Synthesis, Structure, and Electrochemical Performance of High Capacity Li₂Cu_0.5Ni_0.5O₂ Cathodes

Orthorhombic Li 2 NiO 2, Li 2 CuO 2, and solid solutions thereof have been studied as potential cathode materials for lithium-ion batteries due to their high theoretical capacity and relatively low cost. While neither endmember shows good cycling stability, the intermediate composition, Li 2 Cu 0.5 Ni 0.5 O 2, yields reasonably high reversible capacities. A new synthetic approach and detailed characterization of this phase and the parent Li 2 CuO 2 are presented. The cycle life of Li 2 Cu 0.5 Ni 0.5 O 2 is shown to depend critically on the voltage window. The formation of Cu 1+ at low voltage and oxygen evolution at high voltage limit the electrochemical reversibility. In situ X-ray absorption spectroscopy (XAS), in situ Raman spectroscopy, and gas evolution measurements are used to follow the chemical and structural changes that occur as a function of cell voltage.