Conversion of Colloidal ZnO−WO3 Heteroaggregates into Strongly Blue Luminescing ZnWO4 Xerogels and Films
Source abstract
Abstract
The colloidal synthesis of ZnO−WO 3 heteroaggregates composed of 3−5 nm particles is presented. These sols can be used to prepare nanocrystalline ZnWO 4 xerogels, powders, and thin films with strong blue fluorescence (quantum yield between 25 and 50% at room temperature). The conversion of the precursor aggregates into nano- and microcrystalline monoclinic ZnWO 4 Sanmartinite has been followed by XRD, DTA−TG−MS, SEM, FTIR, optical absorption, and fluorescence methods. The ZnWO 4 crystallites start to develop at 350 °C, and their mean crystal size increases with temperature to 35 nm at 400 °C and 120 nm at 600 °C. At the same time, the fluorescence intensity increases by 3 orders of magnitude within the aforementioned temperature regime, no matter whether X-rays or UV photons are used to excite the samples. In complementary time-resolved X-ray fluorescence investigations, two recombination processes in the micro- and millisecond range were detected. In weakly fluorescing ZnO−WO 3 aggregate samples at sizes between 10 and 30 nm, the slow millisecond process dominates the recombination of the charge carriers whereas in 50−275 nm crystals and above, the faster 2.5 μs process dominates the decay kinetics. Accordingly, the slow afterglow process is attributed to a recombination between electrons and holes deeply trapped at the surface of the heteroaggregates. The faster 2.5 μs recombination process takes place only in the perfectly developed Sanmartinite phase.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Luminescence Properties of Advanced Materials · Ga2O3 and related materials · Transition Metal Oxide Nanomaterials
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Bayerische Julius-Maximilians-Universität Würzburg, Lehrstuhl für Silicatchemie Röntgenring 10, D-97070 Würzburg, Germany
Siemens AG Corporate Technology, Otto-Hahn-Ring 6, D-81730 Munich, Germany
References (19)
Show source-provided references
1. Kröger F. A. · 194810.1063/1.3066188 ↗
2. Blasse G. · 199410.1007/978-3-642-79017-1 ↗
3. Grassmann H. · J. Lumin. · 1985 · 33 · 10910.1016/0022-2313(85)90034-1 ↗
4. Kolbe, W.; Petermann, K.; Huber, G.IEEE J.QuantumElectron.1985,QE-21, 1596.10.1109/JQE.1985.1072545 ↗
5. Pisarevskii Y. V. · Phys. Status Solidi A · 1988 · 107 · 16110.1002/pssa.2211070115 ↗
6. Rushbrooke J. G. · Nucl. Instrum. Methods Phys. Res. A · 1989 · 280 · 8310.1016/0168-9002(89)91274-6 ↗
7. Ovechkin A. E. · Phys. Status Solidi A · 1987 · 103 · 28510.1002/pssa.2211030133 ↗
8. Jander W. · Anorg. Allg. Chem. · 1941 · 246 · 6710.1002/zaac.19412460109 ↗
9. Lesne J. P. · Can. J. Spectrosc. · 1973 · 18 · 69
10. Greenwood, N. N.; Earnshaw, A.Chemie der Elemente; VCH-Verlag: Weinheim, 1990; p 1557.
11. (a) JCPDS 15-0774.
12. (b) Ibid. 36-1451.
13. (c) Ibid. 33-1387.
14. Sakohara S. · J. Phys. Chem. · 1992 · 96 · 1108610.1021/j100205a084 ↗
15. Gerischer H. · Top. Appl. Phys. · 1979 · 31 · 11510.1007/3-540-09224-2_4 ↗
16. Spanhel · J. Am. Chem. Soc. · 1991 · 113 · 282610.1021/ja00008a004 ↗
17. Bedja I. · J. Phys. Chem. · 1993 · 97 · 1106410.1021/j100144a027 ↗
18. Bahnemann D. · Solar Energy Materials · 1991 · 24 · 56410.1016/0165-1633(91)90091-X ↗
19. Kamat P. V. · Prog. Inorg. Chem. · 1997 · 44 · 273