Thermally Enhancing the Surface Areas of Yamamoto-Derived Porous Organic Polymers
Source abstract
Abstract
Thermal treatment of highly stable porous organic polymers based upon the Yamamoto polymerization of 2,2′,7,7′-tetrabromo-9,9′-spirobifluorene was done. The polymers are shown to be thermally and chemically stable. Upon thermal treatment the polymers are shown to have BET surface areas of ca. 2,000 m 2 /g and 2,500 m 2 /g respectively.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Covalent Organic Framework Applications · Metal-Organic Frameworks: Synthesis and Applications · Membrane Separation and Gas Transport
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Department of Chemistry, Northwestern University, 2145 Sheridan Road, Evanston, Illinois 60208, United States
Micromeritics Instrument Corporation, One Micromeritics Drive, Norcross, Georgia 30093, United States
References (31)
Show source-provided references
1. Lee J. · Chem. Soc. Rev. · 2009 · 38 · 145010.1039/b807080f ↗
2. Kaur P. · ACS Catal. · 2011 · 1 · 81910.1021/cs200131g ↗
3. Ma L. · Chem. Soc. Rev. · 2009 · 38 · 124810.1039/b807083k ↗
4. Murray L. J. · Chem. Soc. Rev. · 2009 · 38 · 129410.1039/b802256a ↗
5. Hu Y. H. · Adv. Mater. · 2010 · 22 · E11710.1002/adma.200902096 ↗
6. Li J.-R. · Chem. Soc. Rev. · 2009 · 38 · 147710.1039/b802426j ↗
7. An J. · J. Am. Chem. Soc. · 2010 · 132 · 3810.1021/ja909169x ↗
8. Bae Y.-S. · J. Mater. Chem. · 2009 · 19 · 213110.1039/b900390h ↗
9. Britt D. · Proc. Natl. Acad. Sci. U. S. A. · 2009 · 106 · 2063710.1073/pnas.0909718106 ↗
10. Weitkamp J. · Int. J. Hydrogen Energy · 1995 · 20 · 96710.1016/0360-3199(95)00058-L ↗
11. Tranchemontagne D. J. · Chem. Soc. Rev. · 2009 · 38 · 125710.1039/b817735j ↗
12. Cote A. P. · Science · 2005 · 310 · 116610.1126/science.1120411 ↗
13. Hunt J. R. · J. Am. Chem. Soc. · 2008 · 130 · 1187210.1021/ja805064f ↗
14. Dawson R. · Prog. Polym. Sci. · 2012 · 37 · 53010.1016/j.progpolymsci.2011.09.002 ↗
15. McKeown N. B. · Macromolecules · 2010 · 43 · 516310.1021/ma1006396 ↗
16. Farha O. K. · Chem. Mater. · 2009 · 21 · 303310.1021/cm901280w ↗
17. Farha O. K. · Chem. Commun. · 2010 · 46 · 105610.1039/b922554d ↗
18. Dawson R. · Energy Environ. Sci. · 2011 · 4 · 423910.1039/c1ee01971f ↗
19. Kassab R. M. · Res. Chem. Intermed. · 2011 · 37 · 74710.1007/s11164-011-0321-z ↗
20. Saha D. · J. Phys. Chem. Lett. · 2009 · 1 · 7310.1021/jz900028u ↗
21. Zhou W. · Chem. Phys. Lett. · 2010 · 499 · 10310.1016/j.cplett.2010.09.032 ↗
22. Weber J. · Langmuir · 2010 · 26 · 1565010.1021/la1028806 ↗
23. Xie L.-H. · Curr. Org. Chem · 2010 · 14 · 216910.2174/138527210793351599 ↗
24. Schmidt J. · Macromolecules · 2009 · 42 · 442610.1021/ma9005473 ↗
25. Ben T. · Angew. Chem., Int. Ed. · 2009 · 48 · 945710.1002/anie.200904637 ↗
26. Yuan D. · Adv. Mater. · 2011 · 23 · 372310.1002/adma.201101759 ↗
27. Walton K. S. · J. Am. Chem. Soc. · 2007 · 129 · 855210.1021/ja071174k ↗
28. Weber J. · Macromolecules · 2008 · 41 · 288010.1021/ma702495r ↗
29. Schmidt J. · Adv. Mater. · 2009 · 21 · 70210.1002/adma.200802692 ↗
30. Yuan S. · Macromolecules · 2009 · 42 · 155410.1021/ma802394x ↗
31. Dawson R. · Macromolecules · 2010 · 43 · 852410.1021/ma101541h ↗