From Core/Shell Structured FePt/Fe3O4/MgO to Ferromagnetic FePt Nanoparticles
Source abstract
Abstract
This paper reports an improved synthesis of hard magnetic fct-FePt nanoparticles (NPs) from reductive annealing of fcc-FePt/Fe 3 O 4 /MgO NPs followed by MgO removal. The fcc-FePt/Fe 3 O 4 NPs are made by a one-pot reaction of Pt(acac) 2 with Fe(CO) 5 in the presence of oleic acid and oleylamine and are coated with a layer of MgO via the thermal decomposition of Mg(acac) 2 . The MgO coating prevents FePt from sintering under high temperature reductive annealing conditions. The fct-FePt NPs obtained from the 650 °C annealing of the fcc-FePt/Fe 3 O 4 /MgO NPs show a coercivity value of 2 T at 300 K, suitable for various nanomagnetic applications.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Magnetic properties of thin films · Electromagnetic wave absorption materials · Copper Interconnects and Reliability
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Department of Chemistry, Brown University, Rhode Island 02912, and Department of Physics, University of Texas at Arlington, Arlington, Texas 76019
References (38)
Show source-provided references
1. Kneller E. F. · IEEE Trans. Magn. · 1991 · 27 · 358810.1109/20.102931 ↗
2. Skomski R. · Phys. Rev. B · 1993 · 48 · 1581210.1103/PhysRevB.48.15812 ↗
3. Zeng H. · Nature · 2002 · 420 · 39510.1038/nature01208 ↗
4. Weller D. · Annu. Rev. Mater. Sci. · 2000 · 30 · 61110.1146/annurev.matsci.30.1.611 ↗
5. Sun S. · Science · 2000 · 287 · 198910.1126/science.287.5460.1989 ↗
6. Moser A. · J. Phys. D: Appl. Phys · 2002 · 35 · R15710.1088/0022-3727/35/19/201 ↗
7. Pankhurst Q. A. · J. Phys. D: Appl. Phys. · 2003 · 36 · R167−R18110.1088/0022-3727/36/13/201 ↗
8. Sun S. · Adv. Mater. · 2006 · 18 · 39310.1002/adma.200501464 ↗
9. Gao J. · J. Am. Chem. Soc. · 2008 · 130 · 1182810.1021/ja803920b ↗
10. Ulmeanu M. · Phys. Rev. B · 2004 · 69 · 05441710.1103/PhysRevB.69.054417 ↗
11. Antoniak C. · Phys. Rev. Lett. · 2006 · 97 · 11720110.1103/PhysRevLett.97.117201 ↗
12. Dai Z. R. · Nano Lett. · 2001 · 1 · 44310.1021/nl0100421 ↗
13. Elkins K. E. · Nano Lett. · 2003 · 3 · 164710.1021/nl034734w ↗
14. Vedantam T. S. · J. Appl. Phys. · 2003 · 93 · 718410.1063/1.1558233 ↗
15. Yamamoto S. · Appl. Phys. Lett. · 2005 · 87 · 03250310.1063/1.1995959 ↗
16. Tamada Y. · Appl. Phys. Lett. · 2007 · 90 · 16250910.1063/1.2728760 ↗
17. Kim J. · Adv. Mater. · 2008
18. Li D. · J. Appl. Phys. · 2006 · 99 · 08E91110.1063/1.2166597 ↗
19. Rong C. · J. Appl. Phys. · 2008 · 103 · 07E13110.1063/1.2832506 ↗
20. Parkin S. S. P. · Nat. Mater. · 2004 · 3 · 86210.1038/nmat1256 ↗
21. Chen W. · J. Phys. Chem. C · 2007 · 111 · 1345210.1021/jp072385e ↗
22. Chen W. · Langmuir · 2007 · 23 · 1130310.1021/la7016648 ↗
23. Chen W. · J. Phys. Chem. C · 2008 · 112 · 389110.1021/jp7110204 ↗
24. Chen M · J. Am. Chem. Soc. · 2004 · 126 · 839410.1021/ja047648m ↗
25. Sun S. · J. Am. Chem. Soc. · 2002 · 124 · 820410.1021/ja026501x ↗
26. Zeng H. · J. Am. Chem. Soc. · 2004 · 126 · 1145810.1021/ja045911d ↗
27. See theSupporting Information.
28. Maeda T. · Appl. Phys. Lett. · 2002 · 80 · 214710.1063/1.1463213 ↗
29. Kai T. · J. Appl. Phys. · 2004 · 95 · 60910.1063/1.1635978 ↗
30. Sun X. · J. Appl. Phys. · 2003 · 93 · 733710.1063/1.1543863 ↗
31. Takahashi Y. K. · J. Magn. Magn. Mater. · 2002 · 246 · 25910.1016/S0304-8853(02)00065-3 ↗
32. Kang S. S. · J. Appl. Phys. · 2003 · 93 · 717810.1063/1.1543859 ↗
33. Kang S. S. · IEEE Trans. Magn. · 2003 · 39 · 275310.1109/TMAG.2003.815589 ↗
34. Jia Z. · IEEE Trans. Magn. · 2005 · 41 · 338510.1109/TMAG.2005.855210 ↗
35. Yan Q. · Adv. Mater. · 2005 · 17 · 223310.1002/adma.200500949 ↗
36. Harrell J. W. · Scr. Mater. · 2005 · 53 · 41110.1016/j.scriptamat.2005.04.033 ↗
37. Tomou A. · J. Appl. Phys. · 2007 · 102 · 02391010.1063/1.2752141 ↗
38. Gersten J. I. · 2001