Synthesis of Li[(Ni_0.5Mn_0.5)_1-xLi_x]O₂ by Emulsion Drying Method and Impact of Excess Li on Structural and Electrochemical Properties

Layered Li[Ni 0.5 Mn 0.5 ]O 2 ( R 3̄ m space group) was synthesized with controlling the Li/(Ni + Mn) ratio by employing an emulsion drying method, and the effect of Li on the transition-metal layer was investigated. Structural analyses of the final products were done by X-ray diffraction, neutron diffraction, and X-ray absorption near-edge spectroscopy. From the structural studies, we found that an excess amount of Li is located at the transition-metal layer and the presence of Li in the transition metal significantly improved structural ordering in the crystal structure. High capacity with good cyclability, faster Li + chemical diffusivity, less changes in the host structure by Li + de-/intercalation, and higher thermal stability were achieved for the Li-excess Li[(Ni 0.5 Mn 0.5 ) 0.94 Li 0.06 ]O 2 compound relative to Li[Ni 0.5 Mn 0.5 ]O 2 . It is believed that such enhanced electrochemical properties are related to the improved physical and structural properties of Li-excess Li[(Ni 0.5 Mn 0.5 ) 0.94 Li 0.06 ]O 2 .