Understanding Na Mobility in NASICON Materials: A Rietveld, 23Na and 31P MAS NMR, and Impedance Study
Source abstract
Abstract
The structures and electrical properties of four NASICON compositions, Na 1.4 M 1.6 In 0.4 (PO 4 ) 3 (M = Ti, Sn, Hf, Zr), have been determined and compared. Rietveld refinement of powder X-ray diffraction data confirmed the basic rhombohedral NASICON structure with random occupancy of the octahedral In/M sites, full occupancy of the Na(1) sites and partial occupancy of the Na(2) sites. For three compositions, M = Zr, Sn, and Hf, the 31 P MAS NMR peak intensities of the four detected signals, attributed to four different phosphorus environments [P(OM) 4 - n (OIn) n ( n = 0−3)], were close to the ratios expected for a random distribution of In/M. For M = Ti, some departures from statistical occupancy were apparent. 23 Na MAS NMR data gave evidence for two Na + positions at room temperature for M = Ti, Sn, attributable to occupation of Na(1) and Na(2) sites. For M = Hf, Zr, only a single signal could be resolved at room temperature, which splits into two signals on cooling to − 50 °C, indicating high Na mobility at room temperature. Impedance data obtained on pressed sintered pellets over the range 25−300 °C showed that bulk ionic conductivities increased and activation energies decreased in the sequence Ti, Sn, Hf, Zr. The geometry of the M1M2 bottleneck has been determined from structural data, and a direct correlation found between activation energy for ion conduction and the bottleneck size.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Solid-state spectroscopy and crystallography · Chemical Synthesis and Characterization · X-ray Diffraction in Crystallography
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Department of Chemistry, University of Aberdeen, Meston Walk, Aberdeen AB24 3UE, U.K.
References (18)
Show source-provided references
1. Hong H. Y.-P. · Mat. Res. Bull. · 1976 · 11 · 17310.1016/0025-5408(76)90073-8 ↗
2. Goodenough J. B. · Mater. Res. Bull. · 1976 · 11 · 20310.1016/0025-5408(76)90077-5 ↗
3. Tran-Qui D. · Solid State Ionics · 1981 · 3 · 219
4. Kholer H. · Mater. Res. Bull. · 1986 · 21 · 2310.1016/0025-5408(86)90025-5 ↗
5. Delmas C. · Mater. Res. Bull. · 1981 · 16 · 28510.1016/0025-5408(81)90044-1 ↗
6. Winand J. M. · J. Mater. Sci. · 1990 · 25 · 400810.1007/BF00582473 ↗
7. Kholer H. · Mater. Res. Bull. · 1985 · 20 · 146110.1016/0025-5408(85)90164-3 ↗
8. Kholer H. · Solid State Ionics · 1983 · 9 · 79510.1016/0167-2738(83)90089-9 ↗
9. Saito Y. · Solid State Ionics · 1992 · 58 · 32710.1016/0167-2738(92)90136-D ↗
10. Gusakovskaya I. G. · Russ. J. Inorg. Chem. (Engl. Transl.) · 1994 · 39 · 1221
11. Aono H. · J. Electrochem. Soc. · 1990 · 137 · 102310.1149/1.2086597 ↗
12. Aono H. · Solid State Ionics · 1993 · 62 · 30910.1016/0167-2738(93)90387-I ↗
13. Rietveld H. M. · J. Appl. Crystallogr. · 1969 · 2 · 6510.1107/S0021889869006558 ↗
14. Thompson P. · J. Appl. Crystallogr. · 1987 · 20 · 7910.1107/S0021889887087090 ↗
15. Finger L. W. · J. Appl. Crystallogr. · 1994 · 27 · 89210.1107/S0021889894004218 ↗
16. Jäger C. · Chem. Phys. Lett. · 1989 · 154 · 4510.1016/0009-2614(89)87435-4 ↗
17. Shannon R. D. · Acta Crystallogr. · 1976 · 32 · 75110.1107/S0567739476001551 ↗
18. Winand J. M. · J. Solid State Chem. · 1991 · 93 · 34110.1016/0022-4596(91)90308-5 ↗