Synthesis and Characterization of Lamellar and Hexagonal Mesostructured Aluminophosphates Using Alkyltrimethylammonium Cations as Structure-Directing Agents
Source abstract
Abstract
Lamellar and hexagonal mesostructured aluminophosphates (AlPOs) were prepared and characterized. The lamellar mesostructured AlPO (APW-1) formed hydrothermally and the condensed framework was composed of alternating AlO 4 and PO 4 units. The hexagonal mesostructured AlPO (APW-2) is formed by transformation of a layered precipitate composed of both aluminophosphate oligomers and alkyltrimethylammonium (ATMA) cations. Calcined APW-2 had a mesoporosity with the BET surface area of 980 m 2 g - 1 and a pore diameter of 1.8 nm after substantial shrinkage of the framework. Lamellar APW-1 formed under most of the conditions surveyed, while hexagonal APW-2 was obtained under very restricted conditions. In this system, the charge matching in the products is the most important factor, although the assemblies of ATMA cations are essential as the structure-directing agents.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Mesoporous Materials and Catalysis · Zeolite Catalysis and Synthesis · Layered Double Hydroxides Synthesis and Applications
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Department of Applied Chemistry, Waseda University, Ohkubo-3, Shinjuku-ku, Tokyo 169-8555, Japan, and Kagami Memorial Laboratory for Materials Science and Technology, Waseda University, Nishiwaseda-2, Shinjuku-ku, Tokyo 169-0051, Japan
References (63)
Show source-provided references
1. Wilson S. T. · J. Am. Chem. Soc. · 1982 · 104 · 114710.1021/ja00368a063 ↗
2. Lok B. M. · J. Am. Chem. Soc. · 1984 · 106 · 609310.1021/ja00332a064 ↗
3. Davis M. E. · Nature · 1988 · 331 · 69910.1038/331699a0 ↗
4. Huo Q. · J. Chem. Soc., Chem. Commun. · 1992 · 875 · 876
5. Yanagisawa T. · Bull. Chem. Soc. Jpn. · 1990 · 63 · 992
6. Kresge C. T. · Nature · 1992 · 359 · 71210.1038/359710a0 ↗
7. Beck J. S. · J. Am. Chem. Soc. · 1992 · 114 · 1084310.1021/ja00053a021 ↗
8. Huo Q. · Nature · 1994 · 368 · 32110.1038/368321a0 ↗
9. Huo Q. · Chem. Mater. · 1994 · 6 · 1191
10. Behrens P. · Angew. Chem., Int. Ed. Engl. · 1996 · 35 · 518
11. Sayari A. · Microporous Mater. · 1997 · 12 · 17710.1016/S0927-6513(97)00059-X ↗
12. Biomimetic Materials Chemistry · 1996
13. Czarnetzki B. K. · J. Inorg. Chem. · 1993 · 32 · 5033
14. Fyfe C. A. · 1995
15. Kimura T. · Phosphorus Res. Bull. · 1996 · 6 · 20810.3363/prb1992.6.0_205 ↗
16. Oliver S. · Nature · 1995 · 378 · 5010.1038/378047a0 ↗
17. Oliver S. · Adv. Mater. · 1995 · 7 · 935
18. Ozin G. A. · Adv. Mater. · 1995 · 7 · 947
19. Oliver S. R. J. · J. Mater. Chem. · 1998 · 8 · 1085
20. Oliver S. R. J. · Inorg. Chem. · 1998 · 37 · 5028
