In situ Supported Nanoscale RuxTi1−xO2 on Anatase TiO2 with Improved Electroactivity
Source abstract
Abstract
Electrocatalytic coatings with a novel supported structure of active nanoscale rutile RuxTi1−xO2 particles (3 nm) onto in situ formed anatase TiO2 (20 nm) were achieved by a facile sol−gel/solvothermal route. They exhibit significantly enhanced catalytic activity for electrochemical evolution of chlorine.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Electrochemical Analysis and Applications · Electrocatalysts for Energy Conversion · Advanced battery technologies research
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Physikalische Chemie
Technische Chemie
Bayer MaterialScience AG, 51368 Leverkusen, Germany
References (35)
Show source-provided references
1. aBeer, H. B.British Patent 1 147 442, 1965.10.5694/j.1326-5377.1965.tb71806.x ↗
2. De Nora O. · Chem. Eng. Technol. · 1970 · 42 · 222
3. Trasatti S. · Electrochim. Acta · 2000 · 45 · 237710.1016/S0013-4686(00)00338-8 ↗
4. Moussallem I. · J. Appl. Electrochem. · 2008 · 38 · 117710.1007/s10800-008-9556-9 ↗
5. Hine F. · J. Electrochem. Soc. · 1977 · 124 · 50010.1149/1.2133337 ↗
6. Arikawa T. · J. Phys. Chem. B · 1998 · 102 · 373610.1021/jp9728114 ↗
7. Panić V. V. · Colloids Surf., A · 1999 · 157 · 26910.1016/S0927-7757(99)00094-1 ↗
8. Roginskaya Yu. E. · Electrochim. Acta · 1995 · 40 · 81710.1016/0013-4686(95)00002-V ↗
9. Schlögl R. · Angew. Chem., Int. Ed. · 2004 · 43 · 162810.1002/anie.200301684 ↗
10. Over H. · Science · 2000 · 287 · 147410.1126/science.287.5457.1474 ↗
11. Hansen H. A. · Phys. Chem. Chem. Phys. · 2010 · 12 · 28310.1039/B917459A ↗
12. Wu N. L. · Science · 1999 · 285 · 137510.1126/science.285.5432.1375 ↗
13. Chen B. · Phys. Rev. Lett. · 2007 · 98 · 10610310.1103/PhysRevLett.98.106103 ↗
14. Joo S. H. · Nat. Mater. · 2009 · 8 · 12610.1038/nmat2329 ↗
15. Gupta G. · Chem. Mater. · 2006 · 18 · 623910.1021/cm0616681 ↗
16. Feng Y. · Chem. Mater. · 2008 · 20 · 2610.1021/cm7024763 ↗
17. Swamy V. · Phys. Rev. B · 2008 · 77 · 19541410.1103/PhysRevB.77.195414 ↗
18. Ocaña M. · J. Solid State Chem. · 1988 · 75 · 36410.1016/0022-4596(88)90176-4 ↗
19. Liu H. · Langmuir · 2003 · 19 · 300110.1021/la026600o ↗
20. Oliveira M. M. · Chem. Mater. · 2003 · 15 · 190310.1021/cm0210344 ↗
21. Vegard L. · Z. Phys. · 1921 · 5 · 1710.1007/BF01349680 ↗
22. Nakano H. · J. Phys.: Condens. Matter · 2009 · 21 · 064214
23. Korotcov A. V. · J. Raman Spectrosc. · 2007 · 38 · 73710.1002/jrs.1655 ↗
24. Chang K. H. · Chem. Mater. · 2007 · 19 · 211210.1021/cm0629661 ↗
25. Colomer M. T. · J. Eur. Ceram. Soc. · 2007 · 27 · 236910.1016/j.jeurceramsoc.2006.09.006 ↗
26. Cushing B. L. · Chem. Rev. · 2004 · 104 · 389310.1021/cr030027b ↗
27. Li G. · J. Am. Chem. Soc. · 2005 · 127 · 865910.1021/ja050517g ↗
28. Barnard A. S. · Nano Lett. · 2005 · 5 · 126110.1021/nl050355m ↗
29. Pillai S. C. · J. Phys. Chem. C · 2007 · 111 · 160510.1021/jp065933h ↗
30. Ryan J. V. · Nature · 2000 · 406 · 16910.1038/35018040 ↗
31. Galizzioli D. · J. Appl. Electrochem. · 1974 · 4 · 5710.1007/BF00615906 ↗
32. Burrows I. R. · Electrochim. Acta · 1978 · 23 · 49310.1016/0013-4686(78)85026-9 ↗
33. Alves V. A. · J. Appl. Electrochem. · 1998 · 28 · 89910.1023/A:1003431130954 ↗
34. Jirkovský J. · J. Electrochem. Soc. · 2005 · 152 · A161310.1149/1.1939147 ↗
35. Ruban A. · J. Mol. Catal. A · 1997 · 115 · 42110.1016/S1381-1169(96)00348-2 ↗