NASICON-Structured NaSn2(PO4)3 with Excellent High-Rate Properties as Anode Material for Lithium Ion Batteries
Source abstract
Abstract
Advanced Li-ion batteries with high rate properties are in high demand and have generated much attention in the research community. Here, we present a simple sol–gel and solid-state reaction to synthesize NASICON-structured NaSn 2 (PO 4 ) 3 as anode material for lithium-ion batteries. The obtained material exhibits excellent cycling performance and high rate capacity for half cell and LiFePO 4 /NaSn 2 (PO 4 ) 3 full cell. Cyclic voltammograms (CV) and galvanostatic intermittent titration technique (GITT) were used to analyze the kinetics and thermodynamics of the electrode. Morphology and structure evolution of the NaSn 2 (PO 4 ) 3 electrode after cycling were explored by transmission electron microscopy (TEM). These results showed nanoscale Sn was uniformly dispersed in the lithium phosphate matrix during the first discharge. It is proposed that the enhanced properties are attributed to the “in situ” formation of the ionic conductor as protective matrices, which prevents the aggregation of nanoparticles during the cycling and provides Li + diffusion channels in the electrode for fast electrochemical reaction.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Advancements in Battery Materials · Advanced Battery Materials and Technologies · Extraction and Separation Processes
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Qingdao Industrial Energy Storage Research Institute, Qingdao Institute of Bioenergy and Bioprocess Technology, Chinese Academy of Sciences, Qingdao 266101, P. R. China
University of Chinese Academy of Sciences, Beijing 100049, P. R.China
Funding
Ministry of Science and Technology of the People's Republic of China · National Natural Science Foundation of China · Key Technology Research Projects of Qingdao
References (37)
Show source-provided references
1. 10.1021/acs.chemmater.5b0021810.1021/acs.chemmater.5b00218 ↗
2. 10.1002/adma.20070292810.1002/adma.200702928 ↗
3. 10.1002/adma.20060073310.1002/adma.200600733 ↗
4. 10.1021/jz500224210.1021/jz5002242 ↗
5. 10.1021/nn506223h10.1021/nn506223h ↗
6. 10.1149/1.139071510.1149/1.1390715 ↗
7. 10.1016/j.jpowsour.2015.03.09310.1016/j.jpowsour.2015.03.093 ↗
8. 10.1021/cm504101h10.1021/cm504101h ↗
9. 10.1021/acsami.5b0277410.1021/acsami.5b02774 ↗
10. 10.1021/am506818h10.1021/am506818h ↗
11. 10.1021/cm900613d10.1021/cm900613d ↗
12. 10.1149/1.139076910.1149/1.1390769 ↗
13. 10.1149/1.139388910.1149/1.1393889 ↗
14. 10.1016/S0378-7753(02)00061-710.1016/S0378-7753(02)00061-7 ↗
15. 10.1016/j.electacta.2003.12.02410.1016/j.electacta.2003.12.024 ↗
16. 10.1016/j.carbon.2005.01.00810.1016/j.carbon.2005.01.008 ↗
17. 10.1016/j.jpowsour.2006.02.06810.1016/j.jpowsour.2006.02.068 ↗
18. 10.1021/ja034552410.1021/ja0345524 ↗
19. 10.1021/cm801853c10.1021/cm801853c ↗
20. 10.1021/jp908244m10.1021/jp908244m ↗
21. 10.1126/science.276.5317.139510.1126/science.276.5317.1395 ↗
22. 10.1021/jp035769n10.1021/jp035769n ↗
23. 10.1149/1.183794110.1149/1.1837941 ↗
24. 10.1149/1.139252410.1149/1.1392524 ↗
25. 10.1016/S0013-4686(02)00017-810.1016/S0013-4686(02)00017-8 ↗
26. 10.1016/j.jnoncrysol.2014.05.03410.1016/j.jnoncrysol.2014.05.034 ↗
27. 10.1021/jp908560210.1021/jp9085602 ↗
28. 10.1021/ic403053710.1021/ic4030537 ↗
29. 10.1063/1.486966410.1063/1.4869664 ↗
30. 10.1016/j.matlet.2009.08.05710.1016/j.matlet.2009.08.057 ↗
31. 10.1016/j.jpowsour.2012.05.11710.1016/j.jpowsour.2012.05.117 ↗
32. 10.1021/cm801607e10.1021/cm801607e ↗
33. 10.1016/S0378-7753(00)00569-310.1016/S0378-7753(00)00569-3 ↗
34. 10.1021/jp062875r10.1021/jp062875r ↗
35. 10.1039/c4cp00746h10.1039/c4cp00746h ↗
36. 10.1002/adma.20070136410.1002/adma.200701364 ↗
37. 10.1002/aenm.20147005210.1002/aenm.201470052 ↗