21. Chenite A. · Chem. Commun. · 1996 · 411 · 412
22. Sayari A. · Chem. Commun. · 1996 · 413 · 414
23. Sayari A. · Chem. Mater. · 1996 · 8 · 2088
24. Gao Q. · J. Chem. Soc., Dalton Trans. · 1996 · 3303 · 3307
25. Gao Q. · Chem. Mater. · 1997 · 9 · 462
26. Pophal C. · Stud. Surf. Sci. Catal. · 1997 · 105 · 108
27. Kimura T. · 1996
28. Kimura T. · Chem. Lett. · 1997 · 983 · 984
29. Feng P. · Chem. Commun. · 1997 · 949 · 950
30. Chakraborty B. · Chem. Commun. · 1997 · 911 · 912
31. Chakraborty B. · Appl. Catal. · 1998 · 167 · 18110.1016/S0926-860X(97)00319-0 ↗
32. Zhao D. · Chem. Commun. · 1997 · 1009 · 1010
33. Zhao D. · J. Phys. Chem. · 1997 · 101 · 6948
34. Luan Z. · J. Phys. Chem. · 1998 · 102 · 125910.1021/jp973109a ↗
35. Luan Z. · Microporous Mesoporous Mater. · 1998 · 20 · 9910.1016/S1387-1811(97)00018-8 ↗
36. Holland B. T. · J. Am. Chem. Soc. · 1997 · 119 · 6803
37. Cheng S. · Chem. Mater. · 1997 · 9 · 179610.1021/cm9700357 ↗
38. Kimura T. · Chem. Commun. · 1998 · 559 · 560
39. Kimura T. · Microporous Mesoporous Mater. · 1998 · 22 · 12610.1016/S1387-1811(98)00072-9 ↗
40. Davis M. E. · J. Am. Chem. Soc. · 1989 · 111 · 392410.1021/ja00193a025 ↗
41. Müller D. · Chem. Phys. Lett. · 1984 · 109 · 33610.1016/0009-2614(84)85596-7 ↗
42. Beck J. S. · Chem. Mater. · 1994 · 6 · 1821
43. Mortlock R. F. · J. Phys. Chem. · 1993 · 97 · 782
44. Mortlock R. F. · J. Phys. Chem. · 1993 · 97 · 774
45. Blackwell C. S. · J. Phys. Chem. · 1984 · 88 · 613910.1021/j150669a016 ↗
46. Horváth G. · J. Chem. Eng. Jpn. · 1983 · 16 · 47510.1252/jcej.16.470 ↗
47. Müller D. · J. Chem. Soc., Dalton Trans. · 1986 · 1277 · 1281
48. Jones R. H. · J. Chem. Soc., Chem. Commun. · 1991 · 1266 · 1268
49. Thomas J. M. · J. Chem. Soc., Chem. Commun. · 1992 · 929 · 931
50. Chippindale A. M. · J. Solid State Chem. · 1994 · 111 · 2510.1006/jssc.1994.1193 ↗
51. Chippindale A. M. · J. Chem. Soc., Dalton Trans. · 1997 · 2639 · 2643
52. Huo Q. · Science · 1995 · 268 · 132710.1126/science.268.5215.1327 ↗
53. Huo Q. · Chem. Mater. · 1996 · 8 · 1160
54. Fyfe C. A. · J. Am. Chem. Soc. · 1995 · 117 · 9714
55. Khimyak Y. Z. · J. Chem. Soc., Faraday Trans. · 1998 · 94 · 224710.1039/a802221f ↗
56. Khimyak Y. Z. · Chem. Mater. · 1998 · 10 · 226510.1021/cm9807081 ↗
57. Vartuli J. C. · Chem. Mater. · 1994 · 6 · 2326
58. Kuperman A. · Nature · 1993 · 365 · 24210.1038/365239a0 ↗
59. Tieli W. · J. Solid State Chem. · 1990 · 89 · 395
60. Chippindale A. M. · J. Solid State Chem. · 1992 · 96 · 21010.1016/S0022-4596(05)80312-3 ↗
61. Inagaki S. · J. Chem. Soc., Chem. Commun. · 1993 · 680 · 682
62. Inagaki S. · Bull. Chem. Soc. Jpn. · 1996 · 69 · 145710.1246/bcsj.69.1449 ↗
63. Chen C.-Y. · Microporous Mater. · 1995 · 4 · 20