Predicting the Q-Phase in Al-Cu-Mg-Si Alloys
Source abstract
Abstract
The objective of this work was to predict whether or not Al5Cu2Mg8Si6, the Q-phase, can be dissolved by solutionizing depending on the composition of Al-Cu-Mg-Si alloys. The procedure was to predict a series of isopleths at 505 °C using ThermoCalc software with a newly constructed database. Then zero-phase-fraction lines for the Q-phase on the isopleths were projected onto various planes to form isothermal, polyisopleth projections that show the effect of Si, Mg, and Cu on Q-phase stability.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Aluminum Alloy Microstructure Properties · Aluminum Alloys Composites Properties · Microstructure and mechanical properties
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (16)
Show source-provided references
1. G. Phragmen, The Phases Occurring in Alloys of Aluminum with Copper, Magnesium, Manganese, Iron, and Silicon, J. Inst. Met., 1950, 77, p 489-552
2. F.H. Samuel, Incipient Melting of Al5Mg8Si6Cu2 and Al2Cu Intermetallics in Unmodified and Strontium-Modified Al-Si-Cu-Mg (319) Alloys During Solution Heat Treatment, J. Mater. Sci., 1998, 33(9), p 2283-229710.1023/A:1004383203476 ↗
3. L. Backerud, G. Chai, and J. Tamminen, Solidification Characteristics of Aluminum Alloys, AFS/Skanaluminium, 1990, 2, p 85-101
4. I. Ansara, A.T. Dinsdale, and M.H. Rand, COST507—Thermochemical Database for Light Metal Alloys, Vol. 2, European Commission EUR 18499 EN, Luxembourg, 1998
5. X.M. Pan, C. Lin, J.E. Morral, and H.D. Brody, An Assessment of Thermodynamic Data for the Liquid Phase in the Al-Rich Corner of the Al-Cu-Si System and Its Application to the Solidification of a 319 Alloy, J. Phase Equilib. Diffus., 2005, 26(3), p 225-23310.1007/s11669-005-0109-1 ↗
6. X.-Y. Yan and Y.A. Chang, A Thermodynamic Analysis of the Cu-Si System, J. Alloys Compd., 2000, 308, p 221-22910.1016/S0925-8388(00)00983-X ↗
7. Y.M. Muggianu, M. Gambino, and J.P. Bros, Enthalpies of Formation of Liquid Alloy Bismuth-Galliumtin at 723 K. Choice of an Analytical Representation of Integral and Partial Excess Functions of Mixing, J. Chem. Phys., 1975, 72, p 82-88
8. B. Sundman, B. Jansson, and J.O. Andersson, Thermo-Calc Databank System, CALPHAD, 1985, 9(2), p 15310.1016/0364-5916(85)90021-5 ↗
9. D.J. Chakrabarti and J.L. Murray, Eutectic Melting in Al-Cu-Mg-Si Alloys, Mater. Sci. Forum, 1996, 217-222(Pt 1), p 177-18210.4028/www.scientific.net/MSF.217-222.177 ↗
10. D.A. Petrov and N.D. Nagorskaya, Constitution Diagram of the Aluminum-Copper-Magnesium-Silicon System, Zhurnal Obshchei Khimii, 1949, 19(11), p 469-506
11. A. Schrader, Quaternary Alloys, Metall (Berlin, 1914-34), 1949, 3, p 110-115, 150-154
12. J. Lacaze, G. Lesoult, O. Relave, I. Ansara, and J. Riquet, Thermodynamics and Solidification of Aluminum-Copper-Magnesium-Silicon Alloys, Z. Metallkd., 1987, 78(2), p 141-150
13. D.P. Simth, The Constitution of Quaternary Aluminium-Copper-Magnesium-Silicon Alloys at 500°C, Metallurgia, 1961, 63, p 223-230
14. J.E. Morral and H. Gupta, Phase Boundary, ZPF, and Topological Lines on Phase Diagrams, Scr. Metall. Mater., 1991, 25, p 1393-139610.1016/0956-716X(91)90420-6 ↗
15. J.E. Morral, Two-Dimensional Phase Fraction Charts, Scr. Metall., 1984, 18, p 407-41010.1016/0036-9748(84)90463-0 ↗
16. H. Gupta, J.E. Morral, and H. Norotny, Constructing Multicomponent Phase Diagrams by Overlapping ZPF Lines, Scr. Metall., 1986, 20, p 889-89410.1016/0036-9748(86)90461-8 ↗