Flexible Aerogels from Hyperbranched Polyurethanes: Probing the Role of Molecular Rigidity with Poly(Urethane Acrylates) Versus Poly(Urethane Norbornenes)
Source abstract
Abstract
Flexible and foldable aerogels have commercial value for applications in thermal insulation. This study investigates the molecular connection of macroscopic flexibility using polymeric aerogels based on star-shaped polyurethane-acrylate versus urethane-norbornene monomers. The core of those monomers is based either on a rigid/aromatic, or a flexible/aliphatic triisocyanate. Terminal acrylates or norbornenes at the tips of the star branches were polymerized with free radical chemistry, or with ROMP, respectively. At the molecular level, aerogels were characterized with FTIR and solid-state 13 C NMR. The porous network was probed with N 2 -sorption and Hg-intrusion porosimetry, SEM and SAXS. The interparticle connectivity was assessed in a top-down fashion with thermal conductivity measurements and compression testing. All aerogels of this study consist of aggregates of nanoparticles, whose size depends on the aliphatic/aromatic content of the monomer, the rigidity/flexibility of the polymeric backbone, and generally varies with density. At higher densities (0.3–0.7 g cm –3 ), all materials were stiff, strong, and tough. Aerogels based on urethane-acrylates built around a rigid/aromatic core exhibited a rapid decrease of their elastic modulus with density (slopes of the log–log plots >5.0), and at about 0.14 g cm –3, they were foldable. Data support that molecular properties of the monomer affect macroscopic flexibility indirectly, not so through the particle size, but rather through the growth mechanism and consequently through the interparticle contact area. Thus, flexible aerogels of this study showed no indication for polymer accumulation onto the primary nanostructure (particle sizes via N 2 -sorption and SAXS were comparable), and their interparticle contact area was comparatively lower. Because for flexibility purposes, interparticle contact area is related to interparticle bonding, it is speculated that if the latter is controlled properly (e.g., through adjustment of the monomer functional group density) it might lead to superelasticity and shape-memory effects.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Aerogels and thermal insulation · Surface Modification and Superhydrophobicity · Advanced Sensor and Energy Harvesting Materials
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Department of Chemistry, Missouri University of Science and Technology, Rolla, Missouri 65409, United States
Funding
Army Research Office · BASF Corporation
References (92)
Show source-provided references
1. Pierre A. C. · Chem. Rev. · 2002 · 102 · 424310.1021/cr0101306 ↗
2. Begag R. · Thermal Cond. · 2008 · 29 · 323
3. Coffman B. E. · AIP Conf. Proc. · 2010 · 55 · 91310.1063/1.3422458 ↗
4. Koebel M. · J. Sol-Gel Sci. Technol. · 2012 · 63 · 31510.1007/s10971-012-2792-9 ↗
5. Jelle B. J. · Energy Buildings · 2011 · 43 · 254910.1016/j.enbuild.2011.05.015 ↗
6. Gronauer M. · Acta Acust. Acust. · 1986 · 59 · 177
7. Gerlach R. · J. Non-Cryst. Solids · 1992 · 145 · 22710.1016/S0022-3093(05)80461-2 ↗
8. Gibiat V. · J. Non-Cryst. Solids · 1995 · 186 · 24410.1016/0022-3093(95)00049-6 ↗
9. Morris C. A. · Science · 1999 · 284 · 62210.1126/science.284.5414.622 ↗
10. Hüsing N. · Angew. Chem., Int. Ed. Engl. · 1998 · 37 · 2210.1002/(SICI)1521-3773(19980202)37:1/2<22::AID-ANIE22>3.0.CO;2-I ↗
11. Kistler S. S. · J. Phys. Chem. · 1932 · 36 · 5210.1021/j150331a003 ↗
12. Tsou P. · J. Non-Cryst. Solids · 1995 · 186 · 41510.1016/0022-3093(95)00065-8 ↗
13. Randall J. P. · ACS Appl. Mater. Interfaces · 2011 · 3 · 61310.1021/am200007n ↗
14. Alexa L. C. · Nucl. Instrum. Methods Phys. Res., Sect. A · 1995 · 365 · 29910.1016/0168-9002(95)00515-3 ↗
15. Cantin M. · Nucl. Instrum. Methods · 1974 · 118 · 17710.1016/0029-554X(74)90700-9 ↗
16. daCunha J. P. · Nucl. Instrum. Methods Phys. Res., Sect. A · 2000 · 452 · 40110.1016/S0168-9002(00)00452-6 ↗
17. Schneider M. · Catal. Rev. · 1995 · 37 · 51510.1080/01614949508006450 ↗
18. Vallet-Regi M. · J. Mater. Chem. · 2006 · 16 · 2610.1039/B509744D ↗
19. Bang A. · ACS Appl. Mater. Interfaces · 2014 · 6 · 489110.1021/am4059217 ↗
20. Leventis N. · Nano Lett. · 2002 · 2 · 95710.1021/nl025690e ↗
21. Leventis N. · Acc. Chem. Res. · 2007 · 40 · 87410.1021/ar600033s ↗
22. Mulik S. · Chem. Mater. · 2008 · 20 · 503510.1021/cm800963h ↗
23. Mohite D. P. · Chem. Mater. · 2012 · 24 · 343410.1021/cm3017648 ↗
24. Leventis N. · J. Mater. Chem. · 2007 · 17 · 150210.1039/B612625A ↗
25. Leventis N. · Chem. Mater. · 2010 · 22 · 279010.1021/cm903662a ↗
26. Leventis N. · 2011 · 276
27. Leventis N. · Chem. Mater. · 2010 · 22 · 669210.1021/cm102891d ↗
28. Leventis N. · ACS Appl. Mater. Interfaces · 2014 · 6 · 687210.1021/am500685k ↗
29. Lee J. K. · J. Sol-Gel Sci. Technol. · 2009 · 49 · 20910.1007/s10971-008-1861-6 ↗
30. Chidambareswarapattar C. · RSC Adv. · 2013 · 3 · 2645910.1039/c3ra43717e ↗
31. Leventis N. · Chem. Mater. · 2011 · 23 · 225010.1021/cm200323e ↗
32. Chidambareswarapattar C. · J. Mater. Chem. · 2010 · 20 · 966610.1039/c0jm01844a ↗
33. Rhine, W.; Wang, J.; Begag, R.Polyimide Aerogels, Carbon Aerogels, and Metal Carbide Aerogels and Methods of Making Same. U.S. Patent No. 7,074,880, 2006.
34. Kawagishi K. · Macromol. Rapid Commun. · 2007 · 28 · 9610.1002/marc.200600587 ↗
35. Meador M. A. B. · Polym. Prepr. (Am. Chem. Soc. Div. Polym. Chem.) · 2010 · 51 · 265
36. Lorjai P. · J. Sol-Gel Sci. Technol. · 2009 · 52 · 5610.1007/s10971-009-1992-4 ↗
37. Mahadik-Khanolkar S. · Chem. Mater. · 2014 · 26 · 130310.1021/cm403483p ↗
38. Leventis N. · J. Mater. Chem. · 2011 · 21 · 1198110.1039/c1jm11472g ↗
39. Sadekar A. G. · Chem. Mater. · 2012 · 24 · 2610.1021/cm202975p ↗
40. Lee J. K. · J. Sol-Gel Sci. Technol. · 2007 · 44 · 2910.1007/s10971-007-1598-7 ↗
41. Mohite D. P. · Soft Matter · 2013 · 9 · 151610.1039/C2SM26931G ↗
42. Mohite D. P. · Soft Matter · 2013 · 9 · 153110.1039/C2SM27606B ↗
43. Biesmans G. · J. Non-Cryst. Solids · 1998 · 225 · 6410.1016/S0022-3093(98)00010-6 ↗
44. http://www.aerogel.com/markets/subsea.html(accessed August 16, 2014) .
45. Mendenhall R. · 2011 · 865
46. Meador M. A. B. · ACS Appl. Mater. Interfaces · 2012 · 4 · 53610.1021/am2014635 ↗
47. http://www.aerogel.com/(accessed August 16, 2014) .
48. http://www.cabot-corp.com/aerogel(accessed August 16, 2014) .
49. Nadargi D. Y. · Microporous Mesoporous Mater. · 2009 · 117 · 61710.1016/j.micromeso.2008.08.025 ↗
50. Rao A. V. · J. Colloid Interface Sci. · 2007 · 305 · 12410.1016/j.jcis.2006.09.025 ↗
51. Reynolds J. G. · J. Non-Cryst. Solids · 2001 · 292 · 12710.1016/S0022-3093(01)00882-1 ↗
52. Chen W. · Soft Matter · 2011 · 7 · 1036010.1039/c1sm06179h ↗
53. Hayase G. · ACS Appl. Mater. Interfaces · 2014 · 6 · 946610.1021/am501822y ↗
54. Sai H. · J. Mater. Chem. A · 2013 · 1 · 796310.1039/c3ta11198a ↗
55. Schwan M. · J. Mater. Chem. A · 2013 · 1 · 1346210.1039/c3ta13172f ↗
56. Chidambareswarapattar C. · Chem. Mater. · 2013 · 25 · 320510.1021/cm401623h ↗
57. Leventis N. · ACS Appl. Mater. Interfaces · 2014 · 6 · 687210.1021/am500685k ↗
58. Gao C. · Prog. Polym. Sci. · 2004 · 29 · 18310.1016/j.progpolymsci.2003.12.002 ↗
59. Ruzette A. V. · Nat. Mater. · 2005 · 4 · 1910.1038/nmat1295 ↗
60. Halperin A. · Macromolecules · 1990 · 23 · 272410.1021/ma00212a023 ↗
61. Zhang J. · Chem. Soc. Rev. · 2013 · 42 · 912710.1039/c3cs60192g ↗
62. Yates C. R. · Eur. Polym. J. · 2004 · 40 · 125710.1016/j.eurpolymj.2004.02.007 ↗
63. Burel F. · Thermochim. Acta · 1999 · 326 · 13310.1016/S0040-6031(98)00587-5 ↗
64. Wang C. · J. Appl. Polym. Sci. · 2011 · 122 · 244910.1002/app.34364 ↗
65. Chen X. · Polym. Adv. Technol. · 2008 · 19 · 32210.1002/pat.995 ↗
66. Noh S. M. · Prog. Org. Coat. · 2012 · 74 · 25710.1016/j.porgcoat.2012.01.002 ↗
67. Gang X. · Prog. Org. Coat. · 2005 · 52 · 11010.1016/j.porgcoat.2004.10.001 ↗
68. Oprea S. · J. Appl. Polym. Sci. · 2007 · 105 · 250910.1002/app.26534 ↗
69. House D. W. · 2000 · 489
70. Beaucage G. · J. Appl. Crystallogr. · 1995 · 28 · 71710.1107/S0021889895005292 ↗
71. Beaucage G. · J. Appl. Crystallogr. · 1996 · 29 · 13410.1107/S0021889895011605 ↗
72. Parker W. J. · J. Appl. Phys. · 1961 · 32 · 167910.1063/1.1728417 ↗
73. Lee D. · J. Non-Cryst. Solids · 1995 · 186 · 28510.1016/0022-3093(95)00055-0 ↗
74. Lu X. · Science · 1992 · 255 · 97110.1126/science.255.5047.971 ↗
75. Reichenauer G. · Colloids Surf., A · 2007 · 300 · 20410.1016/j.colsurfa.2007.01.020 ↗
76. Stephan K. · J. Phys. Chem. Ref. Data · 1985 · 14 · 22710.1063/1.555749 ↗
77. http://hyperphysics.phy-astr.gsu.edu/hbase/tables/thrcn.html(accessed August 12, 2014).
78. Katti A. · Chem. Mater. · 2006 · 18 · 28510.1021/cm0513841 ↗
79. Fricke J. · Int. J. Heat Mass Transfer · 1992 · 35 · 230510.1016/0017-9310(92)90073-2 ↗
80. Lu X. · J. Non-Cryst. Solids · 1995 · 188 · 22610.1016/0022-3093(95)00191-3 ↗
81. American Society for Metals. ASM Engineering Materials Handbook, Composites, Vol.1;ASM International:Materials Park, OH, 1998; p178, Table 2.
82. Luo H. · Int. J. Appl. Ceram. Technol. · 2004 · 1 · 25410.1111/j.1744-7402.2004.tb00177.x ↗
83. Luo H. · J. Am. Ceram. Soc. · 2006 · 89 · 26610.1111/j.1551-2916.2005.00688.x ↗
84. Fricke J. · J. Non-Cryst. Solids · 1988 · 100 · 16910.1016/0022-3093(88)90014-2 ↗
85. Gross J. · Nanostructured Mater. · 1995 · 6 · 90510.1016/0965-9773(95)00206-5 ↗
86. Leventis N. · J. Mater. Chem. · 2008 · 18 · 247510.1039/b801770k ↗
87. Luo H. · J. Sol Gel Sci. Technol. · 2008 · 48 · 11310.1007/s10971-008-1788-y ↗
88. Rajamanickam R. · Chem. Mater. · 2014 · 26 · 516110.1021/cm502643a ↗
89. Pavia, D. L.; Lampman, G. M.; Kriz, G. S.; Engel, R. G.A Small Scale Approach to Organic Laboratory Techniques3rd ed.Brooks Cole:Independence, KY, 2010; pp405–409.
90. Ilavsky J. · J. Appl. Crystallogr. · 2009 · 42 · 34710.1107/S0021889809002222 ↗
91. Cowan R. D. · J. Appl. Phys. · 1961 · 32 · 136310.1063/1.1736235 ↗
92. Cowan R. D. · J. Appl. Phys. · 1963 · 34 · 92610.1063/1.1729564 ↗