Universal and Solution-Processable Precursor to Bismuth Chalcogenide Thermoelectrics
Source abstract
Abstract
We describe a universal precursor to compounds of the form Bi2Te3−xSex. This precursor can be dispensed using traditional solution-processing techniques and then thermally decomposed into its respective parent compound. Room temperature measurements of these materials yield thermoelectric figures of merit, ZT, ranging from 0.2 to 0.4.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Advanced Thermoelectric Materials and Devices · Phase-change materials and chalcogenides · Thermal properties of materials
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Materials Sciences Division, Lawrence Berkeley National Laboratory, Berkeley, California 94720
Department of Mechanical Engineering
Department of Chemical Engineering
References (31)
Show source-provided references
1. Bell L. E. · Science · 2008 · 321 · 145710.1126/science.1158899 ↗
2. Boukai A. I. · Nature · 2008 · 451 · 16810.1038/nature06458 ↗
3. Harman T. C. · Science · 2002 · 297 · 222910.1126/science.1072886 ↗
4. Heremans J. P. · Science · 2008 · 321 · 55410.1126/science.1159725 ↗
5. Hochbaum A. I. · Nature · 2008 · 451 · 16310.1038/nature06381 ↗
6. Hsu K. F. · Science · 2004 · 303 · 81810.1126/science.1092963 ↗
7. Poudel B. · Science · 2008 · 320 · 63410.1126/science.1156446 ↗
8. Venkatasubramanian R. · Nature · 2001 · 413 · 59710.1038/35098012 ↗
9. Wang R. Y. · Nano Lett. · 2008 · 8 · 228310.1021/nl8009704 ↗
10. Zimmer A. · J. Phys. Chem. Solids · 2007 · 68 · 190210.1016/j.jpcs.2007.05.021 ↗
11. Kutasov V. A. · 2006
12. Scherrer H. · 2006
13. Snyder G. J. · Nat. Mater. · 2008 · 7 · 10510.1038/nmat2090 ↗
14. Forrest S. R. · Nature · 2004 · 428 · 91110.1038/nature02498 ↗
15. Jayachandran M. · Mater. Chem. Phys. · 1993 · 34 · 110.1016/0254-0584(93)90112-Y ↗
16. Mitzi D. B. · Nature · 2004 · 428 · 29910.1038/nature02389 ↗
17. Mitzi D. B. · Adv. Mater. · 2009 · 21 · 314110.1002/adma.200802027 ↗
18. Milliron D. J. · Nat. Mater. · 2007 · 6 · 35210.1038/nmat1887 ↗
19. Milliron D. J. · Chem. Mater. · 2006 · 18 · 58710.1021/cm052300r ↗
20. Mitzi D. B. · Adv. Mater. · 2006 · 18 · 244810.1002/adma.200600157 ↗
21. Borca-Tasciuc T. · Rev. Sci. Instrum. · 2001 · 72 · 213910.1063/1.1353189 ↗
22. Cahill D. G. · Rev. Sci. Instrum. · 1990 · 61 · 80210.1063/1.1141498 ↗
23. Fuschillo N. · J. Phys. Chem. Solids · 1959 · 8 · 43010.1016/0022-3697(59)90382-8 ↗
24. Mills A. F. · 1999
25. Satterthwaite C. B. · Phys. Rev. · 1957 · 108 · 116410.1103/PhysRev.108.1164 ↗
26. Kurabayashi K. · J. Microelectromech. Syst. · 1999 · 810.1109/84.767114 ↗
27. Zeng G. H. · J. Appl. Phys. · 2007 · 101
28. Fleurial J. P. · J. Phys. Chem. Solids · 1988 · 49 · 123710.1016/0022-3697(88)90182-5 ↗
29. Kaibe H. · J. Phys. Chem. Solids · 1989 · 50 · 94510.1016/0022-3697(89)90045-0 ↗
30. Kovalenko M. V. · Science · 2009 · 324 · 141710.1126/science.1170524 ↗
31. Tangirala R. · Angew. Chem., Int. Ed. · 2010