Mechanisms of Electronic and Ionic Transport during Mg Intercalation in Mg–S Cathode Materials and Their Decomposition Products

Smobin Vincent, Jin Hyun Chang, Pieremanuele Canepa, Juan Maria García-Lastra

Chemistry of Materials· Volume 35· Issue 9

Abstract

High Resolution Image Download MS PowerPoint Slide Rechargeable Mg–S batteries are attractive for next-generation energy storage devices due to their high theoretical energy density (1684 W h kg –1 and 3286 W h L –1 ) and low costs. The poor cycling performance of Mg–S batteries is linked to the formation of the solid discharge products, i.e., MgS 2 and MgS, which are electronic and ionic insulators. However, the formation of MgS itself contradicts such a premise because it requires further oxidation of MgS 2 . Indeed, the insulating nature of MgS 2 should inhibit such an oxidation process in the first place. Using first-principles calculations and ab initio molecular dynamics simulations, we evaluate the charge transport associated with point defects in MgS 2 and MgS. In MgS 2, the single-electron polaron is the most abundant type of defect that emerges from our model, which appears at a low concentration at thermodynamic equilibrium but displays high mobility. However, under conditions far from thermodynamic equilibrium, mimicking those for battery operations, the concentration of electron polarons increases, enhancing the electronic conductivity in MgS 2 . We demonstrate that in regimes far from thermodynamic equilibrium, the single-electron polarons coalesce to form double-electron polarons, whose mobilities are similar to that of a single-electron polaron. MgS 2 holds electronic conduction through a polaron migration mechanism for ≤3 μm thick deposits, enabling further oxidation to form MgS. For MgS, our model suggests that the doubly positive Mg interstitial and doubly negative Mg vacancy are identified as the prevalent defects with high concentrations. However, due to the low mobility of these defects, their contribution to charge transport is negligible, which stops the oxidation process and severely hinders battery cyclability. Our results indicate that rechargeable Mg–S batteries can be developed if we ensure that the battery discharge does not push the oxidation process beyond the formation of MgS 2 .
Source: openalex_inverted_index · Quality: baseline

Research context

OpenAlex topics: Advancements in Battery Materials · Molten salt chemistry and electrochemical processes · Advanced Battery Materials and Technologies

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

Affiliations

Department of Energy Conversion and Storage, Technical University of Denmark, Kongens Lyngby 2800, Denmark

Department of Materials Science and Engineering, National University of Singapore, Singapore 117575

Department Chemical and Biomolecular Engineering, National University of Singapore, Singapore 117585

Funding

H2020 Future and Emerging Technologies · National Research Foundation

References (41)

Show source-provided references
1. 10.1038/s43246-021-00143-010.1038/s43246-021-00143-0 ↗
2. 10.1002/adma.20190112510.1002/adma.201901125 ↗
3. 10.1002/aenm.20200008910.1002/aenm.202000089 ↗
4. 10.1002/adma.20180282210.1002/adma.201802822 ↗
5. 10.1039/c0ee00777c10.1039/c0ee00777c ↗
6. 10.1038/s41560-018-0107-210.1038/s41560-018-0107-2 ↗
7. 10.1016/0016-7037(95)00038-210.1016/0016-7037(95)00038-2 ↗
8. 10.1038/3503755310.1038/35037553 ↗
9. 10.1149/2.0161513jes10.1149/2.0161513jes ↗
10. 10.1002/aenm.20140115510.1002/aenm.201401155 ↗
11. 10.1039/C9CC02556A10.1039/C9CC02556A ↗
12. 10.1002/adma.20170431310.1002/adma.201704313 ↗
13. 10.1016/j.electacta.2020.13578710.1016/j.electacta.2020.135787 ↗
14. 10.2320/matertrans1960.25.69210.2320/matertrans1960.25.692 ↗
15. 10.2320/matertrans1989.36.126310.2320/matertrans1989.36.1263 ↗
16. 10.1557/JMR.1994.013210.1557/JMR.1994.0132 ↗
17. 10.1021/acs.chemmater.9b0269210.1021/acs.chemmater.9b02692 ↗
18. 10.1016/0927-0256(96)00008-010.1016/0927-0256(96)00008-0 ↗
19. 10.1103/PhysRevB.54.1116910.1103/PhysRevB.54.11169 ↗
20. 10.1103/PhysRevLett.77.386510.1103/PhysRevLett.77.3865 ↗
21. 10.1088/2053-1583/aacfc110.1088/2053-1583/aacfc1 ↗
22. 10.1063/1.156406010.1063/1.1564060 ↗
23. 10.1063/1.240466310.1063/1.2404663 ↗
24. 10.1103/PhysRev.139.A79610.1103/PhysRev.139.A796 ↗
25. 10.1103/PhysRevB.34.539010.1103/PhysRevB.34.5390 ↗
26. 10.1103/PhysRevB.75.23510210.1103/PhysRevB.75.235102 ↗
27. 10.1103/PhysRevB.50.1795310.1103/PhysRevB.50.17953 ↗
28. 10.21105/joss.0071710.21105/joss.00717 ↗
29. 10.1103/PhysRevLett.102.01640210.1103/PhysRevLett.102.016402 ↗
30. 10.1016/j.cpc.2018.01.00410.1016/j.cpc.2018.01.004 ↗
31. Tilley R. J. · 200810.1002/9780470380758 ↗
32. 10.1063/1.132322410.1063/1.1323224 ↗
33. 10.1088/1361-648X/aa680e10.1088/1361-648X/aa680e ↗
34. 10.1107/S205322961700068710.1107/S2053229617000687 ↗
35. 10.1021/ja01186a01810.1021/ja01186a018 ↗
36. Lany, S. Polymorphism, Band-Structure, Band-Lineup, and Alloy Energetics of the Group II Oxides and Sulfides MgO, ZnO, CdO, MgS, ZnS, CdS. Oxide-based Materials and Devices V. 2014; pp 109–116.10.1117/12.2043587 ↗
37. 10.1063/1.498692910.1063/1.4986929 ↗
38. 10.1021/acs.chemmater.7b0021710.1021/acs.chemmater.7b00217 ↗
39. 10.1007/s11837-013-0755-410.1007/s11837-013-0755-4 ↗
40. 10.1016/j.softx.2015.06.00110.1016/j.softx.2015.06.001 ↗
41. Guard, U. C. Chemical Hazard Response Information System (CHRIS)-Hazardous Chemical Data; Commandant Instruction, 1999; p 16465.