Multistep, Low-Temperature Pseudomorphic Transformations of Nanostructured Silica to Titania via a Titanium Oxyfluoride Intermediate

Justin C. Lytle, Hongwei Yan, Ryan T. Turgeon, Andreas Stein

Chemistry of Materials· Volume 16· Issue 20
Publisher page

Abstract

Synthetic silica preforms with an inverse opal or three-dimensionally ordered macroporous (3DOM) structure were converted to 3DOM TiOF 2 and subsequently to 3DOM TiO 2 by solid−gas pseudomorphic transformation reactions, reactions which maintain the shape and structural features of the original material. 3DOM SiO 2 preforms with periodic arrays of macropores and hierarchical feature sizes (e.g., macropore separation 334 nm, average wall thickness 59 nm) were prepared by colloidal crystal templating. They were reacted with TiF 4 in sealed steel pipes at 190, 235, and 300 °C. At 190 °C no conversion took place, while at 300 °C the material was converted mostly to crystalline TiOF 2 with an irregular structure. However, at 235 °C the periodic macroporous structure of the preform was maintained with little change in average pore separation. In these samples, the initially smooth wall structure of 3DOM SiO 2 was largely replaced by interconnected TiOF 2 cubes with edge lengths of 133 nm. The X-ray diffraction (XRD) pattern showed sharp lines of TiOF 2 . The product exhibited opalescence similar to that of the preform, giving a visual confirmation of the success of the pseudomorphic transformation on an extended length scale. An analogous transformation was also investigated with spherical silica preforms. Different stages of transformation were observed by scanning electron microscopy, permitting a discussion of critical parameters in these conversions. The macroporous TiOF 2 product was subsequently converted to TiO 2 (anatase) by reaction with moist air at 300 °C. In this reaction, pseudomorphism was observed on the scale of tens of micrometers, on the submicrometer macropore scale, and on the scale of the cubic particles forming the wall skeleton. The sample was still composed of interconnected cubes with similar edge lengths, and the pore spacing was nearly maintained. XRD showed only TiO 2 anatase reflections. The synthetic paradigms demonstrated for the silica to anatase conversion may be transferable to other 2D or 3D material shapes within the applicable range of feature sizes.
Source: openalex_inverted_index · Quality: baseline

Research context

OpenAlex topics: Photonic Crystals and Applications · Mesoporous Materials and Catalysis · Aerogels and thermal insulation

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

Affiliations

Department of Chemistry, University of Minnesota, 207 Pleasant Street SE, Minneapolis, Minnesota 55455

References (37)

Show source-provided references
1. Iler R. K. · 1979
2. Brinker C. J. · 1990
3. Wright J. D. · 2001
4. Harker R. I. · Science · 1971 · 173 · 23710.1126/science.173.3993.235 ↗
5. Sandhage K. H. · Adv. Mater. · 2002 · 14 · 43310.1002/1521-4095(20020318)14:6<429::AID-ADMA429>3.0.CO;2-C ↗
6. Martin T. · Angew. Chem., Int. Ed. · 2002 · 41 · 2592
7. Sanchez-Valente J. · Langmuir · 2003 · 19 · 358810.1021/la020423+ ↗
8. Golden D. C. · Geoderma · 1988 · 42 · 21110.1016/0016-7061(88)90001-8 ↗
9. Sipple E. · Solid State Ionics · 2001 · 141 · 461
10. Bamberger C. E. · J. Mater. Sci. Lett. · 1996 · 15 · 165
11. Lee J. S. · J. Catal. · 1988 · 112 · 53
12. Bamberger C. E. · J. Cryst. Growth · 1993 · 126 · 52910.1016/0022-0248(93)90801-3 ↗
13. Bamberger C. E. · J. Mater. Sci. Lett. · 1994 · 13 · 174510.1007/BF00776343 ↗
14. Tan B. J. · Chem. Mater. · 1994 · 6 · 926
15. Breslin M. C. · Mater. Sci. Eng., A · 1995 · 195 · 11910.1016/0921-5093(94)06510-1 ↗
16. Torardi C. C. · J. Solid State Chem. · 1995 · 119 · 35810.1016/0022-4596(95)80052-Q ↗
17. Ewsuk K. G. · J. Am. Ceram. Soc. · 1996 · 79 · 2499
18. Duvauchelle N. · J. Solid State Chem. · 1998 · 137 · 32410.1006/jssc.1997.7745 ↗
19. Kumar P. · J. Mater. Sci. · 1999 · 34 · 5769
20. Rogers K. A. · J. Am. Ceram. Soc. · 1999 · 82 · 76010.1111/j.1151-2916.1999.tb01829.x ↗
21. Wagner F. · J. Eur. Ceram. Soc. · 1999 · 19 · 245310.1016/S0955-2219(99)00133-8 ↗
22. Schulmeyer W. V. · Int. J. Refract. Met. Hard Mater. · 2002 · 20 · 26910.1016/S0263-4368(02)00029-X ↗
23. Velev O. D. · Nature · 1997 · 389 · 44810.1038/38921 ↗
24. Velev O. D. · Chem. Mater. · 1998 · 10 · 360210.1021/cm980444i ↗
25. Holland B. T. · Chem. Mater. · 1999 · 11 · 80510.1021/cm980666g ↗
26. Stein A. · Curr. Opin. Solid State Mater. Sci. · 2001 · 5 · 56410.1016/S1359-0286(01)00022-5 ↗
27. Dong · Adv. Mater. · 2002 · 14 · 151010.1002/1521-4095(20021016)14:20<1510::AID-ADMA1510>3.0.CO;2-W ↗
28. Barin I. · 1989
29. Schroden R. C. · J. Mater. Chem. · 2002 · 12 · 332710.1039/B204065B ↗
30. Stöber W. · J. Colloid Interface Sci. · 1968 · 26 · 6910.1016/0021-9797(68)90272-5 ↗
31. Schroden R. C. · Chem. Mater. · 2002 · 14 · 331510.1021/cm020100z ↗
32. Machin J. S. · Nature · 1961 · 189 · 22410.1038/189223b0 ↗
33. Holland B. T. · Science · 1998 · 281 · 54010.1126/science.281.5376.538 ↗
34. Stein A. · Microporous Mesoporous Mater. · 2001 · 44 · 239
35. Unocic R. R. · Chem. Commun. · 2004 · 796 · 797
36. Yagi, S.; Kunii, D.Fifth Symposium on Combustion; Combustion Institute: Pittsburgh, PA, 1955; pp 231−244.10.1016/S0082-0784(55)80033-1 ↗
37. Park J. Y. · Chem. Eng. Sci. · 1975 · 30 · 1214