Structural and Magnetic Transitions Caused by Dimer Formation in the CrCl₃–MoCl₃ Solid Solution

High Resolution Image Download MS PowerPoint Slide In this work, we apply the concept of solid solutions to the two 2D transition metal trihalides CrCl 3 and MoCl 3 . While CrCl 3 belongs to the magnetically active Cr X 3 family, the magnetism in MoCl 3 is intrinsically suppressed by the formation of aligned Mo–Mo dimers, which also distort the regular honeycomb lattice that is typical for the 2D transition metal trihalides. We report suitable synthesis conditions for the gapless solid solution and crystal growth by chemical vapor transport. The CrCl 3 –MoCl 3 solid solution was initially synthesized at 650 °C for 100 h under addition of MoCl 5 as mineralizer, and bulk crystals were subsequently grown by vapor transport in a temperature gradient from 600 °C → 550 °C for 60 h. The obtained solid solution exhibits multiple composition-dependent phase transitions at room temperature, as confirmed by powder X-ray diffraction measurements. The possible presence of Mo–Mo dimers in the solid solution was further investigated by infrared, Raman, electron energy loss, and nuclear quadrupole resonance spectroscopies. The combined results indicate that the Mo–Mo dimers are present over a wide range of compositions. Their orientation changes from parallel alignment for compositions from 70% ≤ c (Mo 3+ ) ≤ 100% to random orientation for samples with c (Mo 3+ ) < 70% content, which significantly affects the course of lattice parameters. Finally, the magnetic properties of the powder samples show a correlation between the Mo 3+ content and the transition temperature into the low-temperature phase.