Chemical Modification of Single-Walled Carbon Nanotubes for the Reinforcement of Precursor-Derived Ceramics

Single-walled carbon nanotubes (SWNTs) were incorporated into precursor-derived ceramics made from a polysilazane. To improve the dispersion of the nanotubes in the liquid precursor and finally in the ceramic matrix, the SWNTs were chemically modified by (iodomethyl)trimethylsilane via a radical reaction. The functionalization degree of the modified SWNTs was determined to be 3 atom %. Microscopic investigation combined with viscosity measurements and thixotropy tests demonstrated that the functionalized SWNTs are more homogeneously dispersed in the liquid SWNT/polymer mixtures and the solid cross-linked precursor, as compared to pristine nanotubes. SWNT/Si−C−N ceramics with nanotube contents of up to 1 wt % were obtained through pyrolysis of cross-linked SWNT/polymer composites at 1000 °C. The presence of intact nanotubes in these composites could be verified by scanning transmission electron microscopy. The high viscosity of the SWNT/polysilazane mixtures was identified as an important prerequisite for attaining good nanotube dispersion in the Si−C−N matrix.