Synthesis and Structural Characterization of Lithium Ionic Conductors Li₂MS₃ (M = Si, Si_0.5Ge_0.5, Ge) and Li₁₆Ge₅S₁₈

High Resolution Image Download MS PowerPoint Slide To develop inorganic Li conductors for all-solid-state Li-ion batteries, the present study clarified temperature-dependent structural changes in the Li 2 M S 3 ( M = Si, Si 0.5 Ge 0.5, Ge) phases, where new crystal structures favoring ionic conduction are potentially formed. Structural analysis was performed on powder X-ray diffraction data obtained at high temperatures. At 600 °C, tetragonal phases were formed in all three cases. Meanwhile, structural changes on cooling from 600 °C were different according to the M species, leading to various crystal systems at room temperature (monoclinic for M = Si, orthorhombic for Si 0.5 Ge 0.5, and hexagonal for Ge). Their ionic conductivities at 25 °C were 2.3 × 10 –5, 1.7 × 10 –7, and 8.6 × 10 –9 S cm –1, respectively, indicating that the conductivity depends significantly on the framework of the crystal structure. These phase identification results were further utilized to search the Li 2 S–GeS 2 pseudobinary system, revealing that the structure of Li 16 Ge 5 S 18 could not be assigned to any polymorphs identified for Li 2 M S 3 . This new crystalline phase showed an ionic conductivity of 7.2 × 10 –5 S cm –1 at room temperature, which is 4 orders of magnitude higher than that of hexagonal Li 2 GeS 3 . This study highlights a drastic increase in the lithium conductivity achieved by controlling the crystal structure of the Li 2 M S 3 -related materials.