Mesoporous Melamine Resins by Soft Templating of Block-co-Polymer Mesophases
Source abstract
Abstract
Mesoporous melamine resins have been prepared using hexamethoxymethyl melamine (HMMM) as monomer and block-co-polymer Pluronic F127 as template. At acidic conditions, HMMM condenses into melamine resins, replicating the mesophases formed by the block-co-polymer template. The template can be removed by solvent extraction, yielding mesoporous melamine resins with surface areas of up to 258 m 2 /g and pore diameters of 7.8 nm. At a HMMM/F127 weight ratio of 1:1 an ordered mesoporous melamine resin is observed exhibiting a 2d hexagonal arrangement of cylindrical pores. The simplicity of the synthesis of these mesoporous films allows the large scale production of the materials, for example, in the form of free-standing films.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Metal-Organic Frameworks: Synthesis and Applications · Covalent Organic Framework Applications · Mesoporous Materials and Catalysis
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Technische Universität Berlin, Englische Strasse 20, 10587 Berlin
Department of Chemical and Biomolecular Engineering, KAIST, Daejeon 305-701 (Korea)
References (61)
Show source-provided references
1. Svec F. · Small · 2009 · 5 · 109810.1002/smll.200801762 ↗
2. Thomas A. · Macromol. Rapid Commun. · 2009 · 30 · 22110.1002/marc.200800642 ↗
3. Wan Y. · Chem. Mater. · 2008 · 20 · 93210.1021/cm7024125 ↗
4. Budd P. M. · Chem. Commun. · 2004 · 23010.1039/b311764b ↗
5. Cooper A. I. · Adv. Mater. · 2009 · 21 · 129110.1002/adma.200801971 ↗
6. Farha O. K. · Chem. Mater. · 2009 · 21 · 303310.1021/cm901280w ↗
7. Jiang J. X. · Angew. Chem., Int. Ed. · 2007 · 46 · 857410.1002/anie.200701595 ↗
8. Kuhn P. · Angew. Chem., Int. Ed. · 2008 · 47 · 345010.1002/anie.200705710 ↗
9. Maly K. E. · J. Mater. Chem. · 2009 · 19 · 178110.1039/b816089a ↗
10. McKeown N. B. · Chem.—Eur. J. · 2005 · 11 · 261010.1002/chem.200400860 ↗
11. Schmidt J. · Adv. Mater. · 2009 · 21 · 70210.1002/adma.200802692 ↗
12. Schmidt J. · Macromolecules · 2009 · 42 · 442610.1021/ma9005473 ↗
13. Schwab M. G. · J. Am. Chem. Soc. · 2009 · 131 · 721610.1021/ja902116f ↗
14. Weber J. · Macromolecules · 2008 · 41 · 288010.1021/ma702495r ↗
15. Weber J. · Macromol. Rapid Commun. · 2007 · 28 · 187110.1002/marc.200700346 ↗
16. Weber J. · J. Am. Chem. Soc. · 2008 · 130 · 633410.1021/ja801691x ↗
17. Hentze H. P. · Curr. Opin. Solid State Mater. Sci. · 2001 · 5 · 34310.1016/S1359-0286(01)00008-0 ↗
18. Thomas A. · Chem. Mater. · 2008 · 20 · 73810.1021/cm702126j ↗
19. Wan Y. · Chem. Rev. · 2007 · 107 · 282110.1021/cr068020s ↗
20. Hamley I. W. · Nanotechnology · 2003 · 14 · R3910.1088/0957-4484/14/10/201 ↗
21. Soler-Illia G. · Curr. Opin. Colloid Interface Sci. · 2003 · 8 · 10910.1016/S1359-0294(03)00002-5 ↗
22. Ryoo R. · Adv. Mater. · 2001 · 13 · 67710.1002/1521-4095(200105)13:9<677::AID-ADMA677>3.0.CO;2-C ↗
23. Zhu X. X. · Macromolecules · 1997 · 30 · 303110.1021/ma961580g ↗
24. Jang J. · Chem. Commun. · 2005 · 120010.1039/b416518g ↗
25. Meng Y. · Angew. Chem., Int. Ed. · 2005 · 44 · 705310.1002/anie.200501561 ↗
26. Zhang F. Q. · J. Am. Chem. Soc. · 2005 · 127 · 1350810.1021/ja0545721 ↗
27. Kosonen H. · Adv. Mater. · 2006 · 18 · 20110.1002/adma.200401110 ↗
28. Valkama S. · Adv. Funct. Mater. · 2007 · 17 · 18310.1002/adfm.200600604 ↗
29. Deng Y. · J. Mater. Chem. · 2008 · 18 · 9110.1039/B713310C ↗
30. Deng Y. H. · Chem. Mater. · 2008 · 20 · 728110.1021/cm802413q ↗
31. Liu H. J. · J. Mater. Chem. · 2009 · 19 · 366110.1039/b819820a ↗
32. Liu R. L. · J. Am. Chem. Soc. · 2006 · 128 · 1165210.1021/ja0633518 ↗
33. Zhai Y. P. · J. Mater. Chem. · 2009 · 19 · 329210.1039/b821945a ↗
34. Su D. S. · ChemSusChem · 2009
35. Goettmann F. · Angew. Chem., Int. Ed. · 2007 · 46 · 271710.1002/anie.200603478 ↗
36. Cheng S. F. · 2008 · 681
37. Weber J. · Adv. Mater. · 2008 · 20 · 259510.1002/adma.200703159 ↗
38. Srivastava R. · Microporous Mesoporous Mater. · 2006 · 90 · 31410.1016/j.micromeso.2005.10.043 ↗
39. Zelenak V. · Microporous Mesoporous Mater. · 2008 · 116 · 35810.1016/j.micromeso.2008.04.023 ↗
40. Zelenak V. · Chem. Eng. J. · 2008 · 144 · 33610.1016/j.cej.2008.07.025 ↗
41. Kim S. N. · Microporous Mesoporous Mater. · 2008 · 115 · 49710.1016/j.micromeso.2008.02.025 ↗
42. Pevida C. · Carbon · 2008 · 46 · 146410.1016/j.carbon.2008.06.026 ↗
43. Fischer A. · ACS Nano · 2008 · 2 · 248910.1021/nn800503a ↗
44. Fischer A. · Chem. Mater. · 2008 · 20 · 738310.1021/cm802127t ↗
45. Fischer A. · Adv. Mater. · 2007 · 19 · 26410.1002/adma.200602151 ↗
46. Jun, Y. S.; Hong, W. H.; Antonietti, M.; Thomas, A.Adv. Mater. 2009, 21, 4270.10.1002/adma.200803500 ↗
47. Odian, G.,Principles of Polymerization;John Wiley & Sons:New York, 1991; p132.
48. von Hohenesche C. D. · Chem. Mater. · 2008 · 20 · 612410.1021/cm8015319 ↗
49. Egger C. C. · 2007 · 86
50. Dong Y. R. · Carbon · 2009 · 47 · 213810.1016/j.carbon.2009.04.011 ↗
51. Jones F. N. · 1993 · 189
52. Snyder D. M. · J. Appl. Polym. Sci. · 1992 · 46 · 130110.1002/app.1992.070460718 ↗
53. Robert S. · J. Appl. Polym. Sci. · 1964 · 8 · 47510.1002/app.1964.070080131 ↗
54. Mequanint K. · Polymer · 2003 · 44 · 263110.1016/S0032-3861(03)00154-X ↗
55. Rahman M. M. · Fiber. Polym. · 2009 · 10 · 610.1007/s12221-009-0006-z ↗
56. Subrayan R. P. · Chem. Mater. · 1998 · 10 · 350610.1021/cm980284a ↗
57. Weber B. · Prog. Org. Coat. · 2009 · 64 · 15010.1016/j.porgcoat.2008.08.032 ↗
58. Ratzsch M. · 2003 · 431
59. Subrayan R. P. · J. Appl. Polym. Sci. · 1996 · 62 · 123710.1002/(SICI)1097-4628(19961121)62:8<1237::AID-APP14>3.0.CO;2-4 ↗
60. Weber J. · Macromolecules · 2007 · 40 · 129910.1021/ma062598m ↗
61. Weber J. · Macromolecules · 2009 · 42 · 823410.1021/ma901322t ↗