Surface-Supported, Highly Ordered Macroporous Crystalline TiO2 Thin Films Robust up to 1000 °C
Source abstract
Abstract
Macroporous crystalline TiO2 thin film is achieved by using an amphiphilic triblock copolymer of PEO-PS-PEO as a templating agent, coupled with a good-poor solvent pair induced phase separation process and sol−gel chemistry. The macroporus TiO2 exhibits unusual thermal structural stability up to at least 1000 °C.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Mesoporous Materials and Catalysis · Polyoxometalates: Synthesis and Applications · Catalytic Processes in Materials Science
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Max-Planck Institute for Polymer Research, Ackermannweg 10, D-55128, Mainz, Germany, and Institute of Physical Chemistry, University of Mainz, Welderweg 11, D-55099, Mainz, Germany
References (35)
Show source-provided references
1. Figueroa O. L. · Sens. Actuators, B · 2005 · 107 · 83910.1016/j.snb.2004.12.025 ↗
2. Fujishima A. · Proc. Jpn. Acad., B · 2005 · 81 · 3310.2183/pjab.81.33 ↗
3. Gratzel M. · J. Photochem. Photobiol., A · 2004 · 164 · 310.1016/j.jphotochem.2004.02.023 ↗
4. Heller A. · Acc. Chem. Res. · 1995 · 28 · 50310.1021/ar00060a006 ↗
5. Henderson M. A. · J. Phys. Chem. B · 2005 · 109 · 1206210.1021/jp0507546 ↗
6. Linsebigler A. L. · Chem. Rev. · 1995 · 95 · 73510.1021/cr00035a013 ↗
7. Stein A. · Curr. Opin. Solid State Mater. · 2001 · 5 · 55310.1016/S1359-0286(01)00022-5 ↗
8. Soler-illia G. J. D. · Chem. Rev. · 2002 · 102 · 409310.1021/cr0200062 ↗
9. Bartl M. H. · Acc. Chem. Res. · 2005 · 38 · 26310.1021/ar040177o ↗
10. Brinker C. J. · Adv. Mater. · 1999 · 11 · 57910.1002/(SICI)1521-4095(199905)11:7<579::AID-ADMA579>3.0.CO;2-R ↗
11. Choi S. Y. · Adv. Funct. Mater. · 2004 · 14 · 33510.1002/adfm.200305039 ↗
12. Choi S. Y. · Small · 2005 · 1 · 22610.1002/smll.200400038 ↗
13. Crepaldi E. L. · J. Am. Chem. Soc. · 2003 · 125 · 977010.1021/ja030070g ↗
14. Soler-Illia G. · Curr. Opin. Colloid Interface Sci. · 2003 · 8 · 10910.1016/S1359-0294(03)00002-5 ↗
15. Yang P. D. · Nature · 1998 · 396 · 15210.1038/24132 ↗
16. Fuertes M. C. · Chem. Mater. · 2006 · 18 · 210910.1021/cm0527064 ↗
17. Angelome P. C. · Adv. Mater. · 2006 · 18 · 239710.1002/adma.200600439 ↗
18. Nakanishi K. · Bull. Chem. Soc. Jpn. · 2006 · 79 · 67310.1246/bcsj.79.673 ↗
19. Bosc F. · Chem. Mater. · 2003 · 15 · 246310.1021/cm031025a ↗
20. Crepaldi E. L. · New J. Chem. · 2003 · 27 · 910.1039/b205497n ↗
21. Kirsch B. L. · J. Phys. Chem. B · 2004 · 108 · 1269810.1021/jp036442p ↗
22. Smarsly B. · Chem. Mater. · 2004 · 16 · 294810.1021/cm0495966 ↗
23. Long J. W. · Chem. Rev. · 2004 · 104 · 446310.1021/cr020740l ↗
24. Turner M. E. · Adv. Mater. · 2001 · 13 · 18010.1002/1521-4095(200102)13:3<180::AID-ADMA180>3.0.CO;2-Y ↗
25. Floudas G. · Macromolecules · 1997 · 30 · 438110.1021/ma9616118 ↗
26. Cheng Y. J. · J. Am. Chem. Soc. · 2006 · 128 · 465810.1021/ja0562853 ↗
27. Cheng Y. J. · Small · 2007 · 3 · 137910.1002/smll.200600712 ↗
28. Cheng Y. J. · Macro. Rapid. Commun. · 2007 · 28 · 139210.1002/marc.200700165 ↗
29. Soo P. L. · J. Polym. Sci., Part B: Polym. Phys. · 2004 · 42 · 92310.1002/polb.10739 ↗
30. Zhang L. F. · Polym. Adv. Technol. · 1998 · 9 · 67710.1002/(SICI)1099-1581(1998100)9:10/11<677::AID-PAT845>3.0.CO;2-# ↗
31. Provencher S. W. · Comput. Phys. Commun. · 1982 · 27 · 22910.1016/0010-4655(82)90174-6 ↗
32. Provencher S. W. · Comput. Phys. Commun. · 1982 · 27 · 21310.1016/0010-4655(82)90173-4 ↗
33. Cheng P. · Mater. Lett. · 2003 · 57 · 298910.1016/S0167-577X(02)01409-X ↗
34. Rao C. N. R. · J. Phys. Chem. Solids · 1959 · 11 · 17310.1016/0022-3697(59)90056-3 ↗
35. Reidy D. J. · J. Mater. Chem. · 2005 · 15 · 349410.1039/b503395k ↗