925-8388(97)00326-5 ↗
17. 10.1016/0167-2738(96)00115-410.1016/0167-2738(96)00115-4 ↗
18. 10.1021/acsami.9b2262910.1021/acsami.9b22629 ↗
19. 10.1021/acs.chemmater.5c0062710.1021/acs.chemmater.5c00627 ↗
20. 10.1002/anie.20221758110.1002/anie.202217581 ↗
21. 10.1126/science.adt967810.1126/science.adt9678 ↗
22. 10.1016/j.ensm.2018.10.01210.1016/j.ensm.2018.10.012 ↗
23. 10.1021/cm030051610.1021/cm0300516 ↗
24. 10.1002/anie.20070114410.1002/anie.200701144 ↗
25. 10.1002/zaac.20100913410.1002/zaac.201009134 ↗
26. 10.1021/jacs.2c0986310.1021/jacs.2c09863 ↗
27. 10.1021/acs.chemmater.9b0185710.1021/acs.chemmater.9b01857 ↗
28. 10.1002/chem.20090302310.1002/chem.200903023 ↗
29. 10.1063/1.316721710.1063/1.3167217 ↗
30. 10.1107/S160057671900997X10.1107/S160057671900997X ↗
31. 10.1107/S002188980000248X10.1107/S002188980000248X ↗
32. 10.1006/jmre.2000.217110.1006/jmre.2000.2171 ↗
33. 10.1063/1.43618210.1063/1.436182 ↗
34. 10.1016/j.ssnmr.2011.04.00410.1016/j.ssnmr.2011.04.004 ↗
35. 10.1103/PhysRevB.54.1116910.1103/PhysRevB.54.11169 ↗
36. 10.1103/PhysRevLett.100.13640610.1103/PhysRevLett.100.136406 ↗
37. 10.1103/PhysRevB.59.175810.1103/PhysRevB.59.1758 ↗
38. 10.1021/acs.jpclett.8b0289210.1021/acs.jpclett.8b02892 ↗
39. 10.1107/S205225251701021110.1107/S2052252517010211 ↗
40. 10.1021/acs.chemmater.0c0389310.1021/acs.chemmater.0c03893 ↗
41. 10.1107/S205252061801571810.1107/S2052520618015718 ↗
42. 10.1107/S002188981103897010.1107/S0021889811038970 ↗
43. 10.1107/S056774087000357610.1107/S0567740870003576 ↗
44. 10.1002/chem.20090247010.1002/chem.200902470 ↗
45. 10.1021/acs.chemmater.2c0032010.1021/acs.chemmater.2c00320 ↗
46. 10.1021/acs.chemmater.2c0210110.1021/acs.chemmater.2c02101 ↗
47. 10.1021/acs.chemmater.3c0152510.1021/acs.chemmater.3c01525 ↗
48. 10.1021/acs.chemmater.6b0363010.1021/acs.chemmater.6b03630 ↗
49. 10.1002/anie.20070390010.1002/anie.200703900 ↗
50. 10.1002/zaac.20110015810.1002/zaac.201100158 ↗
51. 10.1021/jacs.7b0632710.1021/jacs.7b06327 ↗