O3 to O1 Phase Transitions in Highly Delithiated NMC811 at Elevated Temperatures
Source abstract
Abstract
High Resolution Image Download MS PowerPoint Slide Nickel-rich layered oxide cathodes such as NMC811 (Li x Ni 0.8 Mn 0.1 Co 0.1 O 2 ) currently have the highest practical capacities of cathodes used commercially, approaching 200 mAh/g. Lithium is removed from NMC811 via a solid-solution behavior when delithiated to x Li > 0.10, maintaining the same layered (O3 structure) throughout as observed via operando diffraction measurements. Although it is possible to further delithiate NMC811, it is kinetically challenging, and there are significant side reactions between the electrolyte and cathode surface. Here, small format, NMC811-graphite pouch cells were charged to high voltages at elevated temperatures and held for days to access high states of delithiation. Rietveld refinements on high-resolution diffraction data and indexing of selected area electron diffraction patterns, both acquired ex situ, show that NMC811 undergoes a partial and reversible transition from the O3 to the O1 phase under these conditions. The O1 phase fraction depends not only on the concentration of intercalated lithium but also on the hold temperature and hold time, indicating that the phase transition is kinetically controlled. 1 H NMR spectroscopy shows that the proton concentration decreases with O1 phase fraction and is not, therefore, likely to be driving the O3–O1 phase transition.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Advancements in Battery Materials · Advanced Battery Materials and Technologies · Ferroelectric and Piezoelectric Materials
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Yusuf Hamied Department of Chemistry, University of Cambridge, Cambridge CB2 1EW, U.K.
The Faraday Institution, Quad One, Harwell Science and Innovation Campus, Didcot OX11 0RA, U.K.
Department of Materials Science and Metallurgy, University of Cambridge, 27 Charles Babbage Road, Cambridge CB3 0FS, U.K.
Funding
Engineering and Physical Sciences Research Council · Faraday Institution
References (36)
Show source-provided references
1. 10.1038/s41560-019-0513-010.1038/s41560-019-0513-0 ↗
2. 10.1149/2.0021707jes10.1149/2.0021707jes ↗
3. 10.1039/D1EE04053G10.1039/D1EE04053G ↗
4. 10.1149/1945-7111/ac035910.1149/1945-7111/ac0359 ↗
5. 10.1038/ncomms452910.1038/ncomms4529 ↗
6. 10.1021/acs.chemmater.9b0014010.1021/acs.chemmater.9b00140 ↗
7. 10.1016/j.joule.2022.09.00810.1016/j.joule.2022.09.008 ↗
8. 10.1038/s41563-020-0767-810.1038/s41563-020-0767-8 ↗
9. 10.1149/1.139335610.1149/1.1393356 ↗
10. 10.1149/1.151985010.1149/1.1519850 ↗
11. 10.1149/1.183659410.1149/1.1836594 ↗
12. 10.1016/0378-4363(80)90214-410.1016/0378-4363(80)90214-4 ↗
13. 10.1149/1.183861010.1149/1.1838610 ↗
14. 10.1103/PhysRevB.58.297510.1103/PhysRevB.58.2975 ↗
15. 10.1016/S0167-2738(00)00441-010.1016/S0167-2738(00)00441-0 ↗
16. 10.1039/b003377o10.1039/b003377o ↗
17. 10.1103/PhysRevB.66.06411210.1103/PhysRevB.66.064112 ↗
18. 10.1002/adfm.20120069310.1002/adfm.201200693 ↗
19. 10.1021/acs.chemmater.7b0530510.1021/acs.chemmater.7b05305 ↗
20. 10.1039/D0SC03940C10.1039/D0SC03940C ↗
21. 10.1088/0960-1317/11/4/30110.1088/0960-1317/11/4/301 ↗
22. Carter C. B. · 201610.1007/978-3-319-26651-0 ↗
23. De Graef M. · 200310.1017/CBO9780511615092 ↗
24. 10.1039/B600529B10.1039/B600529B ↗
25. 10.1021/cr020734p10.1021/cr020734p ↗
26. 10.1039/C8TA07460G10.1039/C8TA07460G ↗
27. 10.1021/cm020638510.1021/cm0206385 ↗
28. 10.1039/a900016j10.1039/a900016j ↗
29. Genreith-Schriever, A.; Banerjee, H.; Grey, C.; Morris, A. Ni-O-redox, oxygen loss and singlet oxygen formation in LiNiO2 cathodes for Li-ion batteries. arXiv preprint arXiv:2205.10462, 2022.
30. 10.1002/anie.20181247210.1002/anie.201812472 ↗
31. 10.1021/acs.inorgchem.0c0289910.1021/acs.inorgchem.0c02899 ↗
32. 10.1021/acs.jpcc.8b0784810.1021/acs.jpcc.8b07848 ↗
33. 10.1149/2.0311807jes10.1149/2.0311807jes ↗
34. 10.1021/jacs.0c0636310.1021/jacs.0c06363 ↗
35. 10.1038/s41586-021-03584-210.1038/s41586-021-03584-2 ↗
36. 10.1039/D1TA03066C10.1039/D1TA03066C ↗