New 4V-Class and Zero-Strain Cathode Material for Na-Ion Batteries

Here, we introduce Na 3 V(PO 3 ) 3 N as a novel 4V-class and zero-strain cathode material for Na-ion batteries. Structural analysis based on a combination of neutron and X-ray diffraction (XRD) reveals that the Na 3 V(PO 3 ) 3 N crystal contains three-dimensional channels that are suitable for facile Na diffusion. The Na (de)intercalation is observed to occur at ∼4 V vs Na/Na + in the Na cell via the V 3+ /V 4+ redox reaction with ∼67% retention of the initial capacity after over 3000 cycles. The remarkable cycle stability is attributed to the near-zero volume change (∼0.24%) and unique centrosymmetric distortion that occurs during a cycle despite the large ionic size of Na ions for (de)intercalation, as demonstrated by ex situ XRD analysis and first-principles calculations. We also demonstrate that the Na 3 V(PO 3 ) 3 N electrode can display outstanding power capability with ∼84% of the theoretical capacity retained at 10C, even though the particle sizes are on the micrometer scale (>5 μm), which is attributed to its intrinsic three-dimensional open-crystal framework. The combination of this high power capability and extraordinary cycle stability makes Na 3 V(PO 3 ) 3 N a new potential cathode material for Na-ion batteries